Hot melt adhesive formula and manufacturing method thereof

A production method and hot melt adhesive technology are applied in the directions of adhesives, adhesive additives, polymer adhesive additives, etc., to achieve the effects of environmental protection, high adhesion and reasonable components.

Inactive Publication Date: 2017-05-31
天津市统业家俱工贸有限公司
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, hot melt adhesives with reasonable composition, high stability, environmentally friendly composition and high adhesion are rare in the market and need to be developed.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hot melt adhesive formula and manufacturing method thereof
  • Hot melt adhesive formula and manufacturing method thereof
  • Hot melt adhesive formula and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] A hot-melt adhesive formula and a preparation method thereof, the composition of which comprises per hundred parts:

[0012]

[0013]

[0014] Stir EVA resin, ethylene octene copolymer, and polyisobutylene at 85°C for 15 minutes, add stabilizer and antioxidant, stir for 10 minutes, add tackifier, raise the temperature to 110°C and stir for 15 minutes, cool down to 80°C, pass Extruded by extruder, cut and cooled.

Embodiment 2

[0016] A hot-melt adhesive formula and a preparation method thereof, the composition of which comprises per hundred parts:

[0017]

[0018] Stir EVA resin, ethylene octene copolymer, and polyisobutylene at 90°C for 10 minutes, add stabilizer and antioxidant, stir for 5 minutes, add tackifier, raise the temperature to 110°C and stir for 15 minutes, cool down to 80°C, pass Extruded by extruder, cut and cooled.

Embodiment 3

[0020] A hot-melt adhesive formula and a preparation method thereof, the composition of which comprises per hundred parts:

[0021]

[0022] Stir EVA resin, ethylene octene copolymer, and polyisobutylene at 90°C for 8 minutes, add stabilizer and antioxidant, stir for 8 minutes, add tackifier, heat up to 110°C and stir for 12 minutes, cool to 80°C, pass Extruded by extruder, cut and cooled.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a hot melt adhesive formula and a manufacturing method of the hot melt adhesive formula. The hot melt adhesive formula comprises the following ingredients: 35-60 parts of EVA resin, 30-45 parts of a tackifier, 3-6 parts of ethylene-octene copolymers, 2-4 parts of polyisobutene, 0.5-2 parts of a stabilizer, and 0.3-0.5 part of an antioxygen. The EVA resin, the ethylene-octene copolymer and the polyisobutene are stirred for 10-15 minutes at the temperature of 80-90 DEG C, the stabilizer and the antioxygen are added, stirring is performed for 5-10 minutes, the tackifier is added, the temperature is raised to 110 DEG C, the mixture is stirred for 10-15 minutes, the temperature is reduced to 80 DEG C, and the mixture is extruded through an extruder, and is cut and cooled. The hot melt adhesive formula is reasonable in ingredients and high in stability, and is particularly suitable for the field of furniture processing, the ingredients are environmentally friendly, and the degree of adhesion is high.

Description

technical field [0001] The invention relates to the field of hot-melt adhesives, in particular to a hot-melt adhesive formulation and a manufacturing method thereof. Background technique [0002] Hot melt adhesives are widely used, and different fields have different performance requirements for hot melt adhesives. When used in the field of furniture, in addition to high requirements on the safety, stability and adhesion of hot melt adhesives, it is also required to be green and environmentally friendly, so as to avoid harm to the human body when placed indoors for a long time. The furniture manufacturing field uses a large amount of hot melt adhesives, and cost control is also a scope that needs to be considered. Currently, hot melt adhesives with reasonable composition, high stability, environmentally friendly composition, and high adhesion are rare on the market and need to be developed. Contents of the invention [0003] In order to overcome the shortcomings of the e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J123/08C09J11/08
CPCC09J123/0853C08L2205/03C08L2205/035C09J11/08
Inventor 银国清
Owner 天津市统业家俱工贸有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com