High-yield-ratio high-strength cold-rolled steel sheet excellent in hole expandability and manufacturing method thereof

A technology of cold-rolled steel sheet and manufacturing method, applied in the field of high-yield ratio type high-strength cold-rolled steel sheet and its manufacturing, can solve the problems of dents, poor weldability, etc. Effect

Active Publication Date: 2018-04-06
浦项股份有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the steel sheet produced by the technique of Patent Document 2 may have poor weldability due to excessive addition of carbon, and may cause dents in the furnace due to excessive addition of silicon.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-yield-ratio high-strength cold-rolled steel sheet excellent in hole expandability and manufacturing method thereof
  • High-yield-ratio high-strength cold-rolled steel sheet excellent in hole expandability and manufacturing method thereof
  • High-yield-ratio high-strength cold-rolled steel sheet excellent in hole expandability and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0074] Vacuum melting was performed on the slab with the composition in Table 1 below, reheating was carried out at a heating temperature of 1200° C. for one hour in a heating furnace, and then hot rolling and coiling were carried out according to the conditions in Table 2 below. Next, the coiled hot-rolled steel sheet was pickled and cold-rolled at a reduction ratio of 45%, thereby obtaining a cold-rolled steel sheet, and then subjected to continuous annealing, primary cooling, and secondary cooling according to the conditions in Table 2 below. Thereafter, overaging treatment was performed for 300 seconds at the secondary cooling termination temperature. At this time, the primary cooling rate was constant at 2°C / sec, the primary cooling termination temperature was constant at 650°C, and the secondary cooling rate was constant at 15°C / sec.

[0075] Next, the phase fraction, size and hardness of the microstructure of each produced cold-rolled steel sheet were measured, and the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a high strength cold rolled steel sheet having high yield ratio and excellent hole expansibility and a method for manufacturing the same. The cold rolled steel sheet includes, by weight, 0.035-0.07% of C, less than 0.3% and greater than 0% of Si, 2.0-3.5% of Mn, 0.3-1.2% of Cr, 0.03-0.08% of Ti, 0.01-0.05% of Nb, 0.01-0.10% of Sol.Al, 0.0010-0.0050% of B, and the balance Fe and unavoidable impurities. In microstructure, the cold rolled steel sheet includes 90 area% of martensite, wherein the average grain diameter of the martensite is less than 3 [mu]m; the martensite includes tempered martensite and lath martensite; the average grain diameter of the lath martensite is less than 1 [mu]m; the area fraction of the lath martensite with the average grain diameter less than 1 [mu]m is less than 5%; and precipitate with the diameter less than 10 nm and 150 / [mu]m2 is included.

Description

technical field [0001] The present invention relates to a high-yield-ratio high-strength cold-rolled steel plate excellent in hole expandability and a manufacturing method thereof. ), a high-yield-ratio high-strength cold-rolled steel sheet excellent in hole expandability for automotive structural parts such as ), and a method for producing the same. Background technique [0002] In recent years, with the strengthening of various environmental regulations and energy regulatory mechanisms, high-strength steel sheets for automobiles are required to improve fuel efficiency and durability of automobiles. In particular, with the spread of automobile impact safety regulations, high-strength steel sheets are widely used for structural parts such as members, seat rails, and pillars in order to improve the impact resistance of the vehicle body. Use a steel plate. This high-strength steel plate is designed to absorb the impact energy of a car, and is therefore characterized by a ste...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/38C21D8/02
CPCC21D8/02C22C38/38
Inventor 韩成豪徐昌孝
Owner 浦项股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap