Ternary denitration sulfur-resistant catalyst in-situ loaded compound filter material and preparation method thereof

A composite filter material and catalyst technology, applied in chemical instruments and methods, separation methods, filtration and separation, etc., can solve the problems of weak binding force between catalyst and filter material fiber, difficult loading of denitrification and anti-sulfur catalyst, uneven catalyst loading, etc. , to achieve uniform and firm loading, improve anti-sulfur activity, and improve low-temperature activity

Active Publication Date: 2017-03-22
FUZHOU UNIV
View PDF6 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, domestic research in this area is almost blank, mainly because the surface of polyphenylene sulfide filter material is smooth and its chemical properties are stable, making it difficult for the denitrification and anti-sulfur catalyst to be loaded on the surface of the filter material.
Moreover, it can be seen from related research at home and abroad that the general method is to directly attach the denitrification and anti-sulfur catalyst to the filter fiber, but the denitrification and anti-sulfur functional composite filter material prepared by this method has insufficient catalyst load. Disadvantages such as uniformity, poor air permeability and weak binding force between the catalyst and the filter fiber

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ternary denitration sulfur-resistant catalyst in-situ loaded compound filter material and preparation method thereof
  • Ternary denitration sulfur-resistant catalyst in-situ loaded compound filter material and preparation method thereof
  • Ternary denitration sulfur-resistant catalyst in-situ loaded compound filter material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] 1) Weigh a piece of polyphenylene sulfide needle felt with a mass of 0.7g, put it into a beaker, then add 0.0273g of sodium lauryl sulfate, and add 50mL of deionized water, and ultrasonicate the solution for 1h ;

[0027] 2) After ultrasonic treatment, add 0.0534g of anhydrous ferric chloride and 0.1226g of cerium chloride heptahydrate to it, ultrasonic or shake until the solute is completely dissolved, then stir at room temperature for 12 hours, so that enough iron ions and cerium ions are adsorbed on the surface of PPS ;

[0028] 3) Slowly pour 50mL of 0.013mol / L potassium permanganate solution into the solution obtained in step 2), and stir the reaction in a water bath at 80°C for 4.5h until the purple color of the solution disappears, which indicates that the reaction is over, take out the filter material , washed repeatedly with deionized water and ethanol several times until the extruded liquid of the filter material is clear, and then dried in an oven at 110°C f...

Embodiment 2

[0031] 1) Weigh a piece of polyphenylene sulfide needle felt with a mass of 0.7g, put it into a beaker, then add 0.0273g of sodium lauryl sulfate, and add 50mL of deionized water, and ultrasonicate the solution for 1h ;

[0032] 2) After ultrasonic treatment, add 0.0801g of anhydrous ferric chloride and 0.1839g of cerium chloride heptahydrate to it, ultrasonic or shake until the solute is completely dissolved, then stir at room temperature for 12 hours, so that enough iron and cerium ions are adsorbed on the surface of PPS;

[0033] 3) Slowly pour 50mL of 0.020mol / L potassium permanganate solution into the solution obtained in step 2), and stir the reaction in a water bath at 80°C for 4.5h until the purple color of the solution disappears, which indicates that the reaction is over, take out the filter material , washed repeatedly with deionized water and ethanol several times until the extruded liquid of the filter material is clear, and then dried in an oven at 110°C for 8-12...

Embodiment 3

[0036] 1) Weigh a piece of polyphenylene sulfide needle felt with a mass of 0.7g, put it into a beaker, then add 0.0273g of sodium lauryl sulfate, and add 50mL of deionized water, and ultrasonicate the solution for 1h ;

[0037]2) After ultrasonic treatment, add 0.1068g of anhydrous ferric chloride and 0.2452g of cerium chloride heptahydrate to it, ultrasonic or shake until the solute is completely dissolved, then stir at room temperature for 12 hours, so that enough iron and cerium ions are adsorbed on the surface of PPS;

[0038] 3) Slowly pour 50mL of 0.026mol / L potassium permanganate solution into the solution obtained in step 2), stir and react in a water bath at 80°C for 4.5h, until the purple color of the solution disappears, which indicates that the reaction is over, take out the filter material , washed repeatedly with deionized water and ethanol several times until the extruded liquid of the filter material is clear, and then dried in an oven at 110°C for 8-12 hours ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Average pore sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a ternary denitration sulfur-resistant catalyst in-situ loaded compound filter material and a preparation method thereof. The preparation method includes: taking a polyphenylene sulfide filter material as a catalyst carrier, and adopting lauryl sodium sulfate for surface modification of a polyphenylene sulfide needled felt to activate the polyphenylene sulfide filter material; taking potassium permanganate, anhydrous ferric chloride and cerium trichloride heptahydrate as catalyst precursors and taking deionized water as a solvent to realize one-step in-situ loading of a MnO2-Fe2O3-CeOx catalyst on the surface of the activated polyphenylene sulfide filter material. The compound filter material is firm in combination of the catalyst and polyphenylene sulfide fibers, excellent in low-temperature activity and denitration effect on nitric oxides in smoke and great in sulfur resistance, and defects of high cost, complexity and the like of a tail purification system in the prior art can be overcome. The ternary denitration sulfur-resistant catalyst in-situ loaded compound filter material and the preparation method thereof have advantages of technical simplicity in preparation, environment friendliness, low production cost and promising application prospect.

Description

technical field [0001] The invention belongs to the technical field of functional composite filter materials, and in particular relates to an in-situ loaded MnO 2 -Fe 2 o 3 -CeO x The invention discloses a composite filter material of a three-way denitrification anti-sulfur catalyst and a preparation method thereof. Background technique [0002] my country is in a stage of rapid economic development, and the demand for energy is huge, especially the demand for electricity is increasing. However, my country's coal-based energy structure determines that my country's electric power is dominated by thermal power, and most of the power plants are coal-fired power plants. Coal-fired power plants produce large amounts of pollutants such as dust, sulfur dioxide and NO x Toxic gas etc. At present, filter bag dust collectors are mainly used in the industry to control a large amount of dust and trace particles produced by coal-fired power plant boilers, and the core is the filter...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B01D39/08B01D53/56B01D53/86
CPCB01D39/083B01D53/8628B01D2239/0208B01D2239/0492B01D2239/0604B01D2239/10B01D2255/2065B01D2255/2073B01D2255/20738
Inventor 郑玉婴付彬彬
Owner FUZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com