Permanent antistatic ABS (acrylonitrile butadiene styrene) flame-retardant material

A flame retardant material and antistatic technology, applied in the field of ABS materials, can solve the problems of long-term antistatic and flame retardant of office equipment, and achieve the effect of good processing performance and good impact resistance

Inactive Publication Date: 2016-01-20
昆山幻彩塑胶科技有限公司
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In the existing technology, most of the office equipment is made of ABS material, but these materials cannot meet the long-term antistatic and flame retardant requirements of office equipment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Permanent antistatic ABS (acrylonitrile butadiene styrene) flame-retardant material
  • Permanent antistatic ABS (acrylonitrile butadiene styrene) flame-retardant material
  • Permanent antistatic ABS (acrylonitrile butadiene styrene) flame-retardant material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] Embodiment 1: A permanent antistatic ABS flame retardant material, including styrene-acrylonitrile resin, high rubber powder, brominated flame retardant, antimony flame retardant, antistatic agent, antioxidant and lubricant, each The proportion of ingredients is:

[0018]

[0019] Wherein, the styrene-acrylonitrile resin is a SAN resin with a melt flow index greater than 2.5; the high rubber powder is butadiene, and the rubber content of the butadiene is 45%-65%. The brominated flame retardant is one of decabromodiphenylethane, tetrabromobisphenol A or bromotriazine. The antimony-based flame retardant is antimony trioxide or sodium antimonate. The antistatic agent is a polyether ester antistatic agent. The antioxidant is a compound of Ciba Irganox 1076 and Ciba Irgafos 168, and the ratio of the two is 1:2. Described lubricant is polyethylene wax or vinylbisstearamide.

Embodiment 2

[0020] Embodiment 2: A permanent antistatic ABS flame-retardant material. In this embodiment, 59 parts of styrene-acrylonitrile resin, 25 parts of high-grade rubber powder, 9 parts of brominated flame retardant, and 3 parts of antimony-based flame retardant are used. part, 4 parts of antistatic agent, 0.3 part of antioxidant and 0.5 part of lubricant to test the physical properties of ABS material. Under the standard of ISO527, the tensile strength is 35Mpa when the measurement speed is 50mm / min; Under the standard, the bending strength is 60 when the measuring speed is 2mm / min, and the Izod notched impact strength is 19KJ / m under the condition of 23°C under the ISO180 standard 2 , under the UL94 standard, the thickness is 1.6mm, the flame retardancy level is HB; under the GB / T1410 standard, the length is 100mm, the width is 80mm, the thickness is 3mm, and the surface resistance is 10 15 Ω.

Embodiment 3

[0021] Embodiment 3: A permanent antistatic ABS flame-retardant material. In this embodiment, 60 parts of styrene-acrylonitrile resin, 16 parts of high-grade rubber powder, 12 parts of brominated flame retardant, and 4 parts of antimony-based flame retardant are used. part, 8 parts of antistatic agent, 0.3 part of antioxidant and 0.5 part of lubricant to test the physical properties of ABS material. Under the standard of ISO527, the tensile strength is 42Mpa when the measuring speed is 50mm / min; Under the standard, the bending strength is 66 when the measuring speed is 2mm / min, and the Izod notched impact strength is 12KJ / m under the condition of 23°C under the ISO180 standard 2 , under the UL94 standard, the thickness is 1.6mm, the flame retardancy level is V1; under the GB / T1410 standard, the length is 100mm, the width is 80mm, the thickness is 3mm, and the surface resistance is 10 12 Ω.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Notched impact strengthaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a permanent antistatic ABS (acrylonitrile butadiene styrene) flame-retardant material. The material is characterized by comprising, in percentage by weight, 40%-65% of styrene-acrylonitrile resin, 15%-25% of high glue powder, 8%-20% of a brominated flame retardant, 2%-6% of an antimony flame retardant, 4%-12% of an antistatic agent, 0.1%-1% of an antioxidant and 0.2%-1% of a lubricant. The styrene-acrylonitrile resin is SAN (styrene acrylonitrile) resin with the melt flow index larger than 2.5. The good anti-impact performance of the ABS is guaranteed, and the material has a permanent antistatic effect.

Description

technical field [0001] The invention relates to an ABS material, in particular to a permanent antistatic ABS flame-retardant material. Background technique [0002] ABS resin is one of the five major synthetic resins. It has excellent impact resistance, heat resistance, low temperature resistance, chemical resistance and electrical properties. It also has the characteristics of easy processing, stable product size, and good surface gloss. It is easy to paint. , coloring, and secondary processing such as surface metal spraying, electroplating, welding, hot pressing and bonding, etc. It is widely used in industrial fields such as machinery, automobiles, electronic appliances, instrumentation, textiles and construction. Wide range of thermoplastic engineering plastics. [0003] In the prior art, most of the office equipment is made of ABS material, but these materials cannot meet the long-term antistatic and flame-retardant requirements of the office equipment. Therefore, how...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L25/12C08L9/00C08K13/02C08K5/03C08K5/136C08K3/22C08K3/24C08K5/20C08K5/526C08K5/134
Inventor 邓德权
Owner 昆山幻彩塑胶科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com