High temperature resistant carbon fiber reinforced composite material continuous sucker rod and its preparation device and method

A technology for reinforced composite materials and preparation devices, which is applied to drill pipes, drilling equipment, earthwork drilling and production, etc. It can solve problems such as corrosion and partial wear, achieve excellent corrosion resistance and partial wear resistance, reduce the number of joints, and improve bending performance Effect

Active Publication Date: 2017-11-07
SHENGLI OIL FIELD XINDA PIPE IND TECH DEV CO LTD
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to address the above-mentioned defects in the prior art, to provide a high-temperature-resistant carbon fiber reinforced composite material continuous sucker rod and its preparation device and method, so as to solve the problems of corrosion and eccentric wear in the production of oil fields, and to solve the problem of high-temperature well flushing. The main purpose is to solve the problem of oil production in deep wells and ultra-deep wells, and to prepare sucker rods with good corrosion resistance and partial wear resistance, small piston effect, and easy operation and use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High temperature resistant carbon fiber reinforced composite material continuous sucker rod and its preparation device and method
  • High temperature resistant carbon fiber reinforced composite material continuous sucker rod and its preparation device and method
  • High temperature resistant carbon fiber reinforced composite material continuous sucker rod and its preparation device and method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0029] combined with figure 1 , a high-temperature-resistant carbon fiber reinforced composite material continuous sucker rod mentioned in the present invention, from the inside to the outside is the reinforcing fiber carbon fiber A along the rod body axial direction, and the fiber-wound reinforcement layer aramid 1414 fiber B; along the rod body axial direction Reinforcement fiber high-strength glass fiber C, fiber weaving reinforcement layer aramid 1414 fiber D, a layer of fiber-wound reinforcement layer aramid 1414 fiber B is wound on the outside of the reinforcement fiber carbon fiber A, and then covered by reinforcement fiber high-strength glass fiber C For pre-curing, use a braiding machine to weave a layer of fiber braided reinforcement layer aramid 1414 fiber D on the outer layer; finally inject multifunctional epoxy resin outside the outermost fiber braided reinforcement layer aramid 1414 fiber D, and the four-layer structure is cured at the same time Forming, its Tg ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
angleaaaaaaaaaa
Login to View More

Abstract

The invention relates to a high-temperature-resisting carbon fiber reinforced composite continuous sucker rod and a preparing device and method. According to the technical scheme, reinforced fiber carbon fiber (A) and fiber winding reinforced layer aramid fiber 1414 fiber (B) in the axial direction of a rod body are sequentially arranged from interior to exterior; and reinforced fiber high-strength glass fiber (C) and fiber weaving reinforced layer aramid fiber 1414 fiber (D) are arranged in the axial direction of the rod body, polyfunctional group epoxy resin is injected into the exterior of the outermost fiber weaving reinforced layer aramid fiber 1414 fiber (D), and four layers of structures are solidified and formed at the same time, wherein the Tg value reaches more than 210 DEG C, and the continuous length of the manufactured rod body ranges from 300 m to 5,000m. The sucker rod has the beneficial effects that the sucker rod is endowed with superior temperature resistance, eccentric wear resistance and radial and axial pressure resistance and small winding diameter, the production efficiency of products formed at a time is high, operation is easy and convenient, and performance is stable.

Description

technical field [0001] The invention relates to a continuous sucker rod, a preparation device and a method, in particular to a high-temperature resistant carbon fiber reinforced composite material continuous sucker rod, a preparation device and a method. Background technique [0002] Due to the increasingly complex types of developed reservoirs, the continuous increase of well depth and the continuous deterioration of the well and mine environment, the problems of corrosion and eccentric wear have become problems that need to be solved urgently in the oil production process of oilfields. Because of its light weight, high strength and corrosion resistance, composite sucker rods have gradually replaced traditional metal sucker rods. The composite material sucker rods currently used mainly include two categories: glass fiber reinforced plastic sucker rods and carbon fiber reinforced composite continuous sucker rods. FRP sucker rods are prepared by pultrusion of glass fiber rei...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B29C70/52B29C70/54E21B17/20
CPCB29C70/521B29C70/525E21B17/00E21B17/20
Inventor 王瑞星李强刘波
Owner SHENGLI OIL FIELD XINDA PIPE IND TECH DEV CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products