Process for electroplating sand nickel on automobile heat-dissipation grating

A technology of heat dissipation grille and electroplating process, applied in jewelry and other directions, can solve the problems of poor brightness and softness of pearl nickel coating, and achieve the effect of being conducive to chemical bonding, improving bonding force and long service time

Inactive Publication Date: 2015-12-02
太仓市金鹿电镀有限公司
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the treatment process provided by this patent, the composition of the pearl nickel plating solution is simple, and no brightener or emulsifier is added, so the bright effect of the pearl nickel plating is not good and not soft.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Process for electroplating sand nickel on automobile heat-dissipation grating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0055] The following examples are used to illustrate the present invention, but should not be used to limit the scope of the present invention. The implementation conditions used in the examples can be further adjusted according to the manufacturer's conditions, and the unspecified implementation conditions are usually conventional experimental conditions.

[0056] A kind of sandy nickel electroplating process of automobile radiator grille according to the present invention comprises the following steps:

[0057] 1) Degreasing

[0058] Carry out degreasing and dust removal treatment on the surface of the plastic substrate of the injection-molded automobile radiator grille, and then put it into the cleaning tank and rinse it with water;

[0059] 2) coarsening

[0060] Send the plastic substrate into the roughening liquid tank for roughening treatment, then put it into the cleaning tank and rinse it with clean water. The roughening temperature is 50-60°C, and the roughening ti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a process for electroplating sand nickel on an automobile heat-dissipation grating. The process comprises the following steps: 1), oil removal; 2), expansion; 3), roughening; 4), reduction; 5), preimpregnation; 6), activation; 7), dispergation; 8), electroplating. According to the process, an electroplating pretreatment process for a plastic base material is improved, the whole process is environment-friendly and nonhazardous, chemical plating is not required to be used since a specially-made sand nickel electroplating solution is used, the operation is easier, the process stability is improved, the wastewater treatment is simple, the production time is greatly shortened, a hanging tool is not required to be replaced in the production process, and the production efficiency is greatly improved.

Description

technical field [0001] The invention relates to a sand nickel electroplating process for an automobile radiator grille. Background technique [0002] Electroplating is the process of plating a thin layer of other metals or alloys on the surface of the base material by the principle of electrolysis. It is a process of using electrolysis to attach a layer of metal film to the surface of metal or other material parts to prevent metal Oxidation (such as rust), improve wear resistance, electrical conductivity, reflectivity, corrosion resistance (copper sulfate, etc.) and improve appearance. [0003] Among them, in addition to iron-based cast iron, steel and stainless steel, the electroplating substrate materials also include non-ferrous metals, or ABS plastics, polypropylene, polysulfone and phenolic plastics, and electroplating on the surface of plastic substrates is called plastic electroplating. . Plastic electroplating products have the advantages of light weight, easy proc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C25D7/00C25D3/12
Inventor 支建明
Owner 太仓市金鹿电镀有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products