Polymer alkali-resisting mortar and production method thereof

A polymer and high molecular polymer technology, applied in the field of building materials, can solve the problems of low base adhesion, low impermeability, poor construction performance, etc., and achieve high adhesion, high impermeability and construction performance. Good results

Inactive Publication Date: 2016-11-09
北京中德新亚建筑技术有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In order to solve the problems of low impermeability level, poor alkali resistance, poor construction performance, low adhesion to the base layer, and prone to hollowing and cracking of similar products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polymer alkali-resisting mortar and production method thereof
  • Polymer alkali-resisting mortar and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0032] A polymer alkali-resistant mortar and its manufacturing technology. The components and mass parts of this polymer alkali-resistant mortar are as follows: 300 parts of cement, 600 parts of alkali-resistant fine aggregate, 30 parts of compound alkali-resistant compacting agent, 1250 mesh 40 parts of heavy calcium, 15 parts of anti-saponification polymer, 3 parts of high molecular polymer, 5 parts of water reducer, 2 parts of early strength agent, and 2 parts of thixotropic agent. The cement is 52.5-grade Portland cement, the alkali-resistant fine aggregate is limestone or dolomite mechanism sand, the saponification-resistant polymer is imported saponification-resistant redispersible latex powder, and the high molecular polymer It is hydroxypropyl methylcellulose (HPMC), the water reducer is calcium lignosulfonate, the early strength agent is calcium formate, and the thixotropic agent is a special thixotropic agent for imported 602 dry-mixed mortar.

[0033] The manufactur...

example 2

[0042] A polymer alkali-resistant mortar and its manufacturing technology. The components and mass parts of this polymer alkali-resistant mortar are as follows: 290 parts of cement, 610 parts of alkali-resistant fine aggregate, 25 parts of compound alkali-resistant compacting agent, 1250 parts 45 parts of heavy calcium, 15 parts of anti-saponification polymer, 3 parts of high molecular polymer, 5 parts of water reducer, 2 parts of early strength agent, and 2 parts of thixotropic agent. The cement is 52.5-grade Portland cement, the alkali-resistant fine aggregate is limestone or dolomite mechanism sand, the saponification-resistant polymer is imported saponification-resistant redispersible latex powder, and the high molecular polymer It is hydroxypropyl methylcellulose (HPMC), the water reducer is calcium lignosulfonate, the early strength agent is calcium formate, and the thixotropic agent is a special thixotropic agent for imported 602 dry-mixed mortar.

[0043] The manufactu...

example 3

[0046]A polymer alkali-resistant mortar and its manufacturing technology. The components and mass parts of this polymer alkali-resistant mortar are as follows: 310 parts of cement, 590 parts of alkali-resistant fine aggregate, 25 parts of compound alkali-resistant compacting agent, 1250 parts 45 parts of heavy calcium, 15 parts of anti-saponification polymer, 3 parts of high molecular polymer, 5 parts of water reducer, 2 parts of early strength agent, and 2 parts of thixotropic agent. The cement is 52.5 grade Portland cement, the alkali-resistant fine aggregate is limestone or dolomite mechanism sand, the saponification-resistant polymer is imported saponification-resistant redispersible latex powder, and the high molecular polymer It is hydroxypropyl methylcellulose (HPMC), the water reducer is calcium lignosulfonate, the early strength agent is calcium formate, and the thixotropic agent is a special thixotropic agent for imported 602 dry-mixed mortar.

[0047] The manufactur...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses polymer alkali-resisting mortar and a production method thereof. The polymer alkali-resisting mortar is prepared from the following components in parts by mass: 250-550 parts of cement, 250-650 parts of alkali-resisting fine aggregate, 20-40 parts of a compounding alkali-resisting compacting agent, 30-50 parts of 1250-mesh ground calcium powder, 10-20 parts of a saponification-resisting polymer, 2-6 parts of a macromolecule polymer, 3-7 parts of a water reducing agent, 1-5 parts of an early strength agent and 1-3 parts of a thixotropic agent. Compared with similar products and the prior art, the polymer alkali-resisting mortar disclosed by the invention is good in alkali resistance, good in construction property, high in base layer cohering force, and free from hollowing and cracking.

Description

technical field [0001] The invention belongs to the technical field of building materials, and relates to a polymer alkali-resistant mortar and a preparation method thereof. Background technique [0002] Ordinary alkali-resistant mortar has the following problems: 1. Low impermeability level, which leads to a discount in its alkali resistance; 2. Poor adhesion to the base layer, which is easy to cause hollowing or even the alkali-resistant mortar layer to fall off; 3. Low self-cohesion, Hanging phenomenon is easy to occur during construction, and the construction performance is not good; 4. Poor water retention, easy to shrink and crack. Contents of the invention [0003] In order to solve the problems of low impermeability level, poor alkali resistance, poor construction performance, low adhesion with the base layer, and prone to hollowing and cracking of similar products. The invention provides a polymer alkali-resistant mortar and a preparation method thereof. [0004...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B111/20C04B111/27
CPCC04B28/04C04B2111/20C04B2111/27C04B2201/50
Inventor 王学振
Owner 北京中德新亚建筑技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com