Antistatic spinning paste and preparation method thereof

A textile slurry and antistatic technology, which is applied in the field of antistatic textile slurry and its preparation, can solve the problems of unsatisfactory long-term needs, poor air permeability and wear resistance, poor durability of antistatic performance of textile materials, etc., to achieve Ease of industrial production, good antistatic performance, and simple preparation method

Active Publication Date: 2016-06-22
WUJIANG FUHUIYUAN HOME TEXTILES CO LTD
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the antistatic properties of textile materials treated with this treatment agent are poor in durability and cannot meet long-term needs.
[0004] Therefore, a kind of antistatic fabric is urgently needed, but the air permeability and abrasion resistance of existing this type of fabric are not good

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] (1) Weigh 60kg of acrylonitrile fiber, 30kg of polyethylene glycol, 12kg of mannitol, 8kg of vinylidene chloride, 3kg of epoxy polysilane acrylate, 2kg of dodecyl dimethyl betaine, allyl Thiourea 0.5kg, 2-methyl-3-hydroxyl-4-methoxyanthraquinone 0.2kg and kaempferol 0.02kg were stirred in a reactor at 90°C and 8MPa for 1 hour;

[0033] (2) Adjust the pH value of the system to 6, add 5kg of carboxymethylcellulose, 0.5kg of polydimethylsiloxane diquaternary ammonium salt and 0.2kg of magnesium aluminosilicate in sequence, and stir at 50°C for 10 minutes to obtain Electrospinning sizing.

[0034] The performance test results of the prepared antistatic textile size are shown in Table 1.

Embodiment 2

[0036] (1) Weigh 60kg of acrylonitrile fiber, 30kg of polyethylene glycol, 12kg of mannitol, 8kg of vinylidene chloride, 3kg of epoxy polysilane acrylate, 2kg of dodecyl dimethyl betaine, allyl Thiourea 0.5kg, 2-methyl-3-hydroxyl-4-methoxyanthraquinone 0.2kg and kaempferol 0.02kg were stirred in a reactor at 90°C and 8MPa for 1 hour;

[0037] (2) Adjust the pH value of the system to 6, add 5kg of carboxymethylcellulose, 0.5kg of polydimethylsiloxane diquaternary ammonium salt, 0.2kg of magnesium aluminosilicate, 1kg of zinc oxide and 3,7-dimethyl Base-6-octenal 1kg, stirred at 50°C for 10 minutes to obtain antistatic textile slurry.

[0038] The performance test results of the prepared antistatic textile size are shown in Table 1.

Embodiment 3

[0040] (1) Weigh 70kg of acrylonitrile fiber, 40kg of polyethylene glycol, 16kg of mannitol, 12kg of vinylidene chloride, 5kg of epoxy polysilane acrylate, 3kg of dodecyl dimethylamine betaine, allyl Thiourea 1kg, 2-methyl-3-hydroxyl-4-methoxyanthraquinone 0.8kg and kaempferol 0.08kg were stirred for 3 hours at 100°C and 12MPa in a reactor;

[0041] (2) Adjust the pH value of the system to 7, add carboxymethylcellulose 8kg, polydimethylsiloxane diquaternary ammonium salt 1kg, magnesium aluminosilicate 0.6kg, zinc oxide 1kg and 3,7-dimethyl - 1 kg of 6-octenal, stirred at 60° C. for 20 minutes to obtain an antistatic textile slurry.

[0042] The performance test results of the prepared antistatic textile size are shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses antistatic spinning paste and a preparation method thereof. The antistatic spinning paste is prepared from the following components in parts by weight: 60-70 parts of acrylonitrile fibers, 30-40 parts of polyethylene glycol, 12-16 parts of mannitol, 8-12 parts of vinylidene chloride, 5-8 parts of carboxymethyl cellulose, 3-5 parts of epoxypolysilicone acrylate, 2-3 parts of N-dodecyl-N,N-dimethylglycine, 0.5-1 part of allylthiourea, 0.5-1 part of polydimethylsiloxane divalent quaternary ammonium salt, 0.2-0.8 part of 2-methyl-3-hydroxyl-4-methoxyanthraquinone, 0.2-0.6 part of magnesium aluminosilicate and 0.02-0.08 part of kaempferol. The invention further provides the preparation method of the antistatic spinning paste.

Description

technical field [0001] The invention belongs to the field of textile materials, in particular to an antistatic textile slurry and a preparation method thereof. Background technique [0002] Fiber materials often contain hydrophilic -OH and -NH 2 Such groups are prone to charge storage. With the continuous improvement of people's requirements for washing and detergent for various types of fabrics, while there are higher requirements for the decontamination ability of washing and detergents, it is also required that washing and detergents have a certain maintenance effect on fabrics. . [0003] Chinese patent CN1553978A discloses a fabric treatment agent, which contains an aqueous dispersion mainly composed of a blocked polyurethane and a hydrophobic solvent, and the prepared treatment agent still has good stability at low temperatures properties, so that the textiles treated with the fabric treatment agent of the present invention have a soft hand and improved shrinkage re...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06M15/31D06M15/53D06M13/148D06M13/08D06M15/09D06M15/643D06M11/77D06M13/152D06M13/432D06M13/463
CPCD06M11/77D06M13/08D06M13/148D06M13/152D06M13/432D06M13/463D06M15/09D06M15/31D06M15/53D06M15/643
Inventor 沈飞峰
Owner WUJIANG FUHUIYUAN HOME TEXTILES CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com