Synthetic method of flake zsm-39 molecular sieve

A technology of ZSM-39 and template agent, which is applied in the field of molecular sieve synthesis, can solve the problems of failure to obtain flaky ZSM-39 zeolite and poor crystallinity of ZSM-39 molecular sieve, achieve good practicability and effectiveness, and improve synthesis efficiency , avoid the effect of cumbersome steps

Active Publication Date: 2017-07-14
CHINA PETROLEUM & CHEM CORP +1
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The technical problem to be solved by the present invention is the poor crystallinity of the ZSM-39 molecular sieve prepared in the prior art, and the technical problem that the flake ZSM-39 zeolite cannot be obtained, and a new synthesis of ZSM-39 molecular sieve is provided method, the prepared ZSM-39 molecular sieve has the advantages of good crystallinity, and SEM shows that the product presents a uniform sheet shape

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Synthetic method of flake zsm-39 molecular sieve
  • Synthetic method of flake zsm-39 molecular sieve
  • Synthetic method of flake zsm-39 molecular sieve

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] Synthesis method: add 0.5g sulfuric acid into 14.4g water, stir evenly, then add 0.544g sodium fluoride, 1.2g n-propylamine, 1.4g hexamethylenetetramine, 0.051g aluminum sulfate octadecahydrate in turn under constant stirring , then continue to stir for 30min. Finally, 4.86 g of silica sol with a mass fraction of 40% was added, and after stirring evenly, the gel was aged at room temperature for 8 hours. After that, it was crystallized at 180°C and stirred at 150rpm for 5 days, cooled to room temperature, washed with deionized water and centrifuged three times, and dried at 80°C for 12 hours to obtain the final product.

[0039] figure 1 It is the XRD spectrum of the product obtained in Example 1, it can be seen that the product has the characteristic diffraction peak of ZSM-39, and has a higher crystallinity. figure 2 , image 3 It is the SEM photo of the product obtained in Example 1 with different magnifications, and it can be seen that the sample presents a unifo...

Embodiment 2

[0041] Using the same conditions as in Example 1, changing the amount of n-propylamine to 4.2g, to obtain the final product. According to the XRD characterization results of the sample, it can be seen that the product has the characteristic diffraction peak of ZSM-39, and the SEM photo shows that the sample has a sheet-like morphology.

Embodiment 3

[0043] Using the same conditions as in Example 1, changing the water consumption is 8g, and the n-propylamine consumption is 1.8g to obtain the final product. According to the XRD characterization results of the sample, it can be seen that the product has the characteristic diffraction peak of ZSM-39, and the SEM photo shows that the sample has a sheet-like morphology.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of molecular sieve synthesis, and concretely relates to a synthetic method of a sheet ZSM-39 molecular sieve. ZSM-39 molecular sieves with sheet morphology have not be reported domestically at present. The synthetic method of the sheet ZSM-39 molecular sieve comprises the following steps: adding weighed solid raw materials comprising a silicon source, an aluminum source, a mineralizer, an organic template and an acidity and alkalinity adjusting agent to a reaction kettle according to a certain sequence, stirring until uniformity, carrying out gel ageing, carrying out hydrothermal crystallization, washing the above obtained crystallization product, filtering, and drying. An XRD result shows that a sample obtained in the invention is the ZSM-39 molecular sieve, and the crystallization degree is good; and an SEM result shows that the product has a uniform sheet morphology. The method can be used in industrial production of the sheet ZSM-39 molecular sieve.

Description

technical field [0001] The invention belongs to the technical field of molecular sieve synthesis, in particular to a method for synthesizing sheet-like ZSM-39 molecular sieves. Background technique [0002] Zeolite is a microporous crystalline aluminosilicate (aluminosilicate), its skeleton is usually composed of silicon-oxygen tetrahedrons and aluminum-oxygen tetrahedrons connected to each other by covalent bonds, and the general chemical formula is [0003] [M 2 (I),M(II)]O·Al 2 o 3 · nSiO2 2 mH 2 o [0004] In the formula, M(I) and M(II) are monovalent and divalent metals (usually Na, Ca, Ka, etc.), respectively, and n is the zeolite silicon-aluminum ratio. Due to its good adsorption performance, high specific surface area, good thermal stability and hydrothermal stability, zeolite molecular sieves are widely used in various fields such as ion exchange, gas storage, and industrial catalysis. [0005] ZSM-39 molecular sieve was developed by Mobil Company of the Unit...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01B39/04
Inventor 史静滕加伟谢在库
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com