Compression-resistant and wear-resistant lubricating agent

A lubricant, molybdenum disulfide technology, applied in the field of compressive and wear-resistant lubricants, can solve the problems affecting the application of nano-molybdenum disulfide, easy to agglomerate, difficult to disperse, etc.

Inactive Publication Date: 2015-09-16
广东正骉国际贸易有限公司
View PDF6 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are problems such as easy agglomeration and difficult dispersion of nano-molybdenum disulfide in lubricants, which affect the application of nano-molybdenum disulfide in lubricants.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] 90 parts by weight of base oil, 2.5 parts by weight of polymethacrylate, 3 parts by weight of phosphobisoctyl basic zinc salt, 1.8 parts by weight of trihydroxybenzoic acid, 1 part by weight of dienyl succinyl The phenylalanine of imine, 1.5 parts by weight, the calcium sulfonate of 0.8 parts by weight, the graphite powder of 2 parts by weight, the modified molybdenum disulfide of 2.5 parts by weight, the naphthyl phenyl phosphate of 2.0 parts by weight and 1.2 parts by weight parts of polyvinyl n-propyl ester.

[0020] Concrete preparation operation is:

[0021] Step 1: Take by weighing 2g ammonium molybdate, 1.5g sulfur powder and 7.5ml glycerol 180 ℃ of mixing reaction 2h, after reaction finishes, extract reaction product with toluene, reclaim lower floor solution, wash and dry with water and make molybdenum disulfide Use; Next, mix 1ml of tetraethoxy silicon with 25ml of absolute ethanol, then add 2.5ml of triethanolamine, 1.8mL of distilled water and 0.12g of hexa...

Embodiment 2

[0026] 95 parts by weight of base oil, 2.0 parts by weight of polymethacrylate, 3.5 parts by weight of thiophosphobisoctyl basic zinc salt, 1.5 parts by weight of trihydroxybenzoic acid, 1.5 parts by weight of dienyl succinyl The phenylalanine of imine, 1.2 parts by weight, the calcium sulfonate of 1.2 parts by weight, the graphite powder of 1.2 parts by weight, the modified molybdenum disulfide of 3.0 parts by weight, the naphthyl phenyl phosphate of 1.8 parts by weight and 1.5 parts by weight parts of polyvinyl n-propyl ester.

[0027] Concrete preparation operation is:

[0028] Weigh 2g of ammonium molybdate, 1.5g of sulfur powder and 7.5ml of glycerin and mix and react for 2h at 180°C. After the reaction, extract the reaction product with toluene, reclaim the lower layer solution, wash and dry with water to obtain molybdenum disulfide for use; Mix 1ml of tetraethoxy silicon with 25ml of absolute ethanol, then add 2.5ml of triethanolamine, 1.8mL of distilled water and 0.12...

Embodiment 3

[0033] A pressure-resistant and wear-resistant lubricant, the composition of which is as follows: 90-95 parts by weight of base oil, 2.8-3 parts by weight of polymethacrylate, 3-3.5 parts by weight of basic zinc salt of phosphobisoctyl, 1-1.2 parts by weight of trihydroxybenzoic acid, 1-1.5 parts by weight of dienyl succinimide, 0.8-1 parts by weight of phenylalanine, 1-1.5 parts by weight of calcium sulfonate, 0.8-1.2 parts by weight Graphite powder in parts by weight, modified molybdenum disulfide in 3.2-3.5 parts by weight, naphthyl phenyl phosphate in 2-2.5 parts by weight and polyvinyl n-propyl ester in 1.5-1.8 parts by weight.

[0034] Concrete preparation operation is:

[0035] Weigh 2g of ammonium molybdate, 1.5g of sulfur powder and 7.5ml of glycerin and mix and react for 2h at 180°C. After the reaction, extract the reaction product with toluene, reclaim the lower layer solution, wash and dry with water to obtain molybdenum disulfide for use; Mix 1ml of tetraethoxy s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Hardnessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a compression-resistant and wear-resistant lubricating agent comprising the following components in parts by weight: 90-95 parts of base oil, 2.0-2.5 parts of polymethacrylate, 3-3.5 parts of base zinc salt of dioctyl thiophosphate, 1.5-1.8 parts of trihydroxybenzoic acid, 1-1.5 parts of dialkenyl succinimide, 1.2-1.5 parts of phenylalanine, 0.8-1.2 parts of calcium sulfonate, 1.2-2 parts of graphite powder, 2.5-3.0 parts of modified molybdenum disulfide, 1.8-2.0 parts of naphthylphenyl phosphate and 1.2-1.5 parts of polyvinyl n-propyl ester. According to the technical scheme, all the components take a synergistic effect, so that the performance of the base oil is improved; and all the components can be uniformly dispersed, so that the lubricating property of the lubricating oil is good, and particularly the wear resistance and high-temperature resistance are remarkable.

Description

technical field [0001] The invention relates to the field of mechanical lubrication, in particular to a pressure-resistant and wear-resistant lubricant. Background technique [0002] Nano-molybdenum disulfide has a layered structure, and the sliding between layers is very easy, and the S atoms in molybdenum disulfide have a strong affinity for the metal surface, which can form a firm lubricating film on the metal surface, thereby significantly reducing friction and wear. However, there are problems such as easy agglomeration and difficult dispersion of nano-molybdenum disulfide in lubricants, which affect the application of nano-molybdenum disulfide in lubricants. In addition, with the development of large-scale machinery, the performance requirements of lubricating oil for high temperature resistance, pressure resistance and wear resistance are also getting higher and higher. Therefore, it is necessary to provide a lubricant that can uniformly disperse nano molybdenum disu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C10M169/04C10N30/04C10N30/06C10N30/08
Inventor 程叶红朱文霞
Owner 广东正骉国际贸易有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com