Composite artificial stone table board and preparation method thereof

A technology of artificial stone and panels, applied in the field of composite artificial stone countertops and its preparation, can solve the problems of poor heat resistance, easy to break, easy to deform, etc., and achieve good heat resistance, high bending resistance, and impact resistance strong effect

Active Publication Date: 2015-11-18
来宾环球经典新型建材有限公司
View PDF4 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to overcome the problems of easy deformation, easy breakage, poor heat resistance, and rapid aging of the existing artificial stone countertops, and provide a high-strength, torsion-resistant, high-bending deformation-resistant performance, high thermal conductivity, and heat dissipation. Fast, heat-resistant, flame-retardant and non-aging and yellowing composite artificial stone countertops

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite artificial stone table board and preparation method thereof
  • Composite artificial stone table board and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Prepare composite artificial stone slab surface materials (×1kg) according to the following proportions by weight: surface quartz sand 60, surface quartz powder 5, curing agent 0.2, accelerator 0.05, solvent 3, multifunctional epoxy resin 7, coupling agent 0.02 , pigment 0.5, thermal powder 5.

[0032] The quartz sand is 8 mesh, the quartz powder is 60 mesh, the curing agent is dicyandiamide, the accelerator is 2-methylimidazole, and the solvent is N,N-dimethylformamide, The multifunctional epoxy resin is phenol novolac epoxy resin (Nan Ya Epoxy Co., Ltd. 638), the coupling agent is KH550 silane coupling agent, the pigment is iron red, and the heat conducting powder is aluminum nitride.

[0033] Prepare the composite artificial stone slab substrate layer raw materials (×4kg) according to the following weight ratio: aluminum hydroxide 60, substrate layer quartz powder 5, curing agent 0.2, accelerator 0.10, solvent 4, multifunctional epoxy resin 15, Coupling agent 0.02, ...

Embodiment 2

[0042] Prepare composite artificial stone plate surface layer raw materials according to the following weight ratio (×1kg): surface layer quartz sand 90, surface layer quartz powder 40, curing agent 0.5, accelerator 0.28, solvent 3, multifunctional epoxy resin 14, coupling agent 0.05 , Pigment 0.6, thermal powder 3.

[0043] The quartz sand is 16 mesh, the quartz powder is 100 mesh, the curing agent is m-phenylenediamine, the accelerator is N,N,2-methylimidazole, the solvent is butanone, and the The multifunctional epoxy resin is o-cresol novolac epoxy resin (Nan Ya Epoxy Co., Ltd. 704), the coupling agent is KH550 silane coupling agent, the pigment is iron yellow, and the heat conducting powder is aluminum powder.

[0044] Prepare the composite artificial stone slab substrate layer raw materials (×6kg) according to the following weight ratio: aluminum hydroxide 90, substrate layer quartz powder 40, curing agent 0.5, accelerator 0.2, solvent 5, multifunctional epoxy resin 25, ...

Embodiment 3

[0053] Prepare composite artificial stone slab surface material (×1kg) according to the following proportions by weight: surface quartz sand 75, surface quartz powder 22.5, curing agent 3, accelerator 0.15, solvent 4, multifunctional epoxy resin 12, coupling agent 0.035 , Pigment 0.3, thermal conductive powder 4.

[0054] The quartz sand is 26 mesh, the quartz powder is 140 mesh, the curing agent is novolac (Shandong Shengquan Chemical, SH-1066), the accelerator is 2-phenylimidazole, and the solvent is cyclo Hexanone, the multifunctional epoxy resin is bisphenol A type novolak epoxy resin (Changchun Resin Factory BNE200), the coupling agent is KH792 silane coupling agent, the pigment is phthalocyanine blue, and the heat conducting powder is aluminum oxide powder .

[0055] Prepare the composite artificial stone slab substrate layer raw materials (×8kg) according to the following weight ratio: aluminum hydroxide 75, substrate layer quartz powder 22.5, curing agent 3, accelerat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
bending strengthaaaaaaaaaa
flexural strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a composite artificial stone table board and a preparation method thereof. The composite artificial stone table board comprises a surface layer and a base material layer, wherein the surface layer is prepared from raw materials, namely, quartz sand, quartz powder, a curing agent, an accelerant, a solvent, multifunctional epoxy resin, a coupling agent, a pigment and heat-conducting powder; the base material layer is prepared from raw materials, namely, aluminum hydroxide powder, quartz powder, a curing agent, an accelerant, a solvent, multifunctional epoxy resin, a coupling agent and a glass mat. The composite artificial stone table board has the advantages that the table board is high in strength, high in torsion and bending deformation resistance, high in heat conductivity coefficient, quick in heat dissipation, good in heat resistance and flame-retardant, does not age and yellow easily and the like, and the table board is suitable for popularization and application.

Description

technical field [0001] The invention relates to the technical field of processing stone or stone-like materials, in particular to a composite artificial stone countertop and a preparation method thereof. technical background [0002] Artificial stone slabs are mainly used for kitchen countertops, laboratory countertops, window sills, dining tables, coffee tables, computers, bar counters, commercial plazas, etc. At present, most of the artificial stones used in the market use unsaturated polyester as a binder, and inorganic marble, quartz stone and other scraps are used as aggregates. Due to the low glass transition temperature of unsaturated polyester (<110 ° C =, and When the particles of different particle sizes are mixed with viscous polyester, it is easy to cause uneven mixing, resulting in poor homogeneity of the substrate. Therefore, the molded substrate has problems such as rapid aging, easy deformation, weak impact resistance, and easy cracking or breaking. , Ser...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/32C04B22/06C04B24/12C04B24/24B32B33/00
Inventor 朱学文丁德政郭栋杨东生蔡建亮
Owner 来宾环球经典新型建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com