Quick-hardening anti-seepage joint mixture

A technology of caulking agent and water-repellent agent, which is applied in the field of fast-hardening and anti-seepage caulking agent, which can solve the problems of long hardening time and insufficient strength of caulking agent, and achieve the effect of increasing the construction speed

Inactive Publication Date: 2017-01-04
上海亚瓦新型建筑材料有限公司
View PDF1 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the caulk is still not strong enough and takes a long time to harden

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Quick-hardening anti-seepage joint mixture

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-5

[0024] This embodiment provides a fast-hardening anti-seepage sealant, including the components shown in Table 1 in parts by weight.

[0025] The preparation method is as follows: clean the mixing equipment, otherwise, clean the mixing equipment; add cement and filler first; add other additives during the stirring process, stir for more than 10-20 minutes, and mix evenly.

[0026] Table 1. Components and parts by weight of the fast-hardening anti-seepage sealant described in Examples 1-5

[0027] components Example 1 Example 2 Example 3 Example 4 Example 5 52.5 Ordinary Portland cement 23 32 4 11 0 FONDU aluminate cement 7 9 14 19 30 Anhydrite 2 5 9 8 5 70-140 mesh quartz sand 64 60 67 65 62 30us 0.2 0.2 0.4 0.2 0.5 Redispersible latex powder 7 8 7 10 7 calcium formate 0.2 0.4 0.25 0.5 0.35 Hydrophobic agent 1 1 1.2 1.5 1.8

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a quick-hardening anti-seepage joint mixture. The quick-hardening anti-seepage joint mixture is prepared from, by weight, 7-15 parts of high-alumina cement, 30-45 parts of ordinary portland cement, 2-10 parts of gypsum, 60-65 parts of quartz sand, 1-3 parts of a water repellent, 0.2-0.8 part of methyl hydroxypropyl cellulose ether, 7-9 parts of redispersible latex powder, 0.2-1.0 part of a water-soluble organic compound early strength agent and 0.05-0.2 part of an alkyl-carboxyl retarder. By bonding the components of ordinary portland cement, high-alumina cement and gypsum and adding a series of additives such as the water repellant and a water reducer, the quick-hardening anti-seepage effect of the joint mixture can be achieved. The bonding strength of the prepared joint mixture can meet the industry regulation requirement within 24 h, the high-strength joint mixture increases the construction speed and accelerates the construction progress, and due to the good anti-seepage property, the waterproofing and saltpetering preventing properties of the product are better optimized.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a fast-hardening anti-seepage caulking agent. Background technique [0002] The laying of ceramic tiles has become a common decoration in daily life. From home to hotels and other public places, from the ground to the wall, the decorative effect brought by ceramic tiles is beautiful. However, in the process of laying and laying, bricks and The gaps between the bricks require special treatment. The sealants commonly used to fill the gaps between tiles are easy to get dirty and black, low in strength, and powdery. [0003] In the prior art, CN105198312A discloses a tile grouting agent, the weight ratio of raw materials is: ordinary Portland cement (P.042.4R) 35-60, quartz sand 30-65, mineral oil type defoaming Agent 0.01-0.2, redispersible latex powder 10-30, hydroxypropyl methylcellulose 0.1-0.5, silicone water repellent 0.2-1, anti-efflorescence agent 0.2-1, anhydrou...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/06C04B111/20C04B111/27
CPCC04B28/06C04B2111/00293C04B2111/00672C04B2111/2023C04B2111/27C04B2201/50
Inventor 黄海涛
Owner 上海亚瓦新型建筑材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com