A processing method for opening centripetal slots of titanium alloy and glass fiber reinforced plastic composite conical parts

A processing method and FRP technology, applied in the field of machining, can solve the problems of slag dropping, design index influence, poor rigidity, etc., and achieve the effects of small deformation of the finished product, reasonable and reliable process method, and small deformation of the product

Active Publication Date: 2017-11-07
HUBEI SANJIANG AEROSPACE GRP HONGYANG ELECTROMECHANICAL
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The embodiment of the present application provides a processing method for the open centripetal notch of titanium alloy and FRP composite conical parts, which solves or partially solves the slag falling in different parts around the opening in the prior art, and the rigidity is poor during processing. The technical problems that have a great impact on the indicators have achieved the technical effect of ensuring that the process method is reasonable and reliable, the product deformation is small, the stability is good, and the processing quality of the parts can be effectively guaranteed.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A processing method for opening centripetal slots of titanium alloy and glass fiber reinforced plastic composite conical parts
  • A processing method for opening centripetal slots of titanium alloy and glass fiber reinforced plastic composite conical parts
  • A processing method for opening centripetal slots of titanium alloy and glass fiber reinforced plastic composite conical parts

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0062] Milling process design: fillet milling, rough milling above the opening, rough milling below the opening, semi-finishing the entire opening 2, semi-finishing the slope, finishing the entire contour, and finishing the fillet; specifically include:

[0063] S1: Fix the milling clamp on the workbench, the conical part 1 fits the inner hole through the milling clamp, attach the flat milling clamp to the bottom surface, place the milling clamp pressure plate on the small end of the conical part 1, and align the outer circle of the large end. Within 0.1.

[0064] S2: Process the four rounded corners by milling holes. This process uses a YG8 carbide end mill with a specification of Ф10. The speed of the spindle is controlled at 600r / min, and the feed is 500mm / r.

[0065] S3: Align the quadrant line, rough mill the opening of the conical part 1; when processing the opening 2, divide the opening 2 into two parts, the upper end of the opening is made of FRP material, and mainly c...

Embodiment 2

[0071] Milling process design: fillet milling, rough milling above the opening, rough milling below the opening, semi-finishing the entire opening 2, semi-finishing the slope, finishing the entire contour, and finishing the fillet; specifically include:

[0072] S1: Fix the milling clamp on the workbench, the conical part 1 fits the inner hole through the milling clamp, attach the flat milling clamp to the bottom surface, place the milling clamp pressure plate on the small end of the conical part, and align the outer circle of the large end at 0.1 within.

[0073] S2: Process the four rounded corners by milling holes. This process uses a YG8 carbide end mill with a specification of Ф10. The spindle speed is controlled at 700r / min and the feed is 550mm / r.

[0074] S3: Align the quadrant line, rough mill the opening of the conical part 1; when processing the opening 2, divide the opening 2 into two parts, the upper end of the opening is made of FRP material, and mainly cut off t...

Embodiment 3

[0079] Milling process design: fillet milling, rough milling above the opening, rough milling below the opening, semi-finishing the entire opening 2, semi-finishing the slope, finishing the entire contour, and finishing the fillet; specifically include:

[0080] S1: Fix the milling clamp on the workbench, the conical part 1 fits the inner hole through the milling clamp, attach the flat milling clamp to the bottom surface, place the milling clamp pressure plate on the small end of the conical part, and align the outer circle of the large end at 0.1 within.

[0081] S2: Process the four rounded corners by milling holes. This process uses a YG8 carbide end mill with a specification of Ф10. The spindle speed is controlled at 800r / min, and the feed is 600mm / r.

[0082] S3: Align the quadrant line, rough mill the opening 2 of the conical part 1; when processing the opening 2, divide the opening 2 into two parts, the upper end of the opening is made of FRP material, and mainly cut th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method for processing a titanium alloy and FRP compound conical part with a centripetal notch, comprising the following steps: fixing the conical part on a workbench; roughly milling the four rounded corners of the conical part; rough milling the opening of the conical part; The side of the opening is processed by the spindle orientation, and the sag of the opening is semi-finishing; the opening contour and slope of the conical part are finely milled; the four fillet contours and the sag of the conical part are finely milled. This processing method reasonably allocates the process margin, controls the deformation, controls the precision of the inner hole of the large end of the part, and uses it as the positioning reference when opening, regulates the process parameters in the cutting process, improves product quality and processing efficiency, and increases the rigidity of the part. , Improve the stability during processing.

Description

technical field [0001] The invention relates to the technical field of machining, in particular to a method for processing a concentric notch of a composite conical part made of titanium alloy and glass fiber reinforced plastic. Background technique [0002] In recent years, with the continuous advancement of science and technology, material technology has developed rapidly. As a new type of material, composite material has gradually become one of the leading materials in the 21st century. Composite materials have the characteristics of light weight, high specific strength, specific modulus, corrosion resistance, high temperature resistance, and ablation resistance. They are ideal materials for weapons such as aircraft, missiles, and aerospace vehicles. "Metal + composite material" is a kind of structural parts that are relatively common in missile weapon systems at present. At present, it is mainly manufactured by winding, suiting, molding and other technologies, and then ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23C3/28
CPCB23C3/28B23C2220/36B23C2220/605
Inventor 刘凯万佩万方云
Owner HUBEI SANJIANG AEROSPACE GRP HONGYANG ELECTROMECHANICAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com