Control arm polishing liquid material composite and preparing method and application of control arm polishing liquid
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A polishing liquid and control arm technology, applied in the field of metal polishing liquid, can solve the problems of uneven quality of the control arm, insufficient gloss of the surface of the control arm, time-consuming and labor-intensive, etc.
Inactive Publication Date: 2016-03-16
ANHUI LUOSHI SHENGTAI AUTO PARTS
View PDF0 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0004] In view of the above-mentioned prior art, the purpose of the present invention is to overcome the problem that the surface of the control arm is not glossy enough due to problems such as processing procedures in the prior art during the processing of the control arm. It is time-consuming and labor-intensive, and the grinding effect is often determined according to the proficiency of the operator, which leads to the problem of uneven quality of the control arm after grinding, so as to provide a method that can effectively polish the surface of the control arm, easy to operate and save time. Labor-saving control arm polishing liquid material composition and preparation method of control arm polishing liquid
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
preparation example Construction
[0018] The present invention also provides a preparation method of the control arm polishing liquid, wherein the preparation method comprises: mixing phosphoric acid, sulfuric acid, oxalic acid, glycerin, nano-alumina, nano-calcium oxide and zinc nitrate to prepare the control arm polishing liquid ;in,
[0019] With respect to 100 parts by weight of the phosphoric acid, the amount of sulfuric acid is 10-30 parts by weight, the amount of oxalic acid is 5-20 parts by weight, the amount of glycerin is 1-10 parts by weight, the nano-oxidation The amount of aluminum is 1-5 parts by weight, the amount of nano calcium oxide is 1-5 parts by weight, and the amount of zinc nitrate is 3-20 parts by weight.
[0020] In a preferred embodiment of the present invention, relative to 100 parts by weight of the phosphoric acid, the amount of sulfuric acid is 15-25 parts by weight, the amount of oxalic acid is 10-15 parts by weight, and the amount of glycerin The dosage is 3-7 parts by weight, ...
Embodiment 1
[0027] Put 100g of phosphoric acid, 15g of sulfuric acid, 10g of oxalic acid, 3g of glycerol, 2g of nano-alumina, 2g of nano-calcium oxide and 5g of zinc nitrate at a temperature of 40°C and stir and mix at a rate of 100r / min to prepare the control Arm polish A1.
Embodiment 2
[0029] Put 100g of phosphoric acid, 25g of sulfuric acid, 15g of oxalic acid, 7g of glycerol, 4g of nano-alumina, 4g of nano-calcium oxide and 15g of zinc nitrate at a temperature of 80°C and stir and mix at a rate of 150r / min to obtain a control Arm polish A2.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
particle diameter
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses a control arm polishing liquid material composite and a preparing method and application of control arm polishing liquid. The composition comprises phosphoric acid, sulfuric acid, oxalic acid, glycerol, nanometer aluminum oxide, nanometer calcium oxide and zinc nitrate and includes, by weight, 10-30 parts of sulfuric acid, 5-20 parts of oxalic acid, 1-10 parts of glycerol, 1-5 parts of nanometer aluminum oxide, 1-5 parts of nanometer calcium oxide and 3-20 parts of zinc nitrate relative to 100 parts of phosphoric acid. By means of the design, after control arms are soaked, the glossiness of the surfaces of the control arms can be greatly and effectively improved, the control arms are well polished, manual labor is omitted, cost of manual operation is greatly reduced, the polishing effect of the control arms can be consistent through soaking, and the problem that the quality of the manufactured control arms is inconsistent is avoided.
Description
technical field [0001] The invention relates to the field of metal polishing liquid, in particular to a control arm polishing liquid material composition and a preparation method and application of the control arm polishing liquid. Background technique [0002] As an important part of the car, the control arm plays an extremely important role in the car. During the processing of the control arm, the surface of the control arm is often not glossy due to processing procedures and other problems, and the post-processing is often done manually. And so on, not only time-consuming and labor-intensive, but also often the grinding effect will be determined according to the proficiency of the operator, which will lead to uneven quality of the control arm after grinding. [0003] Therefore, it is an urgent problem to be solved in the present invention to provide a control arm polishing liquid material composition and a preparation method of the control arm polishing liquid that can ef...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more