Preparation method for modified graphene oxide, MGO-SiO2 nano-hybrid material and MGO-SiO2 modified phenolic resin hot melting adhesive film

A technology of nano-hybrid materials and phenolic resins, applied in chemical instruments and methods, film/sheet-like adhesives, adhesives, etc., can solve problems such as the performance of phenolic resin hot-melt adhesive films that have not been reported, and achieve good compatibility Sexuality and interfacial properties, excellent ablation resistance and wear resistance, and the effect of uniform dispersion

Active Publication Date: 2017-03-22
XI AN JIAOTONG UNIV
View PDF2 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, introducing nano-silica into the matrix can improve wear resistance, increase material toughness, improve tensile strength and impact strength, and heat resistance. However, there is no report in the prior art to improve phenolic resin by modifying graphene. Technology of Hot Melt Adhesive Film Properties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method for modified graphene oxide, MGO-SiO2 nano-hybrid material and MGO-SiO2 modified phenolic resin hot melting adhesive film
  • Preparation method for modified graphene oxide, MGO-SiO2 nano-hybrid material and MGO-SiO2 modified phenolic resin hot melting adhesive film
  • Preparation method for modified graphene oxide, MGO-SiO2 nano-hybrid material and MGO-SiO2 modified phenolic resin hot melting adhesive film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] The preparation method of modified graphene oxide of the present invention comprises the following steps:

[0046] 1a) Weighing graphite oxide, ethanol A, catalyst, silane coupling agent and ethanol B, then adding graphite oxide to ethanol A, stirring for 1 hour and then ultrasonically dispersing for 2 hours to obtain a graphene oxide dispersion;

[0047] 2a) adding the catalyst to the graphene oxide dispersion obtained in step 1a) to obtain a mixed solution A;

[0048] 3a) Mix the silane coupling agent and ethanol B and stir for 30 minutes to obtain a mixed solution B, then add the mixed solution B to the mixed solution A, and stir and react at 75°C for 12 hours, and then carry out suction filtration and drying to obtain Modified graphene oxide;

[0049] Wherein, the ratio of graphite oxide, ethanol A, catalyst, silane coupling agent and ethanol B is 0.1g:50mL:0.05g:1.6g:20mL.

[0050] The catalyst is dicyclohexylcarbodiimide.

[0051] The silane coupling agent is γ...

Embodiment 2

[0067] The preparation method of modified graphene oxide of the present invention comprises the following steps:

[0068] 1a) Weighing graphite oxide, ethanol A, catalyst, silane coupling agent and ethanol B, then adding graphite oxide to ethanol A, stirring for 1 hour and then ultrasonically dispersing for 2 hours to obtain a graphene oxide dispersion;

[0069] 2a) adding the catalyst to the graphene oxide dispersion obtained in step 1a) to obtain a mixed solution A;

[0070] 3a) Mix the silane coupling agent and ethanol B and stir for 30 minutes to obtain a mixed solution B, then add the mixed solution B to the mixed solution A, and stir and react at 75°C for 12 hours, and then carry out suction filtration and drying to obtain Modified graphene oxide;

[0071] Wherein, the ratio of graphite oxide, ethanol A, catalyst, silane coupling agent and ethanol B is 0.1g:50mL:0.05g:1.6g:65mL.

[0072] The catalyst is triphenylphosphine.

[0073] The silane coupling agent is γ-(2,3-...

Embodiment 3

[0089] The preparation method of modified graphene oxide of the present invention comprises the following steps:

[0090] 1a) Weighing graphite oxide, ethanol A, catalyst, silane coupling agent and ethanol B, then adding graphite oxide to ethanol A, stirring for 3 hours and then ultrasonically dispersing for 3 hours to obtain a graphene oxide dispersion;

[0091]2a) adding the catalyst to the graphene oxide dispersion obtained in step 1a) to obtain a mixed solution A;

[0092] 3a) Mix the silane coupling agent with ethanol B and stir for 30 minutes to obtain a mixed solution B, then add the mixed solution B to the mixed solution A, and stir and react at 60°C for 12 hours, and then carry out suction filtration and drying to obtain Modified graphene oxide;

[0093] Wherein, the ratio of graphite oxide, ethanol A, catalyst, silane coupling agent and ethanol B is 0.1g:50mL:0.05g:1.5g:10mL.

[0094] The catalyst is a mixture of dicyclohexylcarbodiimide and triphenylphosphine in a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method for modified graphene oxide, an MGO-SiO2 nano-hybrid material and an MGO-SiO2 modified phenolic resin hot melting adhesive film. The preparation method includes the following steps that (1c), the MGO-SiO2 nano-hybrid material is added into a solvent, then ultrasonic dispersion is performed, and MGO-SiO2 dispersion liquid is obtained; (2c), a film forming agent is added into a thermosetting phenolic resin solution, stirring is performed, and a mixed solution D is obtained; (3c), the MGO-SiO2 dispersion liquid obtained in the step (1c) is added into the mixed solution D obtained in the step (2c), stirring is performed so that the MGO-SiO2 dispersion liquid can be evenly dispersed in the mixed solution D, and a mixed solution E is obtained; and (4c), the mixed solution E is subjected to a vacuum constant-temperature stirring reaction at the temperature of 25-80 DEG C, a redundant solvent in the solution E is removed, when viscosity of reaction products is larger than or equal to a preset value, the reaction products are poured out, and the MGO-SiO2 modified phenolic resin hot melting adhesive film is obtained. The phenolic resin hot melting adhesive film prepared through the preparation method has excellent heat resistance and film forming performance, is low in cost, and can be applicable to a dry method prepreg forming process.

Description

technical field [0001] The invention belongs to the technical field of phenolic resin preparation suitable for hot-melt prepreg technology, and relates to a modified graphene oxide, MGO-SiO 2 Nano-hybrid materials and MGO-SiO 2 The invention discloses a preparation method of a modified phenolic resin hot melt adhesive film. Background technique [0002] There are easily oxidized groups (phenolic hydroxyl groups, methylene groups) in the structure of traditional phenolic resin cured products, which affect its heat resistance, and the poor processing performance of phenolic resin also greatly limits its development. In addition, in the dry prepreg molding process, the phenolic resin film has the disadvantages of high brittleness and poor wettability with fibers, while the wet prepreg molding process commonly used in the industry is difficult to accurately control the resin content, high cost, and pollutes the environment Such disadvantages seriously restrict the development ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J161/14C09J175/06C09J175/08C09J175/04C09J175/14C09J11/04C09J7/00C09C1/44C09C3/08C09C3/12C01B32/198
CPCC09J7/00C09J11/04C09J161/14C09C1/44C09C3/006C09C3/08C09C3/12C08L2201/08C08L2205/025C08L2205/035C08K2201/011C09J2461/00C09J2475/00C08L75/06C08K9/06C08K3/36C08K3/04C08L75/08C08L75/04C08L75/14C08L61/14
Inventor 刘育红井新利吕游姜雪雷子萱
Owner XI AN JIAOTONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com