Polypropylene filling masterbatch and preparation method thereof

A technology of filling masterbatch and polypropylene, which is applied in the field of filling materials, can solve the problems of unfavorable processing of polypropylene resin, influence of melt fluidity, increase of melt viscosity, etc., so as to increase the flow rate of melt finger and improve the processing fluidity and feeding speed, the effect of improving compatibility

Active Publication Date: 2017-03-29
JIANGXI HONGYI POLYMERIC MATERIALS
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, these fillers will greatly affect the fluidity of the melt, making the compatibility between various substances poor, resulting in increased melt viscosity and poor fluidity, making the polypropylene resin with a low melt index more unfavorable for processing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A polypropylene filling masterbatch, made of raw materials containing the following parts by weight: 5 parts of polypropylene, 85 parts of modified barium sulfate and calcium carbonate composite powder, 1.2 parts of polyacrylate, titanate coupling 0.6 parts, 0.7 parts of ethylene bis stearamide, 2.4 parts of polyethylene wax, 1.4 parts of zinc stearate.

[0028] The modified barium sulfate and calcium carbonate composite powder is barium sulfate and calcium carbonate composite powder modified by silane coupling agent, titanate coupling agent, sodium stearate and rosin, wherein barium sulfate and calcium carbonate The mass ratio of calcium is 2:1, and the addition amount of silane coupling agent, titanate coupling agent, sodium stearate and rosin are 1‰, 3‰, 5‰, 1‰.

[0029] The barium sulfate is 3000-5000 mesh, and the calcium carbonate is 2500-3000 mesh heavy calcium carbonate.

[0030] The preparation method of above-mentioned polypropylene filling masterbatch is as...

Embodiment 2

[0036] A polypropylene filling masterbatch, made of raw materials containing the following parts by weight: 8 parts of polypropylene, 90 parts of modified barium sulfate and calcium carbonate composite powder, 1.3 parts of polyacrylate, titanate coupling 0.7 parts, 1.0 parts of ethylene bis stearamide, 3.0 parts of polyethylene wax, 2.0 parts of zinc stearate.

[0037] The modified barium sulfate and calcium carbonate composite powder is barium sulfate and calcium carbonate composite powder modified by silane coupling agent, titanate coupling agent, sodium stearate and rosin, wherein barium sulfate and calcium carbonate The mass ratio of calcium is 3:1, and the addition amounts of silane coupling agent, titanate coupling agent, sodium stearate and rosin are 3‰, 5‰, 6‰, 2‰.

[0038] The barium sulfate is 3000-5000 mesh, and the calcium carbonate is 2500-3000 mesh heavy calcium carbonate.

[0039] The preparation method of above-mentioned polypropylene filling masterbatch is a...

Embodiment 3

[0045] A polypropylene filling masterbatch, made of raw materials containing the following parts by weight: 10 parts of polypropylene, 95 parts of modified barium sulfate and calcium carbonate composite powder, 1.5 parts of polyacrylate, titanate coupling 0.8 parts, 1.2 parts of ethylene bis stearamide, 3.2 parts of polyethylene wax, 2.5 parts of zinc stearate.

[0046] The modified barium sulfate and calcium carbonate composite powder is barium sulfate and calcium carbonate composite powder modified by silane coupling agent, titanate coupling agent, sodium stearate and rosin, wherein barium sulfate and calcium carbonate The mass ratio of calcium is 5:1, and the addition amounts of silane coupling agent, titanate coupling agent, sodium stearate and rosin are 5‰, 7‰, 8‰, 3‰.

[0047] The barium sulfate is 3000-5000 mesh, and the calcium carbonate is 2500-3000 mesh heavy calcium carbonate.

[0048] The preparation method of above-mentioned polypropylene filling masterbatch is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The present invention provides a polypropylene filling masterbatch, which is prepared from the following raw materials by weight: 5-10 parts of polypropylene, 85-95 parts of modified barium sulfate and calcium carbonate composite powder, 1.2-1.5 parts of polyacrylate, 0.6-0.8 part of a titanate coupling agent, 0.7-1.2 parts of N,N'-ethylenedi(stearamide), 2.4-3.2 parts of polyethylene wax, and 1.4-2.5 parts of zinc stearate. The invention further provides a preparation method of the polypropylene filling masterbatch. According to the present invention, with the polypropylene filling masterbatch, the mechanical property and the melt flow rate of the polypropylene can be improved.

Description

[0001] 【Technical field】 [0002] The invention relates to the field of filler materials, in particular to a polypropylene filler masterbatch and a preparation method thereof. [0003] 【Background technique】 [0004] Polypropylene has excellent processing performance, and various processing methods can be used to produce different products for various purposes. However, polypropylene is brittle and has low fracture and tensile strength. Therefore, it is necessary to use modification methods to improve its inherent shortcomings and increase new features. In order to reduce costs with the greatest benefit, the use of inorganic powder filling modification has become the main way of polypropylene modification. [0005] The traditional inorganic powder filler modified polypropylene uses a single filler variety, such as talcum powder, calcium carbonate, etc., which can improve the mechanical properties of polypropylene to a certain extent. However, these fillers will greatly affect...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L33/04C08L23/06C08K13/06C08K9/06C08K9/04C08K3/30C08K3/26C08K5/20C08K5/098
CPCC08K2201/005C08L23/12C08L2205/03C08L33/04C08L23/06C08K13/06C08K9/06C08K9/04C08K2003/3045C08K2003/265C08K5/20C08K5/098C08K3/30C08K3/26
Inventor 徐永华彭鹤松李裕乐周新华
Owner JIANGXI HONGYI POLYMERIC MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com