Negative ion composite powder suitable for building materials

A composite powder and negative ion technology, applied in the field of composite powder, can solve the problems of low concentration of negative ions and poor efficacy durability, and achieve the effects of low price, air purification and indoor odor elimination.

Pending Publication Date: 2016-05-25
ZHUO DA NEW MATERIAL TECH GRP
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] CN103805134A Chinese patent discloses a novel anion additive, the shortcoming of the obtained product is that the anion concentration produced is not high, and the efficacy persistence is poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Negative ion composite powder suitable for building materials

Examples

Experimental program
Comparison scheme
Effect test

Embodiment example 1

[0022] Weigh 30 parts of black tourmaline powder with a particle size of 30 μm, 10 parts of anatase powder with a particle size of 40 μm, and 1 part of water-based acrylic acid. Take 1 part of calcium stearate, 1 part of zinc oxide, 30 parts of rare earth, 30 parts of zeolite powder, 1 part of cerium oxide, and 8 parts of titanium-magnesium hornblende powder, and mix them evenly through a dry powder mixer to obtain negative oxygen ion composite powder material.

Embodiment example 2

[0024] Weigh 80 parts of black tourmaline powder with a particle size of 20 μm, 20 parts of anatase powder with a particle size of 25 μm, and 8 parts of water-based acrylic acid. Take 8 parts of calcium stearate, 1 part of zeolite powder, 5 parts of zinc oxide, 5 parts of cerium oxide, and 1 part of titanium-magnesium hornblende powder, and mix them evenly with a dry powder mixer to obtain negative oxygen ion composite powder.

Embodiment example 3

[0026] Weigh 40 parts of black tourmaline powder with a particle size of 10 μm, 15 parts of anatase powder with a particle size of 15 μm, and 3 parts of water-based acrylic acid. Take 3 parts of calcium stearate, 2 parts of zinc oxide, 5 parts of rare earth, 5 parts of zeolite powder, 3 parts of cerium oxide, and 2 parts of titanium-magnesium hornblende powder, and mix them evenly through a dry powder mixer to obtain negative oxygen ion composite powder material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses negative ion composite powder suitable for building materials. The negative ion composite powder is prepared from, by mass, 30-80 parts of black tourmaline powder, 1-8 parts of calcium stearate, 1-5 parts of zinc oxide, 0-30 parts of rare earth, 1-30 parts of zeolite powder, 1-5 parts of cerium oxide, 1-8 parts of waterborne acrylic acid, 1-30 parts of anatase powder and 1-8 parts of titanium-megnesium hornblende powder. According to the technical scheme, the preparation process is simple, raw materials are low in price, a negative ion plate has durability, high efficiency and environment friendliness, the made negative ion plate can release 2200-4000 negative ions per second.cm<2> efficiently and stably, purify air and eliminate indoor peculiar smells and harmful gases, and the composite powder is an environment-friendly negative ion additive.

Description

technical field [0001] The invention relates to a composite powder, in particular to an anion composite powder suitable for building materials. Background technique [0002] The impact of the living environment on the health of the people is constantly concerned. While people are pursuing luxurious and beautiful interior decoration, they are also concerned about the impact of indoor pollution on human health, the environmental protection of building materials, and the impact on human health. Therefore, various new building functional materials that are beneficial to health have emerged as the times require. [0003] Negative ion materials, as one of the representatives of new materials with multiple functions such as environmental protection and health, are widely used in textiles, ceramics, building materials and other fields. Since Aschkinass and Caspan affirmed that negative air ions have biological significance in 1902, and since Soviet scholars published a paper on usi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B24/08C04B20/02C04B14/04C04B14/30C04B14/34
CPCC04B20/023C04B40/0042C04B14/04C04B24/085C04B14/30C04B14/34C04B14/047C04B14/305
Inventor 杨卓舒刘建波车君超刘国强邝清林张磊
Owner ZHUO DA NEW MATERIAL TECH GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap