Damp-proof burning incense and preparation method thereof

A technology for burning incense and adhesive, which is applied in the fields of botanical equipment and methods, pest control, chemicals for biological control, etc. The effect of avoiding moisture deformation or peeling off, excellent moisture resistance

Inactive Publication Date: 2017-05-10
FUJIAN AGRI & FORESTRY UNIV
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] Burning incense is easily damaged by moisture. Traditional burning incense preparation methods (including the methods disclosed in the above-mentioned documents) have not adopted corresponding preparation techniques in the preparation process to improve the moisture-proof performance of burning incense, mainly by increasing the amount of adhesive. Ways to improve the moisture-proof ability of burning incense, this method will easily lead to an increase in the cost of burning incense, and the flammability will deteriorate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Damp-proof burning incense and preparation method thereof
  • Damp-proof burning incense and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0035] The preparation method of the moisture-proof burning incense comprises the following steps:

[0036] 1) heating and dissolving the paraffin, and storing it in a container in a liquid state;

[0037] 2) Put the plant material into an airtight container with a stirring device, stir at room temperature, and control the rotation speed to 60-90rpm;

[0038] 3) Use an air compressor to spray the above-mentioned dissolved paraffin into the airtight container containing plant raw materials from the feeding port, and control the air flow rate of the nozzle to 30-90m / s; the nozzle can be heated, and the temperature of the compressed air must be higher than the melting point of the paraffin 10-25°C;

[0039] 4) After adding the paraffin, continue to stir for 20-40min;

[0040] 5) Add adhesive and water to the airtight container to make the water content of the mixture in the airtight container 40-60%, and continue to stir for 30-60min;

[0041] 6) Transfer the mixture in the ab...

Embodiment 1

[0045] A moisture-proof burning incense is prepared from the following raw materials:

[0046] 700 parts of plant raw materials, 3 parts of microcrystalline paraffin, 25 parts of adhesive, appropriate amount of deionized water;

[0047] Among them, the plant raw material is wood flour, the moisture content is 8%, and the particle size of wood flour is ≥100 mesh;

[0048] The adhesive is starch glue with a solid content of 60%;

[0049] The preparation method of the moisture-proof burning incense comprises the following steps:

[0050] 1) heating and dissolving the microcrystalline paraffin, and storing it in a container in a liquid state;

[0051] 2) Put the plant material into an airtight container with a stirring device, stir at room temperature, and control the rotation speed to 75rpm;

[0052] 3) Use an air compressor to spray the above-mentioned dissolved microcrystalline paraffin from the feeding port into a closed container containing plant raw materials, and control...

Embodiment 2

[0062] A moisture-proof burning incense is prepared from the following raw materials:

[0063] 400 parts of plant raw materials, 0.5 parts of polyethylene wax, 7 parts of adhesive, appropriate amount of tap water;

[0064] Among them, the plant raw material is wood powder, bamboo powder, and grass powder mixed in any proportion, the moisture content is 10%, and the particle size is ≥100 mesh;

[0065] The adhesive is a polyacrylamide adhesive with a solid content of 100%;

[0066] The preparation method of the moisture-proof burning incense comprises the following steps:

[0067] 1) The polyethylene wax is heated and dissolved, and stored in a container in a liquid state;

[0068] 2) Put the plant material into a closed container with a stirring device, stir at room temperature, and control the rotation speed to 60rpm;

[0069] 3) Use an air compressor to spray the above-mentioned dissolved polyethylene wax from the feeding port into a closed container containing plant raw ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses damp-proof burning incense and a preparation method thereof. The damp-proof burning incense is prepared from plant raw materials, paraffin, an adhesive and water. The dissolved paraffin is sprayed into a closed container filled with the plant raw materials through a charging opening by an air compressor, the nozzle air flow rate is controlled to be 30-90 m / s, the temperature of compressed air is controlled to be 10-25 DEG C higher than the melting point of the paraffin, the adhesive and the water are added into the closed container after stirring is carried out for a certain time, the water content of the mixture in the closed container is 40-60%, stirring continues to be carried out, finally, the mixture in the closed container is transferred into an extruder hopper, die extrusion molding is carried out, the product is dried till the water content is smaller than or equal to 10%, and the damp-proof burning incense is obtained. Surface hydrophilicity loci of the plant raw materials are closed through the paraffin, the damp-proof burning incense is prepared in combination with the adhesive, and the situation that burning incense is affected with damp to deform or peel off in the plum rain season of spring in the south can be effectively avoided.

Description

technical field [0001] The invention relates to the technical field of incense preparation, in particular to a moisture-proof type incense and a preparation method thereof. Background technique [0002] Burning incense (such as mosquito coils, Buddha incense, etc.) is widely used all over the world. The traditional method of preparing burning incense is mainly to crush the raw materials, mix them, and press them into molds after the glue is stirred, and then dry them to obtain the finished burning incense. [0003] The patent application with the application number 201610470645.0 discloses a method for making mosquito-repellent incense, which comprises pulverizing tea leaves, tea leaves, sandalwood, mint, agarwood, mugwort, and charcoal, stirring them with water to evenly form a paste, and pressing them into shape. To obtain a green body, then bake the green body at a temperature of 60-80° C. for 4-5 hours until dry, then let it cool at room temperature and pack it. [0004...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A01N25/18A01N65/08A01N61/00A01P17/00
CPCA01N25/18A01N61/00A01N65/00A01N65/08A01N2300/00
Inventor 陈奶荣林巧佳郑培涛尤泽铭邱九根饶久平曾钦志范毜仔王昕楠林三贝
Owner FUJIAN AGRI & FORESTRY UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com