A kind of method for preparing polyaniline electrochromic film by hydrothermal self-assembly

An electrochromic and polyaniline technology, which is applied in the synthesis of polymer materials and materials, can solve the limitations of electrochromic and display device applications, the poor bonding strength of polyaniline and conductive glass, and the difficulty of large-scale production of polyaniline electrode areas, etc. problems, to achieve the effect of low preparation cost, excellent electrochromic performance and good conductivity

Inactive Publication Date: 2017-09-26
XIAN UNIV OF SCI & TECH
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But there are also some problems: 1) It is difficult to control the morphology of polyaniline prepared by chemical polymerization at low temperature and normal temperature.
2) Polyaniline prepared by electrochemical polymerization is difficult to mass-produce due to the limitation of electrode area
3) The film prepared by spin coating has the characteristics of simple preparation, but the bonding strength between polyaniline and conductive glass is poor, and polyaniline is easy to fall off
At present, there are very few reports on the preparation of polymers by the hydrothermal method. Patent CN 102070783 B discloses a hydrothermal preparation method for micro-nano polyaniline crystal materials. Aniline material, but after testing, it is found that this material cannot be uniformly coated on FTO glass, and it is difficult to prepare a uniform film, which greatly limits its application in electrochromic and display devices

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of method for preparing polyaniline electrochromic film by hydrothermal self-assembly
  • A kind of method for preparing polyaniline electrochromic film by hydrothermal self-assembly
  • A kind of method for preparing polyaniline electrochromic film by hydrothermal self-assembly

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] The growth of polyaniline film on the surface of FTO glass by hydrothermal method includes the following steps:

[0030] 1) Hydroxylation treatment of FTO glass, ultrasonic cleaning of FTO glass with acetone, absolute ethanol and deionized water in sequence, and the cleaning time is 40-60 minutes.

[0031] 2) Immerse the cleaned FTO glass in a mixture of hydrogen peroxide and concentrated sulfuric acid with a volume ratio of 7:3, the heating temperature is 60-80°C, and the time is 12-24h. The hydroxylated FTO glass was rinsed several times with deionized water and treated with N 2 Air-dried for later use to obtain a surface hydroxylated FTO substrate.

[0032] 3) Add 0.7290 g of cetyl trimethyl ammonium bromide to 76 mL of deionized water, leave it to stand until the solution becomes clear and transparent, place the solution in an ice-water bath and stir for 2 minutes, and then dropwise add 0.2 mL of the solution under reduced pressure. After the distilled aniline, 4 ...

Embodiment 2

[0040] 1) Same as Example 1.

[0041] 2) Same as Example 1.

[0042] 3) Add 0.730 g of cetyl trimethyl ammonium bromide to 76 mL of deionized water, leave it to stand until the solution becomes clear and transparent, place the solution in an ice-water bath and stir for 2 minutes, and then dropwise add 0.2 mL of the solution under reduced pressure. After the distilled aniline, 4 mL of dodecylbenzenesulfonic acid was added after the aniline was uniformly dispersed, and after stirring for about 20 minutes, the solution became a uniform milky white, and then 4 mL of ammonium persulfate solution with a concentration of 0.24 mol / L was added and stirred for 5 minutes.

[0043] 4) The conductive surface of the hydroxylated FTO glass is tilted downward and put into the stainless steel reactor lined with PTFE, and then the above-mentioned mixed solution is transferred into the 50ml reactor, and the volume of the reaction solution does not exceed 2 / 2 of the entire reactor. 3. Hydrothermal...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a hydrothermal preparation method of conductive polyaniline film. The raw materials such as aniline monomer and oxidant are pre-reacted at low temperature, and the FTO glass that has been hydroxylated beforehand is put into the hydrothermal reaction kettle with the conductive side facing down. , and then transfer the pre-reacted mixed solution into a hydrothermal reactor to react at a certain temperature for 3-4 hours; the polymer prepared by the method of the present invention can self-assemble and grow on FTO conductive glass, and the results of characterization and testing prove that polyaniline The thin film has good electrical conductivity and electrochromic performance, and can be used in electrochromic materials and the like.

Description

technical field [0001] The invention belongs to the field of materials and the field of polymer material synthesis, in particular to a method for preparing a polyaniline electrochromic film by hydrothermal self-assembly. Background technique [0002] Electrochromism refers to the stable and reversible color change of the material's optical properties (transmittance, reflectivity, absorptivity, etc.) under the action of an external electric field. In recent years, electrochromic materials have a very broad application prospect in the fields of smart windows, automotive anti-rotation rearview mirrors, displays and space temperature control devices. [0003] Among many electrochromic materials, conductive polymer polyaniline films are considered as one of the most potential electrochromic materials due to their advantages of good conductivity, rich colors, inexpensive monomers, and tunable structure. At present, the preparation methods of polyaniline films mainly include elect...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C17/38
Inventor 褚佳张英逯登玉张文龙王先珊彭梦毅杨姣熊善新马晶
Owner XIAN UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com