High-temperature-resistant anti-aging rubber material used for hot-water valve seal ring and preparation method thereof

A technology of valve sealing and rubber materials, which is applied in the field of high temperature resistant and anti-aging rubber materials for hot water valve sealing rings and its preparation. It can solve the problems of low hardness of graphite, unfavorable lubrication and anti-friction performance, and easy wear and tear, and achieve wear resistance. Good, improved compatibility and lubricity, and long service life

Inactive Publication Date: 2017-03-22
岳承华
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the hardness of graphite is low and it is easy to wear and tear. Only using graphite as a lubricating component is not conducive to maintaining long-term lubrication and anti-friction performance, and the effect of prolonging the service life of rubber products is limited. It is necessary to improve it

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] A rubber material for high-temperature-resistant and anti-aging hot water valve sealing rings, prepared from the following component raw materials in weight (kg):

[0016] EPDM rubber 100, bismaleimide resin 5, terpene resin 1, silica 60, zinc oxide 2, sulfur S80 1.5, antioxidant MB 1.5, accelerator TMTD 0.3, methyltrimethoxysilane 2. Polyoxyethylene rosin acid 0.3, tetrabutyl titanate 0.5, titanate coupling agent NDZ-401 0.15, nano graphite powder 6, castor oil 4, trinonylphenyl phosphite 0.3.

[0017] A method for preparing a rubber material for a high-temperature-resistant and anti-aging hot water valve sealing ring, comprising the following steps:

[0018] (1) Weigh the raw materials by weight, first add white carbon black to the acetic acid solution with a mass fraction of 4% in a weight ratio of 1:1 and stir for 0.5h to obtain component 1, and then add methyltrimethoxysilane in a weight ratio of 1 :5 mixed with absolute ethanol to obtain component 2, mixed compon...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Shore hardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-temperature-resistant anti-aging rubber material used for a hot-water valve seal ring. The rubber material is composed of the following raw materials in parts by weight: 100 to 120 parts of EPDM rubber, 5 to 10 parts of bismaleimide resin, 1 to 2 parts of terpene resin, 60 to 80 parts of white carbon black, 2 to 4 parts of zinc oxide, 1.5 to 2.5 parts of sulfur S80, 1.5 to 2.5 parts of an anti-aging agent MB, 0.3 to 0.5 part of an accelerator TMTD, 2 to 4 parts of methyltrimethoxysilane, 0.3 to 0.5 part of rosin-polythylene oxide ester, 0.5 to 1 part of tetrabutyl titanate, 0.15 to 0.25 part of a titanate coupling agent NDZ-401, 6 to 8 parts of nanometer graphite powder, 4 to 6 parts of castor oil and 0.3 to 0.5 part of trinonylphenyl phosphite. The rubber material provided by the invention has the advantages of good wear-resistant effect, durable antifriction performance, good high-temperature-resistant and anti-aging performances, long service life, good sealing properties, and applicability to hot-water valve seal ring materials.

Description

technical field [0001] The invention relates to the technical field of rubber materials, in particular to a high-temperature-resistant and anti-aging rubber material for a sealing ring of a hot water valve and a preparation method thereof. Background technique [0002] As an indispensable and important polymer material in the national economy and daily life, rubber has excellent physical and mechanical properties, elasticity and processing properties, and plays an irreplaceable role in many important fields such as automobile transportation, mining, and chemical industry. . Tribological performance is a very important indicator of rubber materials, related to the wear resistance of rubber tire products, the wear resistance of seals, etc. Improving the wear resistance of rubber materials is conducive to increasing its service life, and can bring considerable economic and social benefits in terms of saving energy, materials, lubricants, etc. [0003] At present, one of the m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/16C08L79/08C08L45/00C08K13/06C08K9/10C08K9/06C08K3/36C08K3/22C08K3/06C08K5/40C08K5/5419C08K5/10C08K3/04C08K5/526
CPCC08K2201/011C08L23/16C08L2201/08C08L2205/035C08L79/085C08L45/00C08K13/06C08K9/10C08K9/06C08K3/36C08K2003/2296C08K3/06C08K5/40C08K5/5419C08K5/10C08K3/04C08K5/526
Inventor 岳承华
Owner 岳承华
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products