A kind of high-efficiency full-interface pump leaching method of rare earth roasted ore by acid method

A leaching and rare earth technology, applied in the field of hydrometallurgy, can solve the problems of equipment, labor, energy consumption, large area, long process flow, etc., and achieve the effect of improving the efficiency of the water leaching process and making the shell soft.

Active Publication Date: 2017-09-29
NAT ENG RES CENT OF RARE EARTH METALLURGY & FUNCTION MATERIALS +1
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The second and third steps of the washing process also use multi-stage continuous leaching tanks, each step of washing takes 30-40 minutes, and the solid-liquid separation takes 30-40 minutes
It can be seen from the above process that the existing process is relatively long, and the cost of equipment, labor, energy consumption, and floor area are relatively large.
As the daily processing volume of concentrate increases, this process brings a great burden to the enterprise

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of high-efficiency full-interface pump leaching method of rare earth roasted ore by acid method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] The acid-processed rare earth roasted ore and water were mixed according to the solid-to-liquid weight ratio of 1:6 and leached for 40 minutes, the leaching temperature was 25°C, and the pH value of the leaching slurry was 2.5. The leached slurry is separated by gravity settling to obtain fine-grained slurry and coarse-grained slurry. The coarse-grained slurry is leached by a 4-stage high-efficiency full-interface pump, combined with a 3-stage tank buffer vortex leaching, and the leached slurry is combined with the fine-grained slurry for solid-liquid separation. A 52.48g / l sulfuric acid rare earth feed solution and leaching residue were obtained, and the leaching residue was washed with dilute sulfuric acid. The pH value of the washing liquid was 0.3, and the dilute sulfuric acid was diluted with acid recovered from tail gas. The acid to slag solid-liquid weight ratio is 1:6, and the time is 10 minutes. 3.21g / l pickling solution and external slag were obtained by soli...

Embodiment 2

[0026] The hot roasted ore and water are mixed according to the solid-to-liquid weight ratio of 1:8, and the slurry is leached for 20 minutes. The leaching temperature is 38°C, and the pH value of the leaching slurry is 1.0~1.5. The leached slurry is separated by gravity settling to obtain fine-grained slurry and coarse-grained slurry. The coarse-grained slurry is leached by a 4-stage high-efficiency full-interface pump, combined with a 3-stage tank buffer vortex leaching, and the leached slurry is combined with the fine-grained slurry for solid-liquid separation. A 39.45g / l sulfuric acid rare earth feed solution and leaching residue were obtained, and the leaching residue was washed with dilute sulfuric acid, the pH of the washing liquid was 1.0, and the dilute sulfuric acid was diluted with acid recovered from tail gas. The acid to slag solid-liquid weight ratio is 1:8, and the time is 20 minutes. The pickling solution with REO content of 1.78g / l and the external slag were ...

Embodiment 3

[0028] The hot roasted ore and water were mixed according to the solid-to-liquid weight ratio of 1:7 and leached for 40 minutes, the leaching temperature was 39.5°C, and the pH value of the leaching slurry was 1.0-1.5. The leached slurry is separated by gravity settling to obtain fine-grained slurry and coarse-grained slurry. The coarse-grained slurry is leached by a 3-stage high-efficiency full-interface pump, combined with the 2-stage tank buffer eddy current leaching, and the leached slurry is combined with the fine-grained slurry for solid-liquid separation. A 44.89g / l sulfuric acid rare earth feed solution and leaching slag were obtained, and the leaching slag was washed with dilute sulfuric acid. The pH value of the washing liquid was 0.5~1.0, and the dilute sulfuric acid was prepared from concentrated sulfuric acid. The acid to slag solid-liquid weight ratio is 1:10, and the time is 20 minutes. The pickling liquid with REO content of 1.5g / l and the external slag were o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to an efficient full-interface pump leaching method for acid-process rare-earth roasted ore. The method is characterized by comprising the following steps: acid-process rare-earth roasted ore and water are mixed to form slurry; the slurry is leached; the leached slurry is subjected to gravitational settling separation to obtain fine grain slurry and coarse grain slurry; the coarse grain slurry is leached through multi-stage pump leaching in combination with multi-stage tank body buffering, wherein a primary pump is connected with a primary buffer tank, then the primary buffer tank is connected with a secondary pump, and so on; after the last pump realizes slurry leaching, the leached coarse grain slurry is combined with the fine grain slurry; solid-liquid separation is performed; the solution obtained after the separation is a sulfuric-acid rare-earth liquid, residues continue to be subjected to quick dilute-acid washing and solid-liquid separation to obtain an acid washing liquid and residues which are discharged outside; and rare earth roasted ore is leached circularly with the acid washing liquid. The method can effectively improve the leaching efficiency and leaching ratio of rare earth in the roasted ore, and saves equipment, energy, labor cost and the like.

Description

technical field [0001] The invention relates to a high-efficiency full-interface pump leaching method of rare earth roasted ore by acid method, which belongs to the technical field of hydrometallurgy. Background technique [0002] The concentrated sulfuric acid enhanced roasting and decomposition process is the main process for treating Baiyan Obo mixed rare earth concentrate, and the traditional multi-stage stirring and continuous leaching method is adopted for the water leaching of the roasted ore. More than 20 stages of 10m for one-step pulping and leaching 3 It takes about 4 hours for the left and right slurry tanks, 1 hour for solid-liquid separation, and the primary leaching rate of REO is only 90%. The second and third steps of the washing process also use multi-stage continuous leaching tanks. Each step of washing takes 30-40 minutes, and the solid-liquid separation takes 30-40 minutes. Therefore, the leaching process takes more than 5 hours, and the total leaching...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22B3/08C22B59/00
CPCC22B3/08C22B59/00Y02P10/20
Inventor 崔建国马志鸿王荣郝肖丽侯睿恩张弓
Owner NAT ENG RES CENT OF RARE EARTH METALLURGY & FUNCTION MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap