Resin composition for civil defense door, door leaf and civil defense door

A resin composition and the technology of civil air defense doors, which are applied in the field of civil air defense doors, can solve the problems of difficult transportation and installation, heavy weight of civil air defense products, and high energy consumption in the production process, and achieve the effects of light weight, less waste, and less environmental pollution

Active Publication Date: 2017-07-04
JILIN HAOAN CIVIL AIR DEFENSE ENG CO LTD
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, civil air defense products made of steel and concrete are heavy and difficult to transport and install
Moreover, the production process of steel bars and concrete has high energy consumption and will cause serious pollution to the environment at the same time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Resin composition for civil defense door, door leaf and civil defense door
  • Resin composition for civil defense door, door leaf and civil defense door
  • Resin composition for civil defense door, door leaf and civil defense door

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0069] Composition of the resin mixture

[0070] Based on the total weight of the resin composition, the ratio of the resin composition is: 36% of 199-type m-benzene unsaturated polyester resin, 20% of basalt fiber cloth, 13% of basalt fiber grid (50mm×50mm), 13% of glass fiber short Cut mat 3%, basalt rock particles (3mm) 20%, flame retardant (aluminum hydroxide) 3%, cobalt naphthenate 2%, methyl ethyl ketone peroxide 3%.

[0071] Manufacture of doors

[0072] First, fully stir the 199-type unsaturated polyester resin, cobalt naphthenate, and flame retardant aluminum hydroxide according to the proportion to obtain the unsaturated polyester resin premix.

[0073] The surface of the mold with the groove in the shape of the ring insert is treated with mold release water, and the locks and hinges are placed in the predetermined positions. Then spray gel coat resin (8300g-1, DSM) on its surface. Before painting, add the curing agent methyl ethyl ketone peroxide in the above pro...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
heat deflection temperatureaaaaaaaaaa
tensile strengthaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a resin composition for a civil air defense door, a door leaf prepared from the resin composition, a method for manufacturing the door leaf, and the civil air defense door. The resin composition comprises: 30 to 40 percent of unsaturated polyester resin, 18 to 25 percent of basalt fiber fabric, 10 to 15 percent of basalt fiber grid, 3 to 5 percent of glass fiber felt, 20 to 30 percent of basalt rock particles, 3 to 5 percent of flame retardant and 1 to 5 percent of curing agent, wherein the thermal deformation temperature of the unsaturated polyester resin is more than or equal to 110 DEG C, and the tensile strength is greater than or equal to 50 MPa. The civil air defense door has the advantages of light weight, high strength and corrosion resistance and has good insulation property, sound insulation property and flame retardancy.

Description

technical field [0001] The invention relates to a resin composition for civil air defense doors based on unsaturated polyester resin, a door leaf made of the resin composition, a preparation method of the door leaf, and a civil air defense door comprising the door leaf. Background technique [0002] At present, civil air defense equipment products are mainly reinforced concrete composite structures and steel structures, and such products have been widely used in the market. However, civil air defense products made of steel bars and concrete are heavy, and the transportation and installation process is relatively difficult. Moreover, the production process of steel bars and concrete consumes a lot of energy and causes serious pollution to the environment. [0003] With the development of composite material technology, new composite materials have advantages that concrete and steel do not have, such as relatively heavy weight and good insulation, sound insulation and flame re...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L67/06C08K13/04C08K7/14C08K7/10C08K5/098C08K3/34E06B3/70E06B5/10
CPCC08K3/22C08K3/34C08K5/098C08K7/10C08K7/14C08K13/04C08K2003/2227C08K2201/003C08K2201/014C08L2201/02E06B3/70E06B5/10C08L67/06
Inventor 侯晓峰
Owner JILIN HAOAN CIVIL AIR DEFENSE ENG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More