Preparation method of wood-plastic composite material aid

A wood-plastic composite material and additive technology, applied in the field of composite materials, can solve problems such as poor mechanical properties, and achieve the effects of improving crystallinity, wide application fields and improving heat transfer performance.

Active Publication Date: 2017-02-01
东莞市振中塑胶有限公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The invention provides a preparation method of additives for wood-plastic composite materials, which solves the problem of poor mechanical properties of existing wood-plastic composite materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of wood-plastic composite material aid

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0019] The present invention provides a method for preparing wood-plastic composite additives. In order to make the purpose, technical solution and effect of the present invention clearer and clearer, the present invention will be further described in detail below.

[0020] A wood-plastic composite additive is an alumina-aluminum nitride composite heat-conducting ceramic composed of alumina heat-conducting ceramics and aluminum nitride heat-conducting ceramics;

[0021] The alumina-aluminum nitride composite heat-conducting ceramic is prepared according to the following steps:

[0022] 1) The original powders of alumina and aluminum nitride with a purity of more than 99.9% are mixed according to a weight ratio of 1:1, added with absolute ethanol, mixed by wet ball milling for 6-8 hours, and pre-dried in an atmosphere at 1100-1150°C after drying. Burn for 6h;

[0023] 2) Add dehydrated ethanol to the powder obtained in step 1), then wet ball mill and mix for 8-10 hours, and ad...

Embodiment 1

[0027] A wood-plastic composite additive is an alumina-aluminum nitride composite heat-conducting ceramic composed of alumina heat-conducting ceramics and aluminum nitride heat-conducting ceramics;

[0028] The alumina-aluminum nitride composite heat-conducting ceramic is prepared according to the following steps:

[0029] 1) The original powders of alumina and aluminum nitride with a purity of more than 99.9% are mixed according to a weight ratio of 1:1, added with absolute ethanol, mixed by wet ball milling for 7 hours, dried and pre-fired in an atmospheric atmosphere at 1125°C for 6 hours;

[0030] 2) Add dehydrated ethanol to the powder prepared in step 1), then wet ball mill and mix for 9 hours, and add 4% BaCu(B 2 o 5 ), 2% La 2 o 3 and 2% Y 2 o 3 well mixed;

[0031] 3) In the powder obtained in step 2), add 3% polyvinyl alcohol solution and 3% carbon powder in an amount accounting for the total mass of the powder, and after granulation, press molding again, where...

Embodiment 2

[0034] A wood-plastic composite additive is an alumina-aluminum nitride composite heat-conducting ceramic composed of alumina heat-conducting ceramics and aluminum nitride heat-conducting ceramics;

[0035] The alumina-aluminum nitride composite heat-conducting ceramic is prepared according to the following steps:

[0036] 1) The original powders of alumina and aluminum nitride with a purity of more than 99.9% are mixed according to a weight ratio of 1:1, added with absolute ethanol, mixed by wet ball milling for 6 hours, and pre-fired in an atmosphere at 1100 ° C for 6 hours after drying;

[0037] 2) Add dehydrated ethanol to the powder obtained in step 1), then wet ball mill and mix for 8 hours, and add 2% BaCu(B 2 o 5 ), 1% La 2 o 3 and 1% of Y 2 o 3 well mixed;

[0038] 3) In the powder obtained in step 2), add 3% polyvinyl alcohol solution and 3% carbon powder in an amount accounting for the total mass of the powder, and after granulation, press molding again, where...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of a wood-plastic composite material aid. The aid is aluminum oxide-aluminum nitride composite heat-conducting ceramic composed of aluminum oxide heat-conducting ceramic and aluminum nitride heat-conducting ceramic. The preparation method mainly comprises the following steps: ball milling, calcination, ball milling, granulation, sintering, pulverization and the like. By adding the aluminum oxide-aluminum nitride composite heat-conducting ceramic, the wood-plastic composite material can have favorable mechanical properties and low water absorptivity, and thus, has wider application range and longer service life. Besides, the aluminum oxide-aluminum nitride composite heat-conducting ceramic has a certain porous structure, and thus, can adsorb harmful gas and purify air, thereby being beneficial to environmental protection. Therefore, the preparation method of the wood-plastic composite material aid has great development potential.

Description

technical field [0001] The invention relates to a preparation method of wood-plastic composite material additives, belonging to the technical field of composite materials. Background technique [0002] Wood-plastic composites (Wood-Plastic Composites, WPC) use thermoplastics as a matrix, pretreated plant powder or wood fiber as a filler or reinforcement, and are mixed with various additives required in a certain proportion. A composite material prepared by extrusion, lamination, molding or injection molding. It has good elastic modulus, compression resistance, bending resistance, durability and other properties, and also has the characteristics of raw material resources, cost economy, product plasticization, environmental protection and recycling. Therefore, wood-plastic composite materials are widely used in many fields. [0003] At present, research on wood-plastic composites focuses on improving interfacial compatibility and improving processing technology to obtain mat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B38/06C04B35/10C04B35/582C04B35/622C04B35/634
CPCC04B35/10C04B35/581C04B35/622C04B35/63416C04B38/068C04B2235/3215C04B2235/3225C04B2235/3227C04B2235/3281C04B2235/3409C04B2235/96C04B2235/9607
Inventor 严秀芹陆绍荣曾岑罗崇禧谢超卢李勤
Owner 东莞市振中塑胶有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com