Energy-saving and light quick-setting waterproof mortar for outer wall

A waterproof mortar and quick-setting technology, applied in the field of building waterproof coatings, can solve the problems of high strength of waterproof mortar, weak compressive and flexural strength, long setting time, etc., to improve the problem of shrinkage cracking, good compressive and flexural strength, The effect of excellent construction performance

Active Publication Date: 2016-04-20
WEIFANG HONGYUAN WATERPROOF MATERIAL
View PDF3 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Wall cracking is a problem often encountered in construction projects. Most of the building walls will have cracks to varying degrees. The traditional waterproof mortar has high strength and poor flexibility, and cannot resist slight deformation and cracking of the wall, resulting in waterproof layer useless
In addition, traditional waterproof mortar is usually made of cement, sand, modifiers, etc. It has a very heavy weight and a single function, which causes a lot of load-bearing pressure on the wall or insulation layer, burying hidden dangers to building safety.
[0006] The existing technology has the following defects: (1) the waterproof mortar is heavy, which increases the safety hazard of the wall; (2) the setting time is long; (3) the impermeability is poor; (4) the compressive and flexural strength is weak; (4) The bonding strength between the waterproof mortar and the base layer is poor; (5) Improve the shrinkage and cracking of the waterproof mortar

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Energy-saving and light quick-setting waterproof mortar for outer wall

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] Example 1 A quick-setting energy-saving lightweight waterproof mortar for exterior walls

[0045] The waterproof mortar includes two components of liquid material and powder material, and its weight ratio is liquid material: powder material = 1:2.77;

[0046] (1) In parts by weight, the liquid material components include: 45 parts of styrene-butadiene emulsion, 0.5 parts of cellulose ether, 54 parts of water, 0.3 parts of defoamer, and 0.2 parts of preservative;

[0047] (2) In parts by weight, the powder components include:

[0048] 30 parts of Portland cement, 15 parts of hollow glass microspheres, 3 parts of fly ash, 50.5 parts of quartz sand, 0.5 parts of cement expansion agent, 0.2 parts of water reducer, 0.2 parts of dispersant, 0.1 part of coagulant, thixotropic 0.5 part of agent;

[0049] The cellulose ether is hydroxyethyl cellulose ether with a viscosity of 1000mPa·s, purchased from Guangdong Longfor Technology Co., Ltd.;

[0050] The Portland cement: the l...

Embodiment 2

[0055] Example 2 A quick-setting energy-saving lightweight waterproof mortar for exterior walls

[0056] The waterproof mortar includes two components of liquid material and powder material, and its weight ratio is liquid material: powder material = 1:3;

[0057] (1) In parts by weight, the liquid material components include: 50 parts of styrene-butadiene emulsion, 0.4 parts of cellulose ether, 48.9 parts of water, 0.4 parts of defoamer, and 0.3 parts of preservative;

[0058] (2) In parts by weight, the powder components include:

[0059] 34 parts of Portland cement, 16 parts of hollow glass microspheres, 4 parts of fly ash, 44.2 parts of quartz sand, 0.6 parts of cement expansion agent, 0.3 parts of water reducing agent, 0.3 parts of dispersant, 0.3 parts of coagulant, thixotropic 0.3 part of agent;

[0060] The cellulose ether is hydroxyethyl cellulose ether with a viscosity of 4000mPa·s, purchased from Guangdong Longfor Technology Co., Ltd.;

[0061] The Portland cement...

Embodiment 3

[0066] Example 3 A quick-setting energy-saving lightweight waterproof mortar for exterior walls

[0067] The waterproof mortar includes two components of liquid material and powder material, the weight ratio of which is liquid material: powder material = 1:3.3;

[0068] (1) In parts by weight, the liquid material components include: 55 parts of styrene-butadiene emulsion, 0.4 parts of cellulose ether, 44 parts of water, 0.3 parts of defoamer, and 0.3 parts of preservative;

[0069] (2) In parts by weight, the powder components include:

[0070] 36 parts of Portland cement, 18 parts of hollow glass microspheres, 4 parts of fly ash, 40.1 parts of quartz sand, 0.8 parts of cement expansion agent, 0.3 parts of water reducing agent, 0.3 parts of dispersant, 0.3 parts of coagulant, thixotropic 0.2 part of dose;

[0071]The cellulose ether is hydroxyethyl cellulose ether with a viscosity of 5000mPa·s, purchased from Guangdong Longfor Technology Co., Ltd.;

[0072] The Portland cem...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
viscosityaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides energy-saving and light quick-setting waterproof mortar for an outer wall. The waterproof mortar is prepared from liquid materials and powder materials. The weight ratio of the liquid materials to the powder materials is 1:2.77-1:3.33. The liquid materials include styrene-butadiene latex, cellulose ether, water, a defoaming agent and a preservative. The powder materials include portland cement, hollow glass beads, coal ash, quartz sand, a cement expansion agent, a water reducing agent, a dispersing agent, a setting accelerator and a thixotropic agent. The waterproof mortar is short in setting time, the initial setting time is 45-70 min, and the final setting time is 1.50-2.50 h; besides, the waterproof mortar is strong in seepage resistance and good in compressive strength and flexural strength.

Description

technical field [0001] The invention relates to a waterproof mortar, in particular to a quick-setting energy-saving lightweight waterproof mortar for exterior walls, which belongs to the field of building waterproof coatings. Background technique [0002] With the development of the economy, environmental pollution and energy crisis have become increasingly prominent, and people have higher and higher requirements for building quality and lifespan, especially the leakage of building exterior walls, which has always troubled people. [0003] Once the exterior wall leaks, it will directly affect the interior wall, and the insulation layer of the exterior wall will also hollow out and fall off under water immersion, directly threatening people's lives. How to reduce or eliminate external wall leakage is an urgent problem to be solved in the construction industry. [0004] There are two schemes for the waterproofing of the exterior wall: 1. Take waterproof measures outside the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B38/08C04B28/04C04B111/40C04B111/27
CPCC04B28/04C04B2111/27C04B2111/40C04B2201/50C04B24/2676C04B24/386C04B2103/50C04B2103/61C04B18/08C04B14/06C04B2103/0068C04B2103/302C04B2103/408C04B2103/12C04B2103/0085C04B38/08C04B24/16C04B22/10C04B22/124
Inventor 刘晓东胡希宝张冬冬杨丰杰齐树凯
Owner WEIFANG HONGYUAN WATERPROOF MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com