Sintered brick prepared from manganese slag and preparation method of sintered brick

A technology of manganese slag and sintered bricks, which is applied in the field of sintered bricks and its preparation, can solve the problem that solid waste cannot be fully utilized for sintered bricks, and achieve the effects of being beneficial to the sustainable development of human beings, reducing water absorption and high economic value

Active Publication Date: 2016-01-27
广西建筑材料科学研究设计院有限公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a fired brick made of manganese slag and its preparation method in view of the problems that the existing solid waste cannot be fully utilized and the fired brick exists

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A fired brick made from manganese slag, comprising the following raw materials in parts by weight: 100 parts of manganese slag, 70 parts of papermaking sludge, 6 parts of redispersible latex powder, 4 parts of rosin resin and 5 parts of boron oxide.

[0026] The preparation method of sintered brick comprises the following steps:

[0027] S1: Weigh the following raw materials in parts by weight: 100 parts of manganese slag, 70 parts of paper sludge, 6 parts of redispersible latex powder, 4 parts of rosin resin and 5 parts of boron oxide. mm, get fine raw material;

[0028] S2: Add the fine raw material obtained in step S1 into a mixer, then add water with a weight ratio of 12% to the fine raw material, and stir for 20 min at a speed of 150 r / min to obtain a mixed material;

[0029] S3: Add the mixed material into the extrusion molding machine, and form it into a green body, and the molding pressure is controlled at 5MPa;

[0030] S4: drying the green body obtained in s...

Embodiment 2

[0033] A sintered brick made from manganese slag, comprising the following raw materials in parts by weight:

[0034] 120 parts of manganese slag, 60 parts of paper sludge, 8 parts of redispersible latex powder, 5 parts of rosin resin and 6 parts of boron oxide.

[0035] The preparation method of sintered brick comprises the following steps:

[0036] S1: Weigh the following raw materials in parts by weight: 120 parts of manganese slag, 60 parts of paper sludge, 8 parts of redispersible latex powder, 5 parts of rosin resin and 6 parts of boron oxide. , to obtain fine raw materials;

[0037] S2: Add the fine raw material obtained in step S1 into a mixer, then add water with a weight ratio of 13% to the fine raw material, and stir for 15 min at a speed of 200 r / min to obtain a mixed material;

[0038] S3: Put the mixed material into the extrusion molding machine, and shape it into a green body, and the molding pressure is controlled at 4MPa;

[0039] S4: drying the green body ...

Embodiment 3

[0042] A sintered brick made of manganese slag comprises the following raw materials in parts by weight: 135 parts of manganese slag, 65 parts of papermaking sludge, 10 parts of redispersible latex powder, 4 parts of rosin resin and 6 parts of boron oxide.

[0043] The preparation method of sintered brick comprises the following steps:

[0044] S1: Weigh the following raw materials in parts by weight: 135 parts of manganese slag, 65 parts of paper sludge, 10 parts of redispersible latex powder, 4 parts of rosin resin and 6 parts of boron oxide. mm, get fine raw material;

[0045] S2: Add the fine raw material obtained in step S1 into a mixer, then add water with a weight ratio of 14% to the fine raw material, and stir for 15 minutes at a rotating speed of 250r / min to obtain a mixed material;

[0046] S3: Put the mixed material into the extrusion molding machine, and shape it into a green body, and the molding pressure is controlled at 6MPa;

[0047] S4: drying the green body...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
water absorptionaaaaaaaaaa
Login to view more

Abstract

The invention discloses a sintered brick prepared from manganese slag and a preparation method of the sintered brick. The sintered brick is prepared from, by weight, 100-150 parts of manganese slag, 60-80 parts of paper mill sludge, 5-10 parts of redispersible powder, 4-6 parts of rosin resin and 5-8 parts of boric oxide. According to the sintered brick, manganese slag and paper mill sludge serve as the main raw materials, an effective approach is provided for comprehensively utilizing solid waste, environment pollution is reduced, clay resources are protected, sustainable development is facilitated for human, and high economic value is achieved. The sintered brick has the advantages of being high in strength, low in water absorption rate, low in density, good in heat preservation and thermal insulation effect, wide in raw material source, low in cost, simple in preparation process, low in energy consumption and the like and has quite good market prospects.

Description

technical field [0001] The invention belongs to the technical field of new building materials, and specifically relates to a sintered brick made from manganese slag and a preparation method thereof. Background technique [0002] Manganese is an important basic material in the national economy and one of the country's important strategic resources. At present, my country has become the world's largest producer, consumer and exporter of electrolytic manganese. As an important metallurgical and chemical raw material, electrolytic manganese has made great contributions to my country's industrial development and regional economic construction. However, the electrolytic manganese industry, as a typical hydrometallurgical industry, has also caused serious environmental problems during its rapid development. Pollution, especially electrolytic manganese waste slag pollution, according to statistics, the amount of acid leaching slag discharged per 1 ton of electrolytic manganese powder...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/00C04B35/622
Inventor 杨志明陈霏朱芳雯叶丹玫徐伟梅嵩
Owner 广西建筑材料科学研究设计院有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka