A kind of tussah silk fibroin protein microsphere containing three-dimensional hole structure and preparation method thereof

A technology of tussah silk fibroin and pores, which is applied in the field of textile materials, can solve the problems of unfavorable fabric feel and air permeability and moisture permeability, and there are not many porous fibroin particles, so as to achieve good skin-friendly and air permeability and moisture permeability. The effect of porosity

Inactive Publication Date: 2020-01-10
上海寓尚电子商务有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Silk fibroin fabric finishing is mostly mixed with silk fibroin solution and other functional agents as a finishing agent, and the fabric is finished by dipping, coating or spraying. In this finishing method, silk fibroin is mostly covered on the fabric in the form of a film. The surface of the fabric is not conducive to the feel and breathability of the fabric
Silk fibroin particles are one form of silk fibroin. The preparation methods of silk fibroin particles include emulsification solvent evaporation method, phase separation method, high-voltage electrostatic method and spray drying method, etc., but the silk particles prepared so far are all solid particles. Compared with solid particles, porous particles have better air and moisture permeability, adsorption performance and functionality, but there are not many studies on silk protein porous particles.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of tussah silk fibroin protein microsphere containing three-dimensional hole structure and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] (1) use tussah silk as raw material, after degumming, be 1g:10ml with solid-liquid ratio, be placed in lithium bromide solvent and dissolve completely at 60 ℃, dialyze, separate, add the elastase solution that mass fraction is 0.5%, in Enzymolysis at 10° C. for 30 minutes, heat inactivation at 80° C., and concentration to obtain a tussah silk fibroin protein solution, wherein the tussah silk fibroin protein has a molecular weight of 15-30 kDa.

[0025] (2) Add 0.5 parts of azobisisobutyronitrile foaming agent and 1 part of glutaraldehyde and citric acid crosslinking agent to the aqueous solution containing 1 part of tussah silk fibroin protein in parts by mass, and let it stand at 20 ° C 2 minutes, stirred for 60 minutes, and centrifuged to form tussah silk fibroin particles.

[0026] (3) In parts by mass, add 1 part of tussah silk fibroin protein particles into an aqueous solution containing 6 parts of sodium chloride, heat and stir at a temperature of 95°C and a speed...

Embodiment 2

[0028] (1) use tussah silk as raw material, after degumming, be 1g: 10ml with solid-liquid ratio, be placed in lithium bromide solvent and dissolve completely at 60 ℃, dialyze, separate, add the elastase solution that mass fraction is 2%, in Enzymolysis at 15°C for 60 minutes, heat inactivation at 80°C, and concentration to obtain a tussah silk fibroin protein solution, wherein the tussah silk fibroin protein has a molecular weight of 15-30kDa.

[0029] (2) Add 0.8 parts of azobisisobutyronitrile foaming agent and 2 parts of glutaraldehyde and citric acid crosslinking agent to the aqueous solution containing 1 part of tussah silk fibroin protein in parts by mass, and let it stand at 25 ° C 5 minutes, stirred for 90 minutes, and centrifuged to form tussah silk fibroin particles.

[0030] (3) In parts by mass, add 1 part of tussah silk fibroin protein particles into an aqueous solution containing 10 parts of sodium chloride, heat and stir at a temperature of 98° C. and a speed o...

Embodiment 3

[0032] (1) use tussah silk as raw material, after degumming, be 1g:10ml with solid-liquid ratio, be placed in lithium bromide solvent and dissolve completely at 60 ℃, dialyze, separate, add the elastase solution that mass fraction is 1%, in Enzymolysis at 12° C. for 45 minutes, heat inactivation at 80° C., and concentration to obtain tussah silk fibroin protein solution, wherein the tussah silk fibroin protein has a molecular weight of 15-30 kDa.

[0033] (2) Add 0.6 parts of azobisisobutyronitrile foaming agent and 1.5 parts of glutaraldehyde and citric acid crosslinking agent to the aqueous solution containing 1 part of tussah silk fibroin protein in parts by mass, and let it stand at 23 ° C 3 minutes, stirred for 70 minutes, and centrifuged to form tussah silk fibroin particles.

[0034] (3) In parts by mass, add 1 part of tussah silk fibroin protein particles into an aqueous solution containing 8 parts of sodium chloride, heat and stir at a temperature of 97° C. and a spee...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
molecular weightaaaaaaaaaa
Login to View More

Abstract

The invention provides a tussah fibroin protein microsphere including a three-dimensional porous structure and a production method thereof. The method comprises the steps of using tussah silk as raw material, degumming the tussah silk, placing degummed tussah silk into solvent to dissolve completely, dialyzing, separating, adding enzyme solution for enzymolysis, heating, and concentrating to obtain tussah fibroin protein solution; adding a foaming agent and a cross-linking agent into the tussah fibroin protein solution, standing, stirring and centrifugally separating to form tussah fibroin protein particles; and adding the tussah fibroin protein particles into sodium chloride solution, heating, stirring, centrifugally separating sediments, washing with ethyl alcohol, taking the washed sediments out, drying and placing into a low temperature environment to cool and dry, thus acquiring the tussah fibroin protein microspheres with three-dimensional porous structures. The production method provided by the invention is simple, and the produced silk fibers are good in porosity and have the properties of being skin-friendly, air and vapor permeable and adsorptive.

Description

technical field [0001] The invention belongs to the technical field of textile materials, and in particular relates to a tussah silk fibroin microsphere containing a three-dimensional hole structure and a preparation method thereof. Background technique [0002] Silk fibroin is an animal protein derived from silk fiber. Whether it is mulberry silk or tussah silk, silk fibroin is mainly composed of 18 kinds of amino acid tissues such as glycine, alanine and serine. Silk fibroin has good degradability, Biocompatibility and formability, etc., silk fibroin has many applications in fabric finishing. [0003] Silk fibroin fabric finishing is mostly mixed with silk fibroin solution and other functional agents as a finishing agent, and the fabric is finished by dipping, coating or spraying. In this finishing method, silk fibroin is mostly covered on the fabric in the form of a film. The surface of the fabric is not conducive to the feel and breathability of the fabric. Silk fibroi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06M15/15B01J13/14
CPCB01J13/14D06M15/15
Inventor 王文庆
Owner 上海寓尚电子商务有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com