Heat-resistant and high-strength concrete having gradient enclosing structure, and preparation method thereof

A high-strength concrete and heat-resistant concrete technology, which is applied in the field of building materials, can solve the problems of rapid strength loss and achieve the effects of improving interface bonding force, increasing heat and moisture transmission channels, and compact structure

Active Publication Date: 2016-11-16
HUBEI UNIV
View PDF2 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the shortcomings of the existing ordinary silicate heat-resistant concrete in high-temperature environments such as rapid strength loss, the present invention proposes a heat-resistant high-strength concrete with a gradient enclosure structure and a preparation method thereof, which can effectively improve the heat resistance of concrete and reduce the Concrete Strength Loss Rate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Heat-resistant and high-strength concrete having gradient enclosing structure, and preparation method thereof
  • Heat-resistant and high-strength concrete having gradient enclosing structure, and preparation method thereof
  • Heat-resistant and high-strength concrete having gradient enclosing structure, and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A heat-resistant high-strength concrete with a gradient maintenance structure, which is composed of an inner layer of high-strength heat-resistant concrete and an outer layer of high-heat-resistant concrete from the inside to the outside (see figure 1 ), where the ratio of the cross-sectional area of ​​the outer layer of high heat-resistant concrete to the inner layer of high-strength heat-resistant concrete is 1:2.5. The mix proportions of the inner high-strength heat-resistant concrete and the outer high-heat-resistant concrete are shown in Table 1 and Table 2 respectively; the test results are shown in Table 3.

[0035] Table 1 The mix ratio of the inner high-strength heat-resistant concrete in Example 1 (kg / m 3 )

[0036]

[0037] Among them, shale ceramsite is used as the light aggregate for internal maintenance, and the bulk density is 830kg / m 3 , simple compressive strength 2.5Mpa, saturated with water 24 hours before the test to drain the water, the additio...

Embodiment 2

[0045] A heat-resistant high-strength concrete with a gradient maintenance structure, which is composed of an inner layer of high-strength heat-resistant concrete and an outer layer of high-heat-resistant concrete from the inside to the outside (see figure 2 ), wherein the ratio of the cross-sectional area of ​​the outer layer of high heat-resistant concrete to the inner layer of high-strength heat-resistant concrete is 1:3.5; the mix ratios of the inner layer of high-strength heat-resistant concrete and the outer layer of high-heat-resistant concrete are shown in Table 4 and Table 5 respectively; The test results are shown in Table 6.

[0046] The mixing ratio of the inner high-strength heat-resistant concrete in Example 2 in Table 4 (kg / m 3 )

[0047]

[0048] Among them, shale ceramsite is used as light aggregate with a bulk density of 750kg / m 3 , simple compressive strength 3.0Mpa, saturated with water 24 hours before the test to drain the water, the addition amount ...

Embodiment 3

[0056] A heat-resistant high-strength concrete with a gradient maintenance structure, which is composed of an inner layer of high-strength heat-resistant concrete and an outer layer of high-heat-resistant concrete from the inside to the outside (see image 3 ), wherein the ratio of the cross-sectional area of ​​the outer layer of high heat-resistant concrete to the inner layer of high-strength heat-resistant concrete is 1:3; the mix ratios of the inner layer of high-strength heat-resistant concrete and the outer layer of high-heat-resistant concrete are shown in Table 7 and Table 8 respectively; The test results are shown in Table 9.

[0057] The mixing ratio of the inner high-strength heat-resistant concrete in Example 3 in Table 7 (kg / m 3 )

[0058]

[0059] Among them, clay ceramsite is used as the light aggregate for internal maintenance, and the bulk density is 950kg / m 3 , simple compressive strength 3.5Mpa, saturated with water for 24 hours before the test to drain ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Bulk densityaaaaaaaaaa
Bulk densityaaaaaaaaaa
Bulk densityaaaaaaaaaa
Login to View More

Abstract

The present invention discloses a heat-resistant and high-strength concrete having a gradient enclosing structure. The heat-resistant and high-strength concrete comprises an inner layer high-strength and heat-resistant concrete and an outer layer high heat-resistant concrete from inside to outside, wherein the inner layer high-strength and heat-resistant concrete adopts a silicate-based cement, fly ash, mineral powder, river sand, basalt graded gravel, toughening fiber, a polycarboxylic acid water reducing agent, an inner curing light aggregate and water as raw materials, and the outer layer high heat-resistant concrete adopts an aluminum-based cement, aluminum sand, aluminum stone, hollow fiber, a polycarboxylic acid water reducing agent, an inner curing light aggregate and water as raw materials. According to the present invention, the gradient enclosing structure is designed, such that the generated calcium aluminate and the generated dicalcium aluminate in the outer layer high heat-resistant concrete in the high temperature environment can be converted into the non-hydrated alumina ceramic phase at the high temperature, and the non-hydrated alumina ceramic phase is firmly bonded with the aluminum stone, the aluminum sand and the like so as to significantly increase the high-temperature resistance; and the large doping amount of the fly ash and the mineral powder are used in the inner layer high-strength and heat-resistant concrete, such that the durability is ensured, and the disadvantages of rapid strength loss in the high temperature environment and the like of the existing ordinary silicate heat-resistant concrete can be effectively solved.

Description

technical field [0001] The invention belongs to the technical field of building materials, and in particular relates to a gradient enclosure structure heat-resistant concrete and a preparation method thereof. Background technique [0002] Heat-resistant concrete refers to a special high-strength concrete whose physical and mechanical properties are not damaged under the long-term action of high temperature of 200-1300 ° C, and has good resistance to rapid cooling and rapid heating, and has small drying shrinkage and deformation under high temperature. Traditional heat-resistant concrete mostly uses ordinary Portland cement, slag Portland cement, etc. as cementitious materials, and uses crushed natural rock as aggregate. Concrete forms a solid structure after hardening, but the content of alkali such as calcium hydroxide is high, and it will be decomposed into calcium oxide and water at a high temperature of 500 ° C, making the volume of concrete shrink, and then the volume o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/04C04B28/06C04B14/06C04B14/14C04B18/08C04B18/12C04B16/06C04B14/48C04B14/38C04B14/42C04B103/30
CPCC04B28/04C04B28/06C04B2111/763C04B18/08C04B18/12C04B14/068C04B14/14C04B16/0633C04B2103/302C04B14/303C04B14/48C04B16/0683C04B14/4656C04B14/42Y02W30/91
Inventor 黄修林卞周宏黄绍龙彭波唐涛金帆罗霄
Owner HUBEI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com