A kind of polypropylene composition and preparation method thereof

A polypropylene composition and polypropylene technology are applied in the field of polypropylene composition and its preparation, which can solve the problems of affecting the odor of composite materials, and achieve the effects of satisfying low odor and low emission performance, improving devolatilization effect and low emission characteristics

Active Publication Date: 2018-02-06
JIANGSU KINGFA ENVIRONMENTAL PROTECTION SCI &TECH CO LTD
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Chinese patent CN102952336 A discloses a kind of active basic magnesium sulfate whisker modified polypropylene composite material and its preparation method, the composite material is composed of polypropylene, basic magnesium sulfate whisker, toughening agent, processing aid, coupling Composed of additives, acid diluents, and heat stabilizers, the engineering parts made of composite materials of the present invention are developed towards lightweight, and are conducive to reducing the amount of materials used and the cost of materials used, but the acid added in the patent Diluents and coupling agents severely impact composite odor and VOCs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of polypropylene composition and preparation method thereof
  • A kind of polypropylene composition and preparation method thereof
  • A kind of polypropylene composition and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-9 and comparative example 1-10

[0073] Embodiment 1-9 and comparative example 1-10: the preparation of polypropylene composition

[0074] According to the formula in Table 1, first weigh polypropylene, toughening agent, foaming agent, odor adsorbent and processing aids and add them to the high-speed mixer and mix for 3-5 minutes, wherein the speed of the high-speed mixer is 200 rpm- 300 rpm; then weigh basic magnesium sulfate whiskers and add them to a high-speed mixer for 3-5 minutes, wherein the speed of the high-speed mixer is 200 rpm-300 rpm; add the above-mentioned mixed materials Melt extrusion, granulation, drying, cooling, and packaging in twin-screw extruder to get ready; among them, the twin-screw extruder is designed for single vacuum (that is, a vacuum pump is installed in the 9th zone), and the vacuum degree is required to be ≤ -0.08bar, the temperature of the twin-screw extruder is 170°C, 200°C, 200°C, 210°C, 210°C, 205°C, 205°C, 205°C, 200°C, 200°C from the feeding section to the machine head ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
boiling pointaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a polypropylene composition which comprises, by weight parts, 100 parts of polypropylene, 10-30 parts of basic magnesium sulfate whisker, 0.1-1.0 part of foaming agent, 0.5-1.5 parts of smell adsorbent and 10-30 parts of flexibilizer. By simultaneously adding basic magnesium sulfate whisker and foaming agent of a specific content, compared with the situation that only basic magnesium sulfate whisker is added, the weight of a workpiece can be greatly reduced while the comprehensive mechanical property is not reduced, and thus the lightweight requirements of an automobile are met. By adding the smell adsorbent of a specific content and adopting single vacuum design of a twin-screw extruder, it is guaranteed that the vacuum degree requirements are not larger than -0.08 bar, micromolecular volatile matter can be pumped away, and the devolatilization effect is improved obviously. The prepared polypropylene composition is low in smell and emission characteristics, the lightweight requirements of the automobile and low-smell low-emission performances of automobile interior part materials can be met, and the application prospect is wide.

Description

technical field [0001] The invention relates to the field of polymer material modification, in particular to a polypropylene composition and a preparation method thereof. Background technique [0002] Polypropylene (PP) is one of the five general-purpose plastics and has been widely used in chemical, construction, light industry, automobile, home appliances, packaging and other industrial sectors. However, with the development of the industry, the requirements for material properties are getting higher and higher. Ordinary polypropylene must be modified to give it high performance in order to meet the needs. [0003] At present, in the modified polypropylene industry, the mainstream of reinforced polypropylene composite materials is to use talcum powder to fill polypropylene modified composite materials. This kind of talc powder filled modified polypropylene composite can be widely used in automotive interior and exterior trim parts, such as: instrument panel , center conso...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/14C08L23/08C08L91/06C08K13/04C08K7/08C08K3/26C08K5/134C08K5/098C08K5/526C08K3/34C08J9/08C08J9/10B29C47/92B29C48/92
CPCB29C48/92B29C2948/92704C08J9/08C08J9/103C08J2203/02C08J2203/04C08J2323/12C08J2423/08C08K2201/003C08K2201/014C08K2201/016C08L23/14C08L2203/14C08L2205/025C08L2205/035C08L23/12C08L23/0815C08L91/06C08K13/04C08K7/08C08K3/26C08K5/1345C08K5/098C08K5/526C08K3/34
Inventor 吴国峰俞飞钱志军陈瑶杨波周英辉丁超罗忠富叶南飚其他发明人请求不公开姓名
Owner JIANGSU KINGFA ENVIRONMENTAL PROTECTION SCI &TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com