Additive for polyurethane synthetic leather and preparation method thereof

A technology of synthetic leather and additives, applied in the field of synthetic leather, can solve the problems of poor waterproofness, insufficient comfort and practicability, poor air permeability, etc. avoidance effect

Inactive Publication Date: 2017-03-22
南平慧薇网知识产权营运有限公司
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Synthetic leather is used to make shoes, boots, bags and balls, and is also widely used in upholstery, mattresses, sofas and cars as a substitute for real leather, but the current synthetic leather is prone to the following problems: In some applications The internal functions are not perfect, the comfort and practicability are not good enough, the handle is jerky, the water resistance is poor, the air permeability is poor, it is not wear-resistant and scratch-resistant, and it is easy to be eaten by insects during storage

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] An additive for polyurethane synthetic leather, made of raw materials with the following weight ratio:

[0029] 25 parts polyester resin,

[0030] 7 parts of terpene resin,

[0031] 2 parts of white carbon black,

[0032] 1.2 parts of soap powder,

[0033] 1.8 parts of ethylene bis stearic acid amide,

[0034] 0.8 part of silane coupling agent,

[0035] Betaine 0.6 parts,

[0036] 1.2 parts of dispersant,

[0037] 0.6 parts of fluorine water repellant,

[0038] 60 parts of water.

[0039] The preparation method of additive for polyurethane synthetic leather comprises the following steps:

[0040] 1. Mix polyester resin and terpene resin uniformly according to the formula to obtain mixture A, then take out 1 / 2 of mixture A and silica matting powder, stir in water, grind and filter to obtain mixture B;

[0041] 2. Add soap powder, ethylene bis stearic acid amide, silane coupling agent, betaine, dispersant and fluorine water repellent to mixture B, and mix well to...

Embodiment 2

[0044] An additive for polyurethane synthetic leather, made of raw materials with the following weight ratio:

[0045] 28 parts of polyester resin,

[0046] 9 parts of terpene resin,

[0047] 3 parts of white carbon black,

[0048] 1.5 parts of soap powder,

[0049] 2.2 parts of ethylene bis stearic acid amide,

[0050] 1.3 parts of silane coupling agent,

[0051] Betaine 0.7 parts,

[0052] 1.2 parts of dispersant,

[0053] 0.6 parts of fluorine water repellant,

[0054] 65 parts of water.

[0055] The preparation method of additive for polyurethane synthetic leather comprises the following steps:

[0056] 1. Mix polyester resin and terpene resin uniformly according to the formula to obtain mixture A, then take out 1 / 2 of mixture A and silica matting powder, stir in water, grind and filter to obtain mixture B;

[0057] 2. Add soap powder, ethylene bis stearic acid amide, silane coupling agent, betaine, dispersant and fluorine water repellent to mixture B, and mix wel...

Embodiment 3

[0060] An additive for polyurethane synthetic leather, made of raw materials with the following weight ratio:

[0061] 26 parts of polyester resin,

[0062] 8 parts of terpene resin,

[0063] 2.5 parts of white carbon black,

[0064] 1.3 parts of soap powder,

[0065] 1.95 parts of ethylene bis stearic acid amide,

[0066] 1.15 parts of silane coupling agent,

[0067] Betaine 0.65 parts,

[0068] 1.2 parts of dispersant,

[0069] 0.6 parts of fluorine water repellant,

[0070] 63 parts of water.

[0071] The preparation method of additive for polyurethane synthetic leather comprises the following steps:

[0072] 1. Mix polyester resin and terpene resin uniformly according to the formula to obtain mixture A, then take out 1 / 2 of mixture A and silica matting powder, stir in water, grind and filter to obtain mixture B;

[0073] 2. Add soap powder, ethylene bis stearic acid amide, silane coupling agent, betaine, dispersant and fluorine water repellent to mixture B, and mi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides an additive for polyurethane synthetic leather and a preparation method thereof. The additive is prepared from the following raw materials by weight: 25-28 parts of polyester resin, 7-9 parts of terpene resin, 2-3 parts of white carbon black, 1.2-1.5 parts of soap powder, 1.8-2.2 parts of ethylene-bis-stearamide, 0.8-1.3 parts of a silane coupling agent, 0.6-0.7 part of betaine, 1.2 parts of a dispersant, 0.6 part of a fluorine drying agent, and 60-65 parts of water. The additive provided by the invention can be added into synthetic leather to use, is harmless to the environment, also has no harm to human health, and can improve the water resistance and stability of synthetic leather. The finally obtained synthetic leather has the characteristics of antistatic properties, low irritation, sterilization, low toxicity, emulsification dispersion, chemical stability and biodegradability, etc.

Description

technical field [0001] The invention relates to the field of synthetic leather, in particular to an additive for polyurethane synthetic leather and a preparation method thereof. Background technique [0002] Synthetic leather is a plastic product that simulates the composition and structure of natural leather and can be used as its substitute material. Usually, the impregnated non-woven fabric is used as the mesh layer, and the microporous polyurethane layer is used as the grain layer. Its front and back are very similar to leather, and has a certain degree of air permeability, which is closer to natural leather than ordinary artificial leather. [0003] Synthetic leather is used to make shoes, boots, bags and balls, and is also widely used in upholstery, mattresses, sofas and cars as a substitute for real leather, but the current synthetic leather is prone to the following problems: In some applications The internal functions are not perfect, the comfort and practicabilit...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06N3/14D06N3/12D06N3/04D06N3/00
CPCD06N3/14D06N3/0059D06N3/0061D06N3/0063D06N3/045D06N3/123D06N2203/042D06N2203/061D06N2203/068D06N2209/046D06N2209/103D06N2209/123D06N2209/142D06N2209/1614D06N2209/1671D06N2211/28
Inventor 黄小平
Owner 南平慧薇网知识产权营运有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com