A kind of building ceramics white toner and preparation method thereof

A technology for building ceramics and white color, applied in the field of building ceramic white toner and its preparation, can solve the problems of easy fading preparation process, insufficient whiteness, high temperature resistance, etc., and achieve the effects of reducing cost, high whiteness and improving efficiency

Active Publication Date: 2017-12-19
佛山市明朝科技开发有限公司 +1
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] For this reason, the technical problem to be solved by the present invention is to overcome the technical bottlenecks in the prior art of insufficient whiteness, high temperature resistance, easy fading after sintering, complex preparation process, high cost, and serious pollution, thereby proposing a high whiteness, High temperature resistance, excellent thermal stability, no fading during high temperature sintering, high image quality; simple preparation process, high efficiency and low cost architectural ceramic white toner and preparation method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of building ceramics white toner and preparation method thereof
  • A kind of building ceramics white toner and preparation method thereof
  • A kind of building ceramics white toner and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Example 1 This example discloses a white toner for architectural ceramics and a preparation method thereof. The white toner for architectural ceramics includes the following components:

[0031]

[0032] The preparation method comprises the steps of:

[0033] Preparation of modified white ceramic pigments:

[0034] a) Sol: Under the condition of stirring, the precursor of zirconia and the precursor of silicon oxide are synchronously and slowly added to the ethanol solution (50%) (the molar ratio of zirconia to silicon oxide is 4:1), after the addition is complete , stirring for hydrolysis for 24 hours, stratified after standing for 6 hours, discarding the supernatant, adding deionized water and stirring for another 24 hours, stratifying after standing for 6 hours, discarding the supernatant, repeating the above steps until the pH value of washing with water is neutral , get sol;

[0035] b) Gel: drying the sol in a drying oven to form a xerogel;

[0036] c) Calcin...

Embodiment 2

[0044] Example 2 This example discloses a white toner for architectural ceramics and a preparation method thereof. The white toner for architectural ceramics includes the following components:

[0045]

[0046] The preparation method comprises the steps of:

[0047] Preparation of modified white ceramic pigments:

[0048] a) Sol: Under the condition of stirring, the precursor of zirconia and the precursor of silicon oxide are synchronously and slowly added to the ethanol solution (50%) (the molar ratio of zirconia to silicon oxide is 4:1), after the addition is complete , stirring for hydrolysis for 24 hours, stratified after standing for 6 hours, discarding the supernatant, adding deionized water and stirring for another 24 hours, stratifying after standing for 6 hours, discarding the supernatant, repeating the above steps until the pH value of washing with water is neutral , get sol;

[0049] b) Gel: drying the sol in a drying oven to form a xerogel;

[0050] c) Calcin...

Embodiment 3

[0058] Embodiment 3 This embodiment discloses a white toner for architectural ceramics and a preparation method thereof. The white toner for architectural ceramics includes the following components:

[0059]

[0060] Described its preparation method, comprises the steps:

[0061] Preparation of modified white ceramic pigments:

[0062] a) Sol: Under the condition of stirring, the precursor of zirconia and the precursor of silicon oxide are synchronously and slowly added to the ethanol solution (50%) (the molar ratio of zirconia to silicon oxide is 4:1), after the addition is complete , stirring for hydrolysis for 24 hours, stratified after standing for 6 hours, discarding the supernatant, adding deionized water and stirring for another 24 hours, stratifying after standing for 6 hours, discarding the supernatant, repeating the above steps until the pH value of washing with water is neutral , get sol;

[0063] b) Gel: drying the sol in a drying oven to form a xerogel;

[0...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of architectural ceramics processing, in particular to a white toner for architectural ceramics and a preparation method thereof. The architectural ceramic white toner comprises: 50-80 parts by weight of resin; 25-40 parts by weight of white ceramic pigment; 2-8 parts by weight of wax; 3-8 parts by weight of charge regulator; 0.2-1 part by weight of fumed silica . The prepared white ceramic toner for building ceramics has high whiteness, high temperature resistance and excellent thermal stability. After high temperature sintering, the text or pattern on the surface of the ceramic substrate still does not fade, and the image quality is high; in terms of preparation technology , the traditional two-step process of crushing and modification is changed to an integrated process of crushing and modification, and surface modification is completed at the same time as ultra-fine crushing, which simplifies the process, improves efficiency, effectively controls particle size distribution, and reduces costs. ; In line with the concept of energy saving and environmental protection, it has great market prospects and economic value.

Description

technical field [0001] The invention belongs to the field of architectural ceramic processing, and in particular relates to a white toner for architectural ceramics and a preparation method thereof. Background technique [0002] Ceramic digital inkjet has developed rapidly in the architectural ceramics industry, bringing rapid changes to architectural ceramics. Ceramic digital inkjet not only enriches products but also makes personalized customization possible. In order to improve the utilization rate of the color material and avoid the disadvantage of low resolution caused by the diffusion of ceramic inkjet, a laser printer is used to print the texture pattern of architectural ceramics on the adhesive film, and then soak the decal paper printed with the texture pattern in clean water. Separate the adhesive film from the white paper, then peel off the adhesive film with the textured pattern and stick it on the glazed brick, and pour the glaze. Put the bricks with the textu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G03G9/08C04B41/85
Inventor 毛海燕
Owner 佛山市明朝科技开发有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com