Anti-fading treatment process for rattan for rattan-plaited handiwork
A treatment process and anti-fading technology, applied in the field of processing raw materials for rattan products, can solve the problems affecting the aesthetics of rattan handicrafts, the color of rattan, and the color of rattan, etc., to enhance antioxidant capacity, increase phosphorus content, The effect of stable fiber structure
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0019] An anti-fading treatment process of rattan for rattan handicrafts, comprising the steps of:
[0020] (1) First select the vigorous vines, then apply accelerator to the bamboo roots of the vines, harvest the rattans after 2 days, remove the branches and leaves of the rattans, and put the freshly harvested rattans in a freezer at -18°C in time 4 hours, spare;
[0021] (2) Take out the rattan after freezing, carry out high temperature treatment for 40 minutes, the treatment temperature is 140 ℃, then place in a closed pressure treatment tank and carry out high pressure treatment, the initial stage is to process under inert gas atmosphere, the treatment pressure is 3MPa, After 10 minutes of treatment, release the pressure until it reaches 0.8MPa, and then fill the pressure treatment tank with anti-fading steam. After the pressure rises to 3.2MPa, take out the rattan after keeping the pressure for 70 minutes, and set aside;
[0022] (3) the rattan after the high-pressure tr...
Embodiment 2
[0029] An anti-fading treatment process of rattan for rattan handicrafts, comprising the steps of:
[0030] (1) First select vigorous vines, then apply accelerator to the bamboo roots of the vines, harvest the rattans after 2 days, remove the branches and leaves of the rattans, and put the freshly harvested rattans in a freezer at -15°C in time 3 hours, spare;
[0031] (2) Take out the rattan after freezing, carry out high-temperature treatment for 30 minutes, the treatment temperature is 130 ℃, then place in a closed pressure treatment tank and carry out high-pressure treatment, the initial stage is to process under an inert gas atmosphere, and the treatment pressure is 2MPa, After 10 minutes of treatment, release the pressure until it reaches 0.5MPa, and then fill the pressure treatment tank with anti-fading steam. After the pressure rises to 3MPa, take out the rattan after keeping the pressure for 50 minutes, and set aside;
[0032] (3) the rattan after the high-pressure t...
Embodiment 3
[0039] An anti-fading treatment process of rattan for rattan handicrafts, comprising the steps of:
[0040] (1) First select the vigorous vines, then apply accelerator to the bamboo roots of the vines, harvest the rattans after 3 days, remove the branches and leaves of the rattans, and put the freshly harvested rattans in a freezer at -20°C in time for 5 hours, spare;
[0041] (2) Take out the rattan after freezing, carry out high temperature treatment for 50 minutes, the treatment temperature is 150 ℃, then place in a closed pressure treatment tank and carry out high pressure treatment, the initial stage is to process under inert gas atmosphere, the treatment pressure is 5MPa, After 10 minutes of treatment, release the pressure until it reaches 1MPa, and then fill the pressure treatment tank with anti-fading steam. After the pressure rises to 3.5MPa, take out the rattan after keeping the pressure for 80 minutes, and set aside;
[0042] (3) the rattan after the high-pressure ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com