Anti-dazzle glass etching liquid and preparation method thereof

A technology of anti-glare glass and etching solution, which is applied in the field of anti-glare glass etching solution and its preparation, and can solve the problems of limiting anti-glare glass, anti-glare glass transmittance and atomization rate, poor impact resistance, unreasonable formula, etc. problem, to achieve the effect of preventing further corrosion, improving the etching effect, and promoting the refinement of grains

Active Publication Date: 2015-11-11
山东御银光电科技有限公司
View PDF4 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the preparation process of anti-glare glass, chemical etching is a method that is often used, and the etching solution is an important factor affecting the etching; the formula of the existing etching solution is not very reasonable, and the obtained anti-glare glass has transmittance and The defects of atomization rate and poor impact resistance limit the application of anti-glare glass

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A kind of antiglare glass etchant that the present invention proposes, its raw material comprises the following components by weight: 35 parts of hydrofluoric acid, 10 parts of ammonium bifluoride, 12 parts of ammonium fluoride, 10 parts of calcium fluoride, 1 part of potassium hydrogen fluoride, 25 parts of ammonium chloride, 3 parts of potassium sulfate, 5 parts of barium sulfate, 1 part of potassium phosphate, 3 parts of sodium fluoroborate, 1 part of agar, 3 parts of sodium alginate, 2 parts of sodium carboxymethyl cellulose, 2 parts of silica sol , 0.2 parts of styrene-butadiene rubber, 3 parts of propylene glycol, 1 part of propylene glycol, 2 parts of sucrose, 50 parts of sulfuric acid solution with a mass fraction of 20%, and 100 parts of water.

[0018] The preparation method of an antiglare glass etching solution proposed by the present invention comprises the following steps: adding water into a sulfuric acid solution with a mass fraction of 20% according to t...

Embodiment 2

[0020] A kind of antiglare glass etchant that the present invention proposes, its raw material comprises the following components by weight: 45 parts of hydrofluoric acid, 5 parts of ammonium bifluoride, 20 parts of ammonium fluoride, 2 parts of calcium fluoride, 5 parts of potassium bifluoride, 10 parts of ammonium chloride, 10 parts of potassium sulfate, 1 part of barium sulfate, 5 parts of potassium phosphate, 0.1 part of sodium fluoroborate, 3 parts of agar, 1 part of sodium alginate, 5 parts of sodium carboxymethyl cellulose, 0.1 part of silica sol , 1.5 parts of styrene-butadiene rubber, 1 part of propylene glycol, 5 parts of propylene glycol, 0.5 part of sucrose, 30 parts of sulfuric acid solution with a mass fraction of 30%, and 150 parts of water.

[0021] The preparation method of a kind of anti-glare glass etching solution proposed by the present invention comprises the following steps: adding water into a sulfuric acid solution with a mass fraction of 30% according ...

Embodiment 3

[0023] A kind of antiglare glass etchant that the present invention proposes, its raw material comprises the following components by weight: 42 parts of hydrofluoric acid, 8 parts of ammonium bifluoride, 13 parts of ammonium fluoride, 8 parts of calcium fluoride, 4 parts of potassium bifluoride, 19 parts of ammonium chloride, 6.8 parts of potassium sulfate, 3.2 parts of barium sulfate, 4.2 parts of potassium phosphate, 0.9 parts of sodium fluoroborate, 2 parts of agar, 2.2 parts of sodium alginate, 3.8 parts of sodium carboxymethylcellulose, 1 part of silica sol , 0.9 parts of styrene-butadiene rubber, 2.2 parts of propylene glycol, 3.5 parts of propylene glycol, 1.3 parts of sucrose, 40 parts of sulfuric acid solution with a mass fraction of 25%, and 120 parts of water.

[0024]The preparation method of a kind of anti-glare glass etching solution proposed by the present invention comprises the following steps: adding water into a sulfuric acid solution with a mass fraction of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
transmittivityaaaaaaaaaa
reflectanceaaaaaaaaaa
glossaaaaaaaaaa
Login to View More

Abstract

The invention discloses anti-dazzle glass etching liquid which comprises, by weight parts, 35-45 parts of hydrofluoric acid, 5-10 parts of ammonium bifluoride, 12-20 parts of ammonium fluoride, 2-10 parts of calcium fluoride, 1-5 parts of potassium bifluoride, 10-25 parts of ammonium chloride, 3-10 parts of potassium sulfate, 1-5 parts of barium sulfate, 1-5 parts of potassium phosphate, 0.1-3 parts of sodium fluoroborate, 1-3 parts of agar, 1-3 parts of sodium alginate, 2-5 parts of sodium carboxymethyl cellulose, 0.1-2 parts of silica sol, 0.2-1.5 parts of butadiene styrene rubber, 1-3 parts of propylene glycol, 1-5 parts of propylene glycol, 1-5 parts of propanediol, 0.5-2 parts of sucrose, 30-50 parts of sulfuric acid solution and 100-150 parts of water. The invention further provides a method for preparing the anti-dazzle glass etching liquid. A process is simple, the conditions are moderate, the obtained etching liquid is good in stability; and prepared anti-dazzle glass is high in transmittance and degree of atomization, excellent in impact resistance and good in anti-dazzle effect.

Description

technical field [0001] The invention relates to the technical field of anti-glare glass, in particular to an anti-glare glass etchant and a preparation method thereof. Background technique [0002] Glass is widely used in daily life due to its advantages of high strength, excellent optical properties, and long-term working stability. However, due to the high reflectivity of the glass surface, it often causes "glare attack", which is what we often call "light pollution". And trouble; when we stop in front of the glass window to explore the scenery inside the window, the reflection of the glass surface often prevents us from clearly observing the scenery inside the window, etc., all of which are caused by the light reflection on the glass surface. To reduce the impact of reflected light from the glass, matting the glass can have a good effect. [0003] Anti-glare glass can reduce the interference of ambient light, reduce the reflection of the screen, improve the viewing angl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C15/00
Inventor 凌卫平
Owner 山东御银光电科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products