Novel burn-out fabric and burn-out technology thereof

A kind of fabric and new technology, applied in the direction of fabric surface trimming, thorn pattern, textile and papermaking, etc., can solve the problems of poor hygroscopicity and non-bacterial, and achieve the effect of good air permeability, natural pattern and simple process

Active Publication Date: 2017-05-10
LILANG CHINA
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But the patent is not antibacte

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0023] Example 1

[0024] A new type of burnt-out fabric is made from burnt-out grey cloth through burnt-out paste. The warp yarn of burnt-out grey cloth is blended by 40wt% bamboo fiber and 60wt% polyester; the weft yarn of burnt-out grey cloth is: 85wt% bamboo Fiber-polyester blended yarn with 15wt% spandex core-spun yarn; the raw materials and mass percentages of burnt pulp are: sulfuric acid 40%, tartaric acid 15%, sodium polyacrylate 2%, xanthan gum 1%, laureth polyoxyethylene Ether 2%, deionized water 40%; among them, the fineness of the warp yarn is 30S; the fineness of the weft yarn is 20S; the preparation process of the burnt pulp is: first dissolve the mass percentage of sodium polyacrylate and xanthan gum After being completely dissolved in deionized water at 40°C, the original paste is obtained. After cooling the original paste to room temperature, add the mass percentage of sulfuric acid, tartaric acid and polyoxyethylene laureth ether, and seal for later use; the vi...

Example Embodiment

[0025] Example 2

[0026] A new type of burnt-out fabric is made from burnt-out grey cloth through burnt-out paste. The warp yarn of burnt-out grey cloth is blended with 50wt% bamboo fiber and 50wt% polyester; the weft yarn of burnt-out grey cloth is: 88wt% bamboo Fiber-polyester blended yarn with 12wt% spandex core-spun yarn; the raw materials and mass percentage of burnt pulp are: sulfuric acid 45%, tartaric acid 20%, sodium polyacrylate 2.5%, xanthan gum 1.5%, laureth polyoxyethylene 1% ether, 30% deionized water; among them, the fineness of the warp yarn is 35S; the fineness of the weft yarn is 25S; the preparation process of the burnt pulp is: first dissolve the mass percentage of sodium polyacrylate and xanthan gum After being completely dissolved in deionized water at 50°C, the original paste is obtained. After cooling the original paste to room temperature, add the mass percentage of sulfuric acid, tartaric acid and polyoxyethylene laureth, and seal for later use; the vis...

Example Embodiment

[0027] Example 3

[0028] A new type of burnt-out fabric made of burnt-out grey cloth through burnt-out paste. The warp yarn of burnt-out grey cloth is blended with 60wt% bamboo fiber and 40wt% polyester; the weft of burnt-out grey cloth is 90wt% bamboo fiber Polyester blended yarn covered 10wt% spandex core-spun yarn; the raw materials and mass percentages of burnt pulp are: sulfuric acid 50%, tartaric acid 10%, sodium polyacrylate 1.5%, xanthan gum 2%, lauryl alcohol polyoxyethylene ether 1.5%, 35% deionized water; among them, the fineness of the warp yarn is 40S; the fineness of the weft yarn is 30S; the preparation process of the burnt flower pulp is: first dissolve the mass percentage of sodium polyacrylate and xanthan gum in 60 After being completely dissolved in deionized water at °C, the original paste is obtained. After cooling the original paste to room temperature, add the mass percentage of sulfuric acid, tartaric acid and polyoxyethylene laureth ether, and seal for l...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
Viscosityaaaaaaaaaa
Viscosityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a novel burn-out fabric and a burn-out technology thereof. A burn-out gray fabric is prepared by pasting burn-out sizing, and warp yarn of the burn-out gray fabric is formed by blending bamboo fibers and terylene; weft yarn of the burn-out gray fabric is a core spun yarn which is formed by blending bamboo fibers terylene and cotton-covering spandex; the raw materials of burn-out sizing comprise sulfate-tartrate, sodium polyacrylate, xanthan gum, lauryl alcohol polyoxyethylene, and deionized water. The burn-out technology comprises the following steps of performing alkali weight reduction treatment on the burn-out gray fabric, washing, and neutralizing, so as to complete the alkali weight reduction treatment; dyeing the burn-out gray fabric after the alkali weight reduction treatment by a double-bath dyeing method; scraping and printing the burn-out sizing to the dyed burn-out gray fabric by a flat screen printing technology, baking until being complete carbonized, and then washing in water; finally, drying, so as to obtain the novel burn-out fabric. The novel burn-out fabric prepared by the invention has the advantages that the weight is light, the air permeation property is realized, the abrasion-resistant property is realized, the dyeing is easy, and the anti-bacterial, bacteria-inhibiting, anti-odorizing and anti-ultraviolet functions are realized.

Description

technical field [0001] The invention relates to the field of textile production, in particular to a novel burnt-out fabric and a burnt-out process thereof. Background technique [0002] Burn-out printed fabrics are often used in summer clothing fabrics. The fabrics are composed of two types of fibers, one of which can be destroyed by certain chemicals. The other fiber is left unaffected; creating a special style, sheer burnout printed fabric. At present, the commonly used clothing fabrics in summer include cotton and linen, chiffon and burnt fabrics. Among them, cotton and linen fabrics are breathable and dry, reduce perspiration, prevent radiation, and prevent static electricity, but they have problems such as rough styles and hard handles; chiffon fabrics Light and transparent, soft to the touch, elastic, elegant to wear, good wear resistance, not easy to pilling, and stable in size, but there are problems such as poor moisture absorption and air permeability, and easy to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06C23/02
CPCD06C23/02D10B2201/10D10B2331/04D10B2331/10
Inventor 陈国仲程兵李洪欧锦蓥史志颖柳婉瑜
Owner LILANG CHINA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap