Alloy element additive used for aluminum alloy production and preparation method thereof

A technology of alloying elements and additives, which is applied in the field of aluminum alloy production, can solve quality problems and other problems, and achieve the effect of improving the environment and excellent refining function

Active Publication Date: 2015-12-23
SHENYANG AEROSPACE UNIVERSITY
View PDF6 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These alkali metals, non-metallic slag inclusions and water vapor will cause serious quality problems to the casting and subsequent processing of aluminum and its alloys

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Example 1: Grinding the electrolytic manganese flakes into powder, the particle size of the manganese powder is below 0.6 mm (30 mesh). Divide the content into MgCl 2 Base fusion 70% (mass percentage) of MgCl 2 Heat and melt with 30% (mass percentage) of KCl, stir evenly, cool and solidify, then crush and grind into powder, the powder particle size is less than 0.6 mm (30 mesh), forming MgCl 2 base fusion powder. Take 700g of manganese powder and 300g of MgCl 2 The base fusion powder was uniformly mixed, and then pressed into blocks of 1000 g each with a press.

Embodiment 2

[0023] Example 2: Grinding the electrolytic manganese flakes into powder, the particle size of the manganese powder is below 0.6 mm (30 mesh). Divide the content into MgCl 2 40% (mass percent) MgCl of base fusion 2 Heating and melting with 60% (mass percentage) of KCl, stirring evenly, cooling and solidifying, then crushing and grinding into powder, the powder particle size is less than 0.6 mm (30 mesh), forming MgCl 2 base fusion powder. Take 700g of manganese powder and 300g of MgCl 2 The base fusion powder was uniformly mixed, and then pressed into blocks of 1000 g each with a press.

Embodiment 3

[0024]Embodiment 3: Grinding the electrolytic manganese flakes into powder, the particle size of the manganese powder is below 0.6 mm (30 mesh). Divide the content into MgCl 2 Base fusion 58% (mass percentage) of MgCl 2 Heating and melting with 42% (mass percentage) of KCl, stirring evenly, cooling and solidifying, then crushing and grinding into powder, the powder particle size is less than 0.6 mm (30 mesh), forming MgCl 2 base fusion powder. Take 900g of manganese powder and 100g of MgCl 2 The base fusion powder was uniformly mixed, and then pressed into blocks of 1000 g each with a press.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Granularityaaaaaaaaaa
Granularityaaaaaaaaaa
Granularityaaaaaaaaaa
Login to View More

Abstract

Disclosed is an alloy element additive used for aluminum alloy production. The alloy element additive is composed of alloy element powder to be added, mgcl2-group fusion powder and an adhesive. The components comprise, by mass, 70%-90% of the alloy element powder, 10%-30% of the mgcl2-group fusion powder and 0-5% of the adhesive. The sum of the mass percents of the three components is 100%. Alloy elements are organically combined with a refining agent, so that the alloy element additive not only has an alloying function, but also has a refining effect. According to the alloy element additive and a preparation method thereof, mgcl2-group fusion serves as a fusing agent, so that not only is the fusing function to the alloy element powder achieved, but also the refining function to aluminum water is achieved, and accordingly the agent is multipurpose indeed. The alloy element additive does not contain toxic substances, thereby being safe and environmentally friendly

Description

technical field [0001] The invention belongs to the technical field of aluminum alloy production, and in particular relates to an alloy element additive for aluminum alloy production. Background technique [0002] In the production process of aluminum alloy, it is often necessary to add various alloying elements such as manganese, iron, silicon, magnesium, and copper. The addition of these alloying elements is mainly carried out through intermediate alloys or alloying element additives. The so-called alloying element additive is a block formed by mixing alloying element powder and other fluxes. [0003] Since the advent of alloying element additives, it has been welcomed by the casting industry. This additive is easy to use and can be easily put into the melting furnace without requiring special equipment. The additive block has a relatively large specific gravity, and it sinks naturally after being put into the metal solution, which prevents the powder from being scatter...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C1/03C22C21/00
Inventor 刘玉林王继杰张利赵玉华刘春忠
Owner SHENYANG AEROSPACE UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com