One-time sintered super-flat ink-jet penetrating porcelain tiles with three-dimensional decorative effects, and manufacturing method thereof

A technology of decorative effect and manufacturing method, which is applied in the field of manufacturing super-flat inkjet ink-bleeding porcelain tiles in one time, can solve the problems of poor three-dimensional effect, blurred patterns, color difference, etc., and achieve clear patterns and chemical corrosion resistance Strong, good anti-fouling performance

Active Publication Date: 2016-02-17
MONALISA GRP CO LTD
View PDF5 Cites 37 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to propose a one-time fired ultra-flat inkjet ink-bleeding porcelain tile with a three-dimensional decorative effect and its preparation method, so as to solve the problem of polishing waves in the prior art, the pattern is blurred and there is serious color difference problem, and the problem of poor three-dimensional sense

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • One-time sintered super-flat ink-jet penetrating porcelain tiles with three-dimensional decorative effects, and manufacturing method thereof
  • One-time sintered super-flat ink-jet penetrating porcelain tiles with three-dimensional decorative effects, and manufacturing method thereof
  • One-time sintered super-flat ink-jet penetrating porcelain tiles with three-dimensional decorative effects, and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0082] 1: Preparation of bottom glaze: In order to match the color development of ordinary ceramic ink, calcium, magnesium, barium and other raw materials are not added to the glaze slurry. Its formula is as follows: 41 parts of potassium feldspar, 14 parts of albite, 10 parts of kaolin, 10 parts of burnt clay, 8 parts of alumina, 5 parts of quartz, 10 parts of zirconium silicate, additive A: 0.5 parts, additive B: 4 parts. The chemical composition analysis of additive A is SiO 2 2.01%, Al 2 o 3 2.89%, Fe 2 o 3 0.03%, TiO 2 93.05%, CaO0.03%, MgO0.09%, K 2 O0.02%, Na 2 O0.06%, balance is 1.35% impurity. The chemical composition analysis of Additive B is SiO 2 94.41%, Al 2 o 3 0.14%, Fe 2 o 3 0.05%, TiO 2 0.05%, CaO0.08%, MgO0.06%, K 2 O0.04%, Na 2 O0.21%, balance is 4.59% impurity. The chemical composition analysis of the bottom glaze is SiO 2 56.5%, Al 2 o 3 24.6%, Fe 2 o 3 0.23%, TiO 2 0.66%, CaO0.32%, MgO0.17%, K 2 O4.7%, Na 2 O2.6, ZrO6.4%, the bala...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
penetration depthaaaaaaaaaa
Login to View More

Abstract

The invention relates to one-time sintered super-flat ink-jet penetrating porcelain tiles with three-dimensional decorative effects, and a manufacturing method thereof. According to the manufacturing method, a bottom green brick layer, a priming glaze slurry, a semitransparent glaze slurry, and a transparent glaze slurry are prepared respectively; the bottom green brick layer is subjected to following treatment respectively: a priming glaze layer is formed via priming glaze slurry pouring, jet printing of decorative patterns is carried out, a semitransparent glaze layer is formed via semitransparent glaze slurry pouring, and drying is carried out; obtained green bricks are printed with decorative patterns with ink-jet of penetrating ink and jet printing of a permeation promoter, and are allowed to stand for more than 5min; the obtained green bricks are printed with isolation glaze with water isolating performance via silk-screen printing, and are dried and cooled; the green bricks are coated with the transparent glaze slurry via pouring; the green bricks are subjected to one time sintering so as to obtain one-time sintered ink-jet penetrating porcelain tile semi-finished products with three-dimensional decorative effects; the semi-finished products are subjected to polishing via inelastic module technology so as to obtain the one-time sintered super-flat ink-jet penetrating porcelain tiles with three-dimensional decorative effects.

Description

technical field [0001] The invention relates to the technical field of architectural ceramics, in particular to a method for manufacturing a once-fired ultra-flat ink-jet ink-bleeding porcelain tile with a three-dimensional decorative effect and a product thereof. Background technique [0002] With the introduction of foreign osmotic inks in recent years, the trend of inkjet osmotic tiles has risen again in the market. Its main feature is to pour a layer of bottom glaze on the body or use secondary cloth to make the body, and spray penetrating ink after drying. Because the ink has a certain penetration function, its pattern penetrates into the bottom glaze layer or blank, so it can be directly polished after firing. [0003] Patent document CN102795892A discloses an inkjet bleed porcelain brick and its production method. The technical solution is to pour a layer of primer on the body, spray the bleed ink after drying, and then fire and polish. Patent document CN104193407A ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B41/89C04B41/86
CPCC03C8/02C03C8/04C04B41/52C04B41/86C04B41/89C04B41/504C04B41/5022
Inventor 刘一军范周强汪庆刚张松竹
Owner MONALISA GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com