Thorium dioxide powder and method for determining nitrogen content in core block

A kind of technology of thorium dioxide and determination method, applied in the field of chemical detection

Inactive Publication Date: 2016-07-27
CHINA NUCLEAR BAOTOU GUANGHUA CHEM IND
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There is no relevant report on the measurement of nitrogen content in thorium dioxide pellets

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Thorium dioxide powder and method for determining nitrogen content in core block
  • Thorium dioxide powder and method for determining nitrogen content in core block

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A method for determining nitrogen content in thorium dioxide powder and pellets, comprising the steps of:

[0036] The first step: sample preparation;

[0037] The thorium dioxide pellet sample was ground, sieved to make the particle size of the sample smaller than 150 μm, and the sample was stored in a dry polyethylene bottle.

[0038] The second step: sample dissolution;

[0039] Weigh 0.1 g of the powder sample obtained from the first step of grinding, accurate to 0.0001 g. Put it in a 100mL beaker, add 5mL hydrochloric acid, 1mL hydrogen peroxide, the hydrochloric acid here is superior grade, the density is 1.15g / cm 3 , where the hydrogen peroxide is superior grade pure, and the mass percent is 30%. Heat it to 350°C, and when the sample starts to react, add 0.05mL of 3 After the reaction is still, add 0.15mL of 30% pure hydrogen peroxide, and dissolve until the solution becomes clear. Continue heating to completely decompose hydrogen peroxide. Remove and let c...

Embodiment 2

[0049] A method for determining nitrogen content in thorium dioxide powder and pellets, comprising the steps of:

[0050] The first step: sample preparation;

[0051] The thorium dioxide pellet sample was ground, sieved to make the particle size of the sample smaller than 150 μm, and the sample was stored in a dry polyethylene bottle.

[0052] The second step: sample dissolution;

[0053] Weigh 0.5 g of the powder sample obtained from the first step of grinding, accurate to 0.0001 g. Put it in a 100mL beaker, add 5.5mL hydrochloric acid, 1mL hydrogen peroxide, the hydrochloric acid here is superior grade, the density is 1.15g / cm 3 , where the hydrogen peroxide is superior grade pure, and the mass percent is 30%. Heat it to 400°C, and when the sample starts to react, add 0.075mL of 3 0.35 mL of high-grade pure hydrofluoric acid with a mass percentage of 30% was added after the reaction was still, and dissolved until the solution became clear. Continue heating to completely...

Embodiment 3

[0060] A method for determining nitrogen content in thorium dioxide powder and pellets, comprising the steps of:

[0061] The first step: sample preparation;

[0062] The thorium dioxide pellet sample was ground, sieved to make the particle size of the sample smaller than 150 μm, and the sample was stored in a dry polyethylene bottle.

[0063] The second step: sample dissolution;

[0064] Weigh 1.0 g of the powder sample obtained from the first step of grinding, accurate to 0.0001 g. Put in a 100mL beaker, add 6mL hydrochloric acid, 1mL hydrogen peroxide, the hydrochloric acid here is superior grade, density is 1.15g / cm 3 , where the hydrogen peroxide is superior grade pure, and the mass percent is 30%. Heat it to 450°C, and when the sample starts to react, add 0.1mL of 3 After the reaction is still, add 0.5mL of 30% pure hydrogen peroxide, and dissolve until the solution becomes clear. Continue heating to completely decompose hydrogen peroxide. Remove and let cool.

[...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of chemical detection technology, and concretely relates to thorium dioxide powder and a method for determining nitrogen content in a core block; and the invention aims at providing the thorium dioxide powder and the method for determining nitrogen content in the core block. The method comprises the following steps: preparation of a sample, dissolving of the sample, distillation and separation of nitrogen, and determination. The trace amount of nitrogen in thorium dioxide is determined by using a Nessler's reagent-spectrophotometry method; dissolving conditions, distillation time, distillation volume, addition of a color developing agent, and developing time of the powder shaped sample are provided; when the sample amount is 0.1-1.0g, the method precision is better than 5%, and the recovery rate is 96-105%.

Description

technical field [0001] The invention belongs to the technical field of chemical detection, and in particular relates to a method for measuring nitrogen content in thorium dioxide powder and pellets. Background technique [0002] Thorium is a fissile material obtained by multiplication. Thorium dioxide is the only stable oxide in thorium, which can form a solid solution with uranium dioxide or plutonium dioxide in any proportion, and can be used as nuclear fuel for light water reactors, heavy water reactors and liquid metal-cooled fast breeder reactors. There is no related report on the measurement of nitrogen content in thorium dioxide pellets. Contents of the invention [0003] The object of the present invention is to provide a method for measuring nitrogen content in thorium dioxide powder and pellets. [0004] The present invention is achieved like this: [0005] A method for determining nitrogen content in thorium dioxide powder and pellets, comprising the steps of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): G01N21/78G01N21/31G01N1/28
Inventor 杨永明刘丽莎
Owner CHINA NUCLEAR BAOTOU GUANGHUA CHEM IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products