Method for displaying P91 and P92 ferrite heat-resistant steel original austenite crystal boundary

A technology of austenite grain boundary and heat-resistant steel, which is used in the preparation of test samples, measuring devices, and material analysis by optical means, to achieve the effects of simple operation, good reproducibility and stable display effect.

Active Publication Date: 2015-10-14
DONGFANG BOILER GROUP OF DONGFANG ELECTRIC CORP
View PDF4 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The object of the present invention is to aim at the deficiencies of the above-mentioned prior art, to provide a simple, convenient, fast, safe, easy-to-control etching process and stable display effect, good reproducibility, low cost, non-toxic and pollution-free, easy to observe A new method with simple equipment and no special requirements. It can clearly and completely display the original austenite grain boundary of P91 and P92 ferritic heat-resistant steel, so as to accurately measure the austenite grain size. Research, quality control and quality problem analysis and processing provide accurate and reliable detection basis

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for displaying P91 and P92 ferrite heat-resistant steel original austenite crystal boundary
  • Method for displaying P91 and P92 ferrite heat-resistant steel original austenite crystal boundary
  • Method for displaying P91 and P92 ferrite heat-resistant steel original austenite crystal boundary

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] (1) Sample: P92 ferritic heat-resistant steel (coarse grain structure)

[0031] (2) Sulfuric acid electrolyte concentration: 5%, sulfuric acid electrolysis voltage 8V, sulfuric acid electrolysis time: 30s;

[0032] (3) Nitric acid electrolyte concentration: 65-68%, nitric acid electrolysis voltage 11V, nitric acid electrolysis time: 8s;

[0033] (4) The complete and clear prior-austenite grain boundaries observed under an optical microscope at a power of 50 times are as follows: image 3 As shown, the measured austenite grain size is 00 grade.

Embodiment 2

[0035] (1) Sample: P92 ferritic heat-resistant steel (coarse grain structure)

[0036] (2) Sulfuric acid electrolyte concentration: 10%, sulfuric acid electrolysis voltage 8V, sulfuric acid electrolysis time: 35s;

[0037] (3) Nitric acid electrolyte concentration: 65-68%, nitric acid electrolysis voltage 10V, nitric acid electrolysis time: 12s;

[0038](4) The complete and clear prior-austenite grain boundaries observed under an optical microscope at a power of 50 times are as follows: Figure 4 As shown, the austenite grain size was determined to be 0.5.

Embodiment 3

[0040] (1) Sample: P92 ferritic heat-resistant steel (fine grain structure)

[0041] (2) Sulfuric acid electrolyte concentration (volume percentage): 15%, sulfuric acid electrolysis voltage 7.5V, sulfuric acid electrolysis time: 40s;

[0042] (3) Nitric acid electrolyte concentration (mass percentage): 60-64%, nitric acid electrolysis voltage 10V, nitric acid electrolysis time: 10s;

[0043] (4) The complete and clear prior-austenite grain boundary diagram observed under the optical microscope at 100 times is as follows Figure 5 As shown, the austenite grain size was determined to be grade 7.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for displaying P91 and P92 ferrite heat-resistant steel original austenite crystal boundary. The P91 and P92 ferrite heat-resistant steel original austenite crystal boundary can be clearly and completely displayed through adopting an aqueous sulfuric acid solution electrolytic etching and concentrated nitric acid solution electrolytic etching combination two-step electrolytic etching technology in order to accurately determine the austenite grain size. The method has the advantages of simple, convenient, fast and safe operation, easy control of the etching process, stable display effect and good reappearance.

Description

technical field [0001] The invention relates to a method for displaying the original austenite grain boundary of P91 and P92 ferritic heat-resistant steels, belonging to the technical field of metallographic display. Background technique [0002] P91 and P92 ferritic heat-resistant steels have excellent high-temperature performance and are widely used in super (super) critical boiler production. Since the actual austenite grain size of the steel directly affects the properties of the steel, the coarse austenite grains often lead to the coarse structure of the material after cooling, so that the material has lower plasticity and toughness. For this reason, strengthening the inspection of the actual austenite grain size of P91 and P92 steel has always been an important indicator for boiler manufacturers to evaluate the quality of such materials. It is of great significance to study the effect of grain size on performance. [0003] In view of the great influence of the prior ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): G01N21/84G01N15/02G01N1/28G01N1/32
Inventor 曾辉毛世勇李健张学星
Owner DONGFANG BOILER GROUP OF DONGFANG ELECTRIC CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com