Titanium blank colored enamel product and manufacturing method

A manufacturing method and enamel technology, applied in the field of enamel products, can solve the problems of easy generation of bubbles and blisters, heavy metal base material, poor firmness of glaze layer, etc. Effect

Inactive Publication Date: 2016-02-10
杨仲华
View PDF7 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Its metal body enamel products generally use gold, silver, copper, iron and other metals as the base material, which has poor hardness and strength. And trachoma, poor flatness; In addition, these metal substrates are heavy and have low corrosion resistance, and other than gold tires are easy to oxidize and rust

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Titanium blank colored enamel product and manufacturing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0023] In order to make the object, technical solution and advantages of the present invention clearer, the present invention will be further described in detail below in conjunction with the accompanying drawings and embodiments. It should be understood that the specific embodiments described here are only used to explain the present invention, not to limit the present invention.

[0024] The titanium body enamel product described in the embodiment of the present invention includes a metal base tire and an enamel layer for titanium covering the surface of the metal base tire; wherein, the metal base tire is made of industrially pure titanium TA1 with a purity of more than 99%. Or TA2 or TA3, which is pickled and pre-fired to form an oxide layer on the surface after taking out the titanium tire; the titanium enamel layer includes a bottom glaze layer and a colored topcoat layer that are sequentially arranged on the surface of the metal base tire from the inside to the outside ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a titanium blank colored enamel product and a manufacturing method. The titanium blank colored enamel product comprises a metal bottom blank and a titanium enamel glaze layer, wherein the metal bottom blank is manufactured by using industrial pure titanium with the purity of more than 99%; a ground glaze layer of the titanium enamel glaze layer is prepared from 10% of titanium oxide, 35% of high-purity quartz, 32% of borax, 3.5% of barium oxide, 4% of zinc oxide, 3.2% of calcium oxide, 3% of magnesium oxide, 4.3% of aluminum oxide and 5% of lead oxide; a colored cover glaze layer is prepared from the mixture of 5% of the titanium oxide, 38% of the high-purity quartz, 34% of the borax, 2.5% of the zinc oxide, 3.2% of the calcium oxide, 6.5% of potassium oxide, 3.8% of the aluminum oxide and 7% of the lead oxide, and a coloring agent type metal oxide at the weight ratio of 100 to (0.5-12); and the titanium blank colored enamel product prepared by the steps of preparing the metal bottom blank and titanium enamel glaze, firing the ground glaze layer and the colored cover glaze layer, discharging from a furnace and trimming can be firmly glazed, has the bright and flat glaze and high rigidity and intensity, and is not easy to oxidize and get rusty.

Description

technical field [0001] The invention belongs to the technical field of enamel products, in particular to a titanium body enamel product and a manufacturing method. Background technique [0002] Enamel products have gradually entered people's lives, not only as traditional decorations, but also widely used as jewelry and clothing. At present, there are two main types of enamel products (enamel wares) on the market, one is metal body filigree enamel from Persia, and the other is metal body painting enamel from Europe. Its metal body enamel products generally use gold, silver, copper, iron and other metals as the base material, which has poor hardness and strength. And trachoma, poor flatness; In addition, these metal substrates are heavy and have low corrosion resistance, except for gold tires, they are easy to oxidize and rust. Contents of the invention [0003] In order to solve the above-mentioned technical problems in the prior art, the present invention provides a gla...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B44C5/00B44C1/00C03C8/12C03C8/20
Inventor 杨仲华
Owner 杨仲华
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com