A sportswear, seamless technology, applied in clothing, clothing, clothing features and other directions, can solve the problems of health care clothing that cannot effectively meet health care and wearing comfort at the same time, cannot be used in clothing production, and affects fabric softness. The effect of line feeling, soft wearing and convenient finishing
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0046] The invention provides a method for preparing magnetic therapy seamless sportswear, comprising the following steps:
[0047] (1) The permanent magnet ferrite is pulverized into magnetic powder particles of 1 μm, and the magnetic powder particles are mixed in the melt of polyethylene terephthalate in a ratio of 13wt%, and magnetic polyester fibers are made through melt spinning;
[0048] (2) Weaving the magnetic polyester fiber described in step (1) seamlessly and integrally to obtain the magnetic therapy seamless sportswear.
Embodiment 2
[0050] The invention provides a method for preparing magnetic therapy seamless sportswear, comprising the following steps:
[0051] (1) The rare earth permanent magnet material is pulverized into magnetic powder particles of 500nm, the magnetic powder particles are mixed into the solution of polyethylene terephthalate in a ratio of 15wt%, and magnetic polyester fibers are made through melt spinning;
[0052] (2) Take the spandex fiber and the magnetic polyester fiber obtained in step (1) and carry out seamless integrated weaving according to the weight ratio of 1:99, to obtain the magnetic therapy seamless sportswear;
[0053] (3) Garment dyeing the magnetic therapy seamless sportswear obtained in step (2) at 110° C. to obtain a finished product.
Embodiment 3
[0055] The invention provides a method for preparing magnetic therapy seamless sportswear, comprising the following steps:
[0056] (1) The permanent magnet ferrite is pulverized into magnetic powder particles of 100nm, the magnetic powder particles are mixed in the melt of polyethylene terephthalate in a ratio of 17wt%, and magnetic polyester fibers are made through melt spinning;
[0057] (2) Take the spandex fiber and the magnetic polyester fiber obtained in step (1) to carry out seamless integrated weaving according to the weight ratio of 8:92, to obtain the magnetic therapy seamless sportswear;
[0058] (3) Garment dyeing the magnetic therapy seamless sportswear obtained in step (2) at 125° C. to obtain a finished product.
[0059] After testing, when the weight ratio of spandex fiber to magnetic polyester fiber is 8:92, it is not only convenient for seamless integral molding, but also the magnetic therapy seamless sportswear produced is highly elastic, comfortable to fit...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com