Water-soluble high-temperature-resistant coating and preparation method thereof

A high temperature resistant coating, water-soluble technology, applied in the field of coatings, can solve the problems of long surface drying time of the paint film, affecting the appearance of the paint film, poor corrosion resistance, etc., and achieves the effect of easy operation, broad application prospects and excellent anti-corrosion effect.

Inactive Publication Date: 2016-08-24
HUANGHE S & T COLLEGE
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, there are many reports on heat-resistant coatings, and the temperature resistance of existing high-temperature-resistant coatings can basically meet the requirements for use, but there are some shortcomings.
For example, the surface drying time of the paint film is long, which will affect the appearance of the paint film due to dust and other reasons during use; most of the high-temperature resistant coatings on the market use hexavalent chromium as a corrosion inhibitor, which will cause great harm to the environment; corrosion resistance at high temperatures Disadvantages such as poor sex

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-soluble high-temperature-resistant coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Embodiment 1 of the present invention provides a water-soluble high-temperature-resistant coating, which includes the following raw materials in parts by weight: 8 parts of aluminum sol, 15 parts of aluminum dihydrogen phosphate, 8 parts of glass powder, 5 parts of talcum powder, 10 parts of kaolin powder, silicon 10 parts of limestone powder, 1 part of dicyclopentenyloxyethyl acrylate and 20 parts of water, wherein, each raw material in this embodiment is industrial grade.

[0020] Preparation method: Under the condition of 40°C, uniformly mix aluminum sol, aluminum dihydrogen phosphate and water to form the first mixed solution; add glass powder, talc powder, wollastonite powder and kaolin powder to the first mixed solution , and ultrasonically dispersed for 30 minutes to obtain a second mixed solution; dicyclopentenyloxyethyl acrylate was added to the second mixed solution, and stirred at a speed of 1200r / min for 6 hours at 40°C , to prepare the water-soluble high-te...

Embodiment 2

[0022] Embodiment 2 of the present invention provides a water-soluble high-temperature-resistant coating, which includes the following raw materials in parts by weight: 9 parts of aluminum sol, 16 parts of aluminum dihydrogen phosphate, 10 parts of glass powder, 7 parts of talcum powder, 12 parts of kaolin powder, silicon 11 parts of limestone powder, 2 parts of dicyclopentenyloxyethyl acrylate and 23 parts of water, wherein, each raw material in this embodiment is industrial grade.

[0023] Preparation method: Under the condition of 50°C, uniformly mix aluminum sol, aluminum dihydrogen phosphate and water to form the first mixed solution; add glass powder, talc powder, wollastonite powder and kaolin powder to the first mixed solution , and ultrasonically dispersed for 30 minutes to obtain a second mixed solution; dicyclopentenyloxyethyl acrylate was added to the second mixed solution, and stirred at a speed of 1100r / min for 6 hours at 50°C , to prepare the water-soluble high-...

Embodiment 3

[0025] Embodiment 3 of the present invention provides a water-soluble high-temperature-resistant coating, which includes the following raw materials in parts by weight: 10 parts of aluminum sol, 17 parts of aluminum dihydrogen phosphate, 11 parts of glass powder, 8 parts of talcum powder, 13 parts of kaolin powder, silicon 13 parts of limestone powder, 2 parts of dicyclopentenyloxyethyl acrylate and 25 parts of water, wherein, each raw material in this embodiment is industrial grade.

[0026] Preparation method: Under the condition of 60°C, uniformly mix aluminum sol, aluminum dihydrogen phosphate and water to form the first mixed solution; add glass powder, kaolin powder, wollastonite powder and talc powder to the first mixed solution , and ultrasonically dispersed for 35 minutes to obtain a second mixed solution; dicyclopentenyloxyethyl acrylate was added to the second mixed solution, and stirred at a speed of 1000r / min for 5 hours under the condition of 60°C , to prepare th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a water-soluble high-temperature-resistant coating. The water-soluble high-temperature-resistant coating comprises, by weight, 8-12 parts of aluminum sol, 15-20 parts of aluminum dihydrogen phosphate, 8-14 parts of ground glass, 5-10 parts of talcum powder, 10-15 parts of kaolin powder, 10-15 parts of wollastonite powder, 1-5 parts of dicyclopenteneoxyethyl acrylate and 20-30 parts of water. The invention also discloses a preparation method of the water-soluble high-temperature-resistant coating. With all components in the water-soluble high-temperature-resistant coating matched mutually and complementing mutual advantages, the water-soluble high-temperature-resistant coating has the advantages of excellent corrosion prevention performance, resistance to high temperature and cracking, thermal shock resistance, good storage stability and the like on the premise of keeping good adhesive force.

Description

technical field [0001] The invention belongs to the technical field of coatings, in particular to a water-soluble high-temperature resistant coating and a preparation method thereof. Background technique [0002] With the rapid development of modern industry and national defense construction (such as aerospace, aviation, weapons, etc.), the requirements for high-temperature resistant coatings for equipment are getting higher and higher. Physical and mechanical properties and anti-corrosion properties. [0003] High temperature resistant coatings, also known as heat resistant coatings, generally refer to coatings that can maintain proper physical and mechanical properties without discoloration or falling off of the paint film above 200°C, so that the protected objects can function normally in high temperature environments Special functional coatings. Therefore, high-temperature resistant coatings are widely used in high-temperature places such as steel chimneys, high-temper...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D1/00C09D5/18C09D7/12
CPCC09D1/00C09D5/18C09D7/61C09D7/63
Inventor 高德峰刘德波王瑞利于书淳李淑君江振西张鑫
Owner HUANGHE S & T COLLEGE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More