Multi-gradient functionalized microcapsule titanium phosphate flame retardant and preparation method thereof

A technology of titanium phosphate and microcapsules, which is applied in the field of flame retardant modification, can solve problems such as complex preparation process, non-catalysis, and influence on catalytic char formation, and achieve enhanced mechanical strength, high char formation, and high thermal stability sexual effect

Inactive Publication Date: 2016-05-04
GUANGDONG UNIV OF TECH
View PDF6 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, magnesium hydroxide itself is not catalytic, and its catalytic char formation is affected to a certain extent, and the preparation process is also relatively complicated.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Multi-gradient functionalized microcapsule titanium phosphate flame retardant and preparation method thereof
  • Multi-gradient functionalized microcapsule titanium phosphate flame retardant and preparation method thereof
  • Multi-gradient functionalized microcapsule titanium phosphate flame retardant and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] (1) Preparation of titanium phosphate:

[0037] Mix 10g of titanium tetrachloride with 100ml of distilled water evenly, add 100ml of 9M phosphoric acid while stirring mechanically, and transfer the mixed solution into a stainless steel reaction kettle with a polytetrafluoroethylene lining, and react under high temperature and high pressure for 72h Afterwards, cool to room temperature, repeatedly wash with deionized water until the pH of the solution is neutral, and then vacuum-dry at 80°C to obtain titanium phosphate powder;

[0038] (2) Intumescent flame retardant coated inner wall:

[0039] Weigh 10g of the titanium phosphate powder obtained in step (1), disperse it in 100ml of tetrahydrofuran, stir it mechanically and raise the temperature to 100°C, weigh a certain amount of pentaerythritol as a carbon source modifier, add it to the above solution, and raise the temperature After reaching 150°C and mechanically stirring for 2 hours, add a certain amount of ammonium ...

Embodiment 2

[0043] (1) Preparation of titanium phosphate:

[0044] Mix 10g of titanium tetrachloride with 100ml of distilled water evenly, add 100ml of 9M phosphoric acid while stirring mechanically, and transfer the mixed solution into a stainless steel reaction kettle with a polytetrafluoroethylene lining, and react under high temperature and high pressure for 72h Afterwards, cool to room temperature, repeatedly wash with deionized water until the pH of the solution is neutral, and then vacuum-dry at 80°C to obtain titanium phosphate powder;

[0045] (2) Intumescent flame retardant coated inner wall:

[0046] Weigh 10g of the titanium phosphate powder obtained in step (1), disperse it in 100ml of tetrahydrofuran, stir it mechanically and raise the temperature to 100°C, weigh a certain amount of pentaerythritol as a carbon source modifier, add it to the above solution, and raise the temperature After reaching 150°C and mechanically stirring for 2 hours, add a certain amount of ammonium ...

Embodiment 3

[0052] (1) Preparation of titanium phosphate:

[0053] Mix 10g of titanium tetrachloride with 100ml of distilled water evenly, add 100ml of 9M phosphoric acid while stirring mechanically, and transfer the mixed solution into a stainless steel reaction kettle with a polytetrafluoroethylene lining, and react under high temperature and high pressure for 72h Afterwards, cool to room temperature, repeatedly wash with deionized water until the pH of the solution is neutral, and then vacuum-dry at 80°C to obtain titanium phosphate powder;

[0054] (2) Intumescent flame retardant coated inner wall:

[0055] Weigh 10g of the titanium phosphate powder obtained in step (1), disperse it in 100ml of tetrahydrofuran, stir it mechanically and raise the temperature to 100°C, weigh a certain amount of pentaerythritol as a carbon source modifier, add it to the above solution, and raise the temperature After reaching 150°C and mechanically stirring for 2 hours, add a certain amount of ammonium ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a multi-gradient functionalized microcapsule titanium phosphate flame retardant and a preparation method thereof. The multi-gradient functionalized microcapsule titanium phosphate flame retardant comprises a core material and a wall material for wrapping the core material, wherein the core material is titanium phosphate; the wall material is double-layered, the inner wall is an intumescent flame retardant prepared from a carbon source modifier, an acid source modifier and a gas source modifier in a mole ratio being (1-2):(1-2):(1-2) through reaction, and the outer wall is an organosilicon cross-linked polymer. The preparation method of the flame retardant comprises the following steps: titanium phosphate powder is prepared firstly; then the titanium phosphate powder is dispersed in a solvent, and the carbon source modifier, the acid source modifier and the gas source modifier are added for the reaction for inner wall wrapping; the outer wall is wrapped with the organosilicon cross-linked polymer finally, and the flame retardant is obtained. According to the flame retardant, the organosilicon cross-linked polymer with high carbon formation amount, water resistance, molten droplet avoidance and heat resistance is taken as the outer wall, the intumescent flame retardant is taken as the inner wall, the titanium phosphate powder with carbon formation catalysis characteristic is taken as the core material, so that the prepared microcapsule titanium phosphate flame retardant has more efficient flame retardance and can show a multi-functional multi-gradient flame retardant effect in a burning process.

Description

technical field [0001] The invention belongs to the field of flame retardant modification, and in particular relates to a multi-gradient functionalized microcapsule titanium phosphate flame retardant and a preparation method thereof. Background technique [0002] Titanium phosphate is a layered inorganic powder that has emerged in recent years. It not only has the commonality of layered compounds such as montmorillonite and layered double hydroxide, but also has characteristics that other layered compounds do not have: (1 ) is easy to prepare, and has a relatively good crystal form; (2) is insoluble in water and organic solvents, has high chemical stability, good thermal stability and mechanical strength; (3) has a relatively large charge density on the surface, and is a strong solid acid ; (4) The hydroxyl groups on the surface of the layer can be substituted by other functional groups, so the hydrophilicity and hydrophobicity of the surface can be adjusted; (5) The aspect ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08K9/10C08K3/32C08L55/02B01J13/02B01J13/22B01J13/14
CPCB01J13/02B01J13/14B01J13/22C08K3/32C08K9/10C08K2003/328C08L2201/02C08L55/02
Inventor 雷彩红徐灵峰徐睿杰张丰
Owner GUANGDONG UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com