Concrete brick with high water permeability

A technology of permeable concrete and metakaolin, applied in the field of concrete, can solve the problems of unsatisfactory strength and water permeability, limited application of permeable concrete bricks, poor water permeability, etc., to improve the compressive strength and resistance to chloride ion penetration, The effect of preventing the decrease of the water permeability coefficient and porosity and improving the water permeability

Inactive Publication Date: 2017-05-17
安徽城洁环境科技有限公司
View PDF3 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the strength and water permeability of the existing concrete are still not ideal, and the concrete bricks made of it have the defects of poor strength and poor water permeability, which limits the application of permeable concrete bricks in many aspects

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A kind of high permeable concrete brick proposed by the present invention, its raw material comprises by weight: 120 parts of cement, 300 parts of gravel, 35 parts of phosphogypsum, 10 parts of slag, 50 parts of steel slag, 200 parts of river sand, 50 parts of fly ash , 5 parts of silica fume, 35 parts of sintered magnesia, 2 parts of metakaolin, 40 parts of mixed fiber, 5 parts of straw powder, 8 parts of water reducer, 0.1 part of sodium ethylenediamine tetramethylene phosphonate, and 50 parts of water.

Embodiment 2

[0016] A kind of highly permeable concrete brick proposed by the present invention, its raw material comprises by weight: 200 parts of cement, 250 parts of gravel, 10 parts of phosphogypsum, 50 parts of slag, 10 parts of steel slag, 350 parts of river sand, 20 parts of fly ash , 20 parts of silica fume, 10 parts of sintered magnesia, 15 parts of metakaolin, 10 parts of mixed fiber, 38 parts of straw powder, 3 parts of water reducing agent, 0.5 parts of sodium ethylenediamine tetramethylene phosphonate, 20 parts of water;

[0017] Wherein, the water reducer is prepared according to the following process: adding hydroxyethylidene diphosphonic acid into chloroform, stirring evenly, adding triethylamine and methacryloyl chloride, raising the temperature to 85°C and stirring for 8 hours. After the reaction, Material A: add isopentenol polyoxyethylene ether into water, stir evenly and heat up to 65°C, then add acrylic acid, material A, ascorbic acid, acrylonitrile, N-carbamoylmaleimi...

Embodiment 3

[0019] A kind of high permeable concrete brick proposed by the present invention, its raw material comprises by weight: 180 parts of cement, 265 parts of gravel, 19 parts of phosphogypsum, 32 parts of slag, 21 parts of steel slag, 260 parts of river sand, 31 parts of fly ash , 18 parts of silica fume, 18 parts of sintered magnesia, 10 parts of metakaolin, 21 parts of mixed fiber, 26 parts of straw powder, 4.9 parts of water reducer, 0.4 part of sodium ethylenediamine tetramethylene phosphonate, and 30 parts of water;

[0020] Wherein, the apparent density of the gravel is 2.5g / cm 3 , bulk density is 1.5g / cm 3 , with a mud content of 0.35% and a porosity of 35%;

[0021] The mixed fiber is a mixture of basalt fiber, steel fiber, polyvinyl alcohol fiber and glass fiber in a weight ratio of 2:8:3:15;

[0022] The water reducer is prepared according to the following process: add hydroxyethylidene diphosphonic acid into chloroform, stir evenly, add triethylamine and methacryloyl ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Apparent densityaaaaaaaaaa
Bulk densityaaaaaaaaaa
Apparent densityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a concrete brick with high water permeability. The concrete brick is prepared from raw materials in parts by weight as follows: 120-200 parts of cement, 250-300 parts of gravel, 10-35 parts of ardealite, 10-50 parts of slag, 10-50 parts of steel slag, 200-350 parts of river sand, 20-50 parts of fly ash, 5-20 parts of silica fume, 10-35 parts of sintered magnesia, 2-15 parts of metakaolin, 10-40 parts of mixed fiber, 5-38 parts of straw powder, 3-8 parts of a water reducer, 0.1-0.5 parts of ethylene diamine tetra (methylene phosphonic acid) sodium and 20-50 parts of water. The concrete brick with high water permeability has very high compressive strength and excellent water permeability and can meet the use requirement of multiple fields.

Description

technical field [0001] The invention relates to the technical field of concrete, in particular to a highly permeable concrete brick. Background technique [0002] Permeable concrete is usually also called porous concrete. It is a porous material that has both a certain material strength and a certain degree of water permeability and air permeability. From its own performance, in addition to effectively relieving surface water, it is also effective in rainwater. It has obvious effects in terms of purification and reduction of road noise. Permeable concrete generally has the following advantages: sound absorption and noise reduction, protection of groundwater, improvement of thermal environment, improvement of surface soil ecological environment, etc. However, the strength and water permeability of existing concrete are still not ideal, and the concrete bricks made of it have the defects of poor strength and poor water permeability, which limit the application of permeable co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/00C04B38/00C04B24/28C08F283/06C08F230/02C08F220/06C08F220/46C08F222/40C04B103/30
CPCC04B24/246C04B28/00C04B2103/302C04B2111/00284C08F283/065C04B14/02C04B22/144C04B18/141C04B18/142C04B14/068C04B18/08C04B18/146C04B14/304C04B14/106C04B18/24C04B14/48C04B16/0641C04B14/42C04B14/4656C04B24/003C04B38/00C08F222/406
Inventor 薛念念汤俊怀李青松王军
Owner 安徽城洁环境科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap