Mould-proof medical stone modified paperboard and preparation method thereof
A medical stone and modified technology, applied in the field of cardboard, can solve the problems of destroying the waterproof effect of the coating layer, reducing the mechanical strength of the carton, and reducing the quality of the product.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
preparation example Construction
[0016] The invention provides a preparation method of a mildew-proof cardboard modified by medical stone, comprising:
[0017] 1) placing the Chinese herbal medicine in water and decocting to obtain the process of the Chinese herbal medicine extract;
[0018] 2) in the presence of ultraviolet rays, medical stone, plant ash, sodium chloroplatinate and molybdenum disulfide are activated to obtain the operation of the activator;
[0019] 3) under acidic conditions, mixing the activator with the amino acid and carrying out modification treatment to obtain the modified activator;
[0020] 4) Contact reaction with acrylic emulsion, polystyrene, dioctyl phthalate, aluminum oxide, boron nitride and sodium nitrite, and then add emulsifier, modified activator, Chinese herbal medicine to the reaction system The process of mixing liquid to obtain anti-mildew coating;
[0021] 5) the process of applying the anti-mildew coating to the surface of the cardboard body and drying to obtain the...
Embodiment 1
[0035] 1) Mix Artemisia argyi, Baiwei, Borneo, Fried Suzi, Chuanxiong, Codonopsis, Angelica, Pueraria, Gualoupi, Coptidis, and water according to 100:80:48:58:33:95:42:31:35:95: 600 in a weight ratio of 600, and decocted at 160°C for 5 hours to obtain a Chinese herbal medicine extract;
[0036] 2) In the presence of ultraviolet rays with a wavelength of 230 nm, mix medical stone, plant ash, sodium chloroplatinate and molybdenum disulfide in a weight ratio of 100:59:19:36, and perform an activation treatment at 80°C for 14 hours to obtain activated thing;
[0037] 3) Under the condition of pH 5, the activated product is mixed with amino acid (weight ratio 100:55) and modified at 55°C for 8 hours to obtain the modified activated product;
[0038] 4) Mix acrylic emulsion, polystyrene (weight-average molecular weight of 5000), dioctyl phthalate, aluminum oxide, boron nitride and sodium nitrite, and heat the mixture at 100°C and under the condition of vacuum degree of 8MPa The co...
Embodiment 2
[0042] 1) Mix Artemisia argyi, Baiwei, Borneol, Fried Suzi, Chuanxiong, Codonopsis, Angelica, Pueraria, Gualoupi, Coptis chinensis, and water according to 100:70:42:55:24:80:36:22:29:88: 400 weight ratio, and decocted at 150°C for 4 hours to obtain Chinese herbal medicine extract;
[0043] 2) In the presence of ultraviolet rays with a wavelength of 200 nm, mix medical stone, plant ash, sodium chloroplatinate and molybdenum disulfide in a weight ratio of 100:55:14:32, and perform activation treatment at 75 ° C for 12 hours to obtain activated thing;
[0044] 3) Under the condition of pH 4, the activated product is mixed with amino acid (weight ratio 100:47), and then modified and treated at 50°C for 6 hours to obtain the modified activated product;
[0045] 4) Mix acrylic emulsion, polystyrene (weight-average molecular weight of 3000), dioctyl phthalate, aluminum oxide, boron nitride and sodium nitrite, and set it at 95°C and under the condition of vacuum degree of 5MPa The con...
PUM
Property | Measurement | Unit |
---|---|---|
wavelength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com