Preparation method of arched graphene three-dimensional network

A three-dimensional network and graphene technology, applied in the field of graphene, can solve the problems of slow and complicated transfer process, structural damage, collapse, etc., and achieve the effect of simple and simplified process

Active Publication Date: 2017-06-30
NANJING UNIV OF AERONAUTICS & ASTRONAUTICS
View PDF12 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0013] However, the graphene foams with the above three-dimensional structures are mostly prepared from irregular three-dimensional metal foams as templates. Afterwards, large structural damage and collapse are caused, which is not conducive to the retention of the three-dimensional structure of graphene and the exertion of intrinsic excellent properties.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of arched graphene three-dimensional network
  • Preparation method of arched graphene three-dimensional network
  • Preparation method of arched graphene three-dimensional network

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0068] 1. Preparation of arched graphene three-dimensional network

[0069] Step 1: Take the three-dimensional copper mesh and cut it to 5 cm * 5 cm * 0.25 mm, take 100 mg of nickel wire with a diameter of 0.1 mm (120 mesh nickel powder can also be used in the specific practice process), and put the copper mesh and nickel wire into the 1:1 equal volume mixed alcohol and acetone mixed solution. Clean with ultrasonic waves at a power of 200-400W for 40-80 minutes, and then rinse repeatedly with deionized water to remove surface impurities and obtain a cleaned three-dimensional copper mesh.

[0070] Put the cleaned three-dimensional copper mesh and nickel wire (100 mg) into a vapor phase chemical deposition growth furnace. The volume of the furnace chamber is 1 liter, and the concentration of nickel vapor in the furnace chamber at the reaction temperature is about 0.13ppm (in the specific implementation process, Ensure that the concentration of nickel vapor in the reaction furna...

Embodiment 2

[0085] The basic experimental method of this embodiment is basically the same as that of Example 1. The difference is that in Step 1: the concentration of nickel vapor in the growth furnace cavity is about 0.05ppm at the reaction temperature of the experimental group, and no nickel wire is added to the control group.

[0086]The growth conditions of both the experimental group and the control group were as follows: the furnace temperature was 1010 degrees Celsius, the methane flow rate was 50 sccm, the hydrogen gas flow rate was controlled at 5 sccm, and the growth time was 60 minutes. All the other conditions and steps are the same as in Example 1.

[0087] Figure 7 and Figure 8 They are the Raman spectra of the graphene networks of the experimental group (with nickel vapor added during growth) and the control group (without nickel vapor), respectively. From the Raman spectra, it can be seen that the graphene obtained in the experimental group is multi-layered, and the con...

Embodiment 3

[0091] The basic experimental method of this embodiment is basically the same as that of Example 1, except that in Step 1: the concentration of nickel vapor in the growth chamber of the experimental group in this embodiment is 2ppm at the reaction temperature, and the control group also does not add nickel.

[0092] The growth conditions of both the experimental group and the control group were: furnace temperature 990° C., methane flow rate 20 sccm, hydrogen flow rate control 15 sccm, and growth time 50 minutes. All the other conditions and steps are the same as in Example 1.

[0093] Figure 11 and Figure 12 Respectively, the Raman spectra of the experimental group (with nickel vapor added in the growth) and the control group (without nickel vapor) after the three-dimensional network transfer of the arched graphene. From the Raman spectrum, it can be seen that the graphene obtained by the experimental group is multi-layered. The control group was a single layer.

[0094]...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
electrical resistanceaaaaaaaaaa
electrical resistanceaaaaaaaaaa
electrical resistanceaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of an arched graphene three-dimensional network. On the basis that graphene grows on a conventional copper substrate through chemical vapor deposition, the number of layers and the continuity of graphene are controlled by introducing trace metallic nickel steam, so that the graphene three-dimensional network growing on a three-dimensional copper-catalyzed template has the best self-supporting property and the best electrical transport performance suitable for stress sensing detection during transferring, and is transferred to a flexible target substrate with a soft gel half-coating method during separation transferring of the graphene three-dimensional network, and the graphene three-dimensional network with the special arched structure is prepared.

Description

technical field [0001] The invention relates to the technical field of graphene, in particular to a method for preparing an arched graphene three-dimensional network. Background technique [0002] Graphene is a two-dimensional honeycomb crystal structure composed of a single layer of carbon atoms tightly packed, with excellent electrical, mechanical, thermal and optical properties. Graphene network structure refers to a network structure formed by graphene as a seamless connection that maintains interconnection in two-dimensional or three-dimensional space. As disclosed in Chinese patent application 201210043497.6, a copper network is used as a template and a graphene network is prepared by chemical vapor deposition. Because the graphene network prepared based on the chemical vapor deposition method has the characteristics of transparency, high strength, and good conductivity, it has important applications in the design of new sensors, such as strain sensors based on graphe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C01B32/186C01B32/194
CPCC01B2204/22C01B2204/32C01P2002/82C01P2004/02C01P2004/03
Inventor 周建新郭成龙陈亚清郭万林
Owner NANJING UNIV OF AERONAUTICS & ASTRONAUTICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com