Hot rolled steel sheet for hot press forming having low deviation of mechanical property and excellent formability and corrosion resistance hot pressed part using the same and method for manufacturing thereof

A technology of hot-rolled steel sheet and hot-press forming, which is applied in the field of hot-rolled steel sheet for hot-press forming and hot-press formed products, which can solve the problems of poor processing and non-disclosure, and achieve small material deviation, excellent formability and corrosion resistance Effect

Active Publication Date: 2016-07-06
浦项股份有限公司
View PDF11 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the technique relates to a thermoformed product obtained by thermoforming a cold-rolled or hot-rolled steel sheet obtained through an existing rolling process, wherein There is no disclosure of any treatment process for reducing material variation in the width direction or length direction of the steel plate before hot press forming, and therefore, it is considered that problems such as poor processing frequently occur when steering components are manufactured according to the above-mentioned technology

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hot rolled steel sheet for hot press forming having low deviation of mechanical property and excellent formability and corrosion resistance hot pressed part using the same and method for manufacturing thereof
  • Hot rolled steel sheet for hot press forming having low deviation of mechanical property and excellent formability and corrosion resistance hot pressed part using the same and method for manufacturing thereof
  • Hot rolled steel sheet for hot press forming having low deviation of mechanical property and excellent formability and corrosion resistance hot pressed part using the same and method for manufacturing thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0036] Next, a hot-rolled steel sheet for hot press forming, which is an aspect of the present invention with little material variation and excellent formability and corrosion resistance, will be described in detail.

[0037] Carbon (C): 0.2 to 0.3% by weight

[0038] Carbon is an element used to form carbides in steel or solid-solve in ferrite to increase the strength of hot-rolled steel sheets. In order to obtain such an effect in the present invention, the carbon is preferably contained in an amount of 0.2% by weight or more, more preferably in an amount of 0.24% by weight or more. However, when the carbon content is too much, a very hard (hard) structure will be formed on the surface of the cast sheet or strip during the continuous casting and rolling process, resulting in surface cracks, or the yield strength of the hot-rolled steel plate may be affected. And the tensile strength is too high, so that when the tube is formed by using multiroll (multiroll) at room temperat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a hot rolled steel sheet for hot press forming having low deviation of mechanical property and excellent formability and corrosion resistance hot pressed part using the same and method for manufacturing thereof. On one hand, the invention provides a hot rolled steel for hot press forming. The hot rolled steel contains by weight percentage:0.2-0.3% of C, 1.2-1.8%of Mn, 0.01-0.5% of Si, less than 0.015% of P, less than 0.004% of S, 0.001-0.05% of A1, 0.006-0.02% of N, 0.0001-0.005% of B, less than 0.1% of Cr and less than 0.05% of Mo, a total of 0.060-1% of more than one selected from Cu and Ni, a total of 0.025-0.09% of more than one selected from Ti and Nb, and Fe containing a residual amount and unavoidable foreign affairs.

Description

technical field [0001] The invention relates to a material with small deviation and good formability A hot-rolled steel sheet for hot-press forming excellent in corrosion resistance, a hot-press-formed product using the same, and a method for producing the same. Background technique [0002] In recent years, in order to improve the fuel consumption efficiency and fuel efficiency of automobiles, the strengthening of automobile structural parts is being accelerated, and the multifunctionalization of said automobile structural parts is also being accelerated in order to meet the various characteristics required by each part. . [0003] Especially for automobile steering parts, not only excellent strength but also excellent fatigue resistance and corrosion resistance are required, and hot-rolled steel sheets are generally used as steel sheets for automobile steering parts. In addition, such a steering member is made into a tubular shape, and various forming processes and heat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/04C22C38/02C22C38/06C22C38/12C22C38/08C22C38/16C22C38/14C21D8/02
CPCC21D8/0226C21D2211/001C21D2211/005C21D2211/008C21D2211/009C22C38/001C22C38/02C22C38/04C22C38/06C22C38/08C22C38/12C22C38/14C22C38/16C22C38/32C21D8/0263C22C38/18
Inventor 成焕球裵成范
Owner 浦项股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap