Sapphire green glaze for faience

A kind of product and gemstone technology, applied in the field of gem green glaze, can solve the problem that ceramic products cannot achieve decorative effects, etc., and achieve the effect of easy permanent preservation and crystal clear glaze color

Inactive Publication Date: 2017-03-22
界首市王京胜彩陶艺术有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the limitations of high-temperature pigments, glazes, and craftsmanship, ceramic products have not been able to achieve perfect decorative effects.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A sapphire green glaze for painted pottery products is characterized in that it is made of the following components in parts by weight: 60 parts of electronic grade red lead, 20 parts of silicon dioxide, 5 parts of Suzhou soil, 5 parts of copper oxide, modified 5 parts of sea mud, 0.2 parts of graphite, 0.2 parts of barium stearate, 0.2 parts of cordierite powder, 2 parts of borax, 0.5 parts of cesium beryl, 3 parts of aluminum silicate, 0.5 parts of selenium powder, 1.5 parts of kyanite, 0.5 parts of zirconium silicate, 0.3 parts of zinc oxide, 0.2 parts of cobalt powder, and 0.3 parts of shell powder; when preparing, mix the above components evenly, send them into a grinder, grind them continuously for 4 hours, pass through a 300-mesh sieve, and heat to 920- At 950°C, it is melted at high temperature to form a co-melt.

[0023] The preparation method of above-mentioned modified sea mud is:

[0024] 1) Get 100 parts by weight of sea mud, 10 parts by weight of tert-but...

Embodiment 2

[0035] A sapphire green glaze for painted pottery products is characterized in that it is made of the following components in parts by weight: 70 parts of electronic grade red lead, 10 parts of silicon dioxide, 6 parts of Suzhou soil, 4 parts of copper oxide, modified 6 parts of sea mud, 0.1 part of graphite, 0.3 part of barium stearate, 0.1 part of cordierite powder, 3 parts of borax, 0.4 part of cesium beryl, 4 parts of aluminum silicate, 0.4 part of selenium powder, 2 parts of kyanite, 0.4 parts of zirconium silicate, 0.4 parts of zinc oxide, 0.1 parts of cobalt powder, and 0.4 parts of shell powder; when preparing, mix the above components, send them into a grinder, grind them continuously for 4 hours, pass through a 300-mesh sieve, and heat to 920- At 950°C, it is melted at high temperature to form a co-melt.

[0036] The preparation method of above-mentioned modified sea mud is:

[0037] 1) Get 100 parts by weight of sea mud, 10 parts by weight of tert-butanol, 5 parts ...

Embodiment 3

[0048] A sapphire green glaze for painted pottery products is characterized in that it is made of the following components in parts by weight: 50 parts of electronic grade red lead, 30 parts of silicon dioxide, 4 parts of Suzhou soil, 6 parts of copper oxide, modified 4 parts of sea mud, 0.3 parts of graphite, 0.1 part of barium stearate, 0.3 parts of cordierite powder, 1 part of borax, 0.6 parts of cesium beryl, 2 parts of aluminum silicate, 0.6 parts of selenium powder, 1 part of kyanite, 0.6 parts of zirconium silicate, 0.2 parts of zinc oxide, 0.3 parts of cobalt powder, and 0.2 parts of shell powder; when preparing, mix the above components evenly, send them into a grinder, grind them continuously for 4 hours, pass through a 300-mesh sieve, and heat to 920- At 950°C, it is melted at high temperature to form a co-melt.

[0049]The preparation method of above-mentioned modified sea mud is:

[0050] 1) Get 100 parts by weight of sea mud, 10 parts by weight of tert-butanol, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a turquoise glaze for colored pottery products. The turquoise glaze is characterized by being prepared from the following components in parts by weight: 50-70 parts of electronic-grade red lead, 10-30 parts of silicon dioxide, 4-6 parts of Soochow clay, 4-6 parts of copper oxide, 4-6 parts of modified sea mud, 0.1-0.3 part of graphite, 0.1-0.3 part of barium stearate, 0.1-0.3 part of cordierite powder, 1-3 parts of borax, 0.4-0.6 part of morganite, 2-4 parts of aluminum silicate, 0.4-0.6 part of selenium powder, 1-2 parts of cyanite, 0.4-0.6 part of zirconium silicate, 0.2-0.4 part of zinc oxide, 0.1-0.3 part of cobalt powder and 0.2-0.4 part of shell powder. The prepared and fired turquoise glaze is glittering and translucent, bright and smooth in glaze color, and is as shine as the turquoise, and therefore, when the turquoise glaze is applied to colored pottery artworks, an excellent decoration effect can be achieved; the modified sea mud is added so that the finished product can be protected from peeling permanently and can be preserved permanently.

Description

technical field [0001] The invention relates to the technical field of pottery making, in particular to a gem green glaze used for painted pottery products. Background technique [0002] China is an ancient country of ceramics. When talking about ceramics, foreigners think of China. Pottery is an artificial form. The basic materials in ceramic form are earth, water, and fire. Only by mastering the plasticity and rheology of water and soil mixing, as well as the molding method and sintering law, can people promote the generation and evolution of ceramic art forms and make ceramic utensils produce beautiful forms. At the same time, it pays attention to the organic combination of modeling and decoration. Through people's keen inspiration and innovative consciousness, it captures and reveals the plastic beauty, flexibility beauty and expressive vitality of the soil. In this way, a new form of ceramic art emerges, which is mastered, developed and used by wise people. innovatio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C8/12
Inventor 王京胜陈翠英王影王敏王海涛
Owner 界首市王京胜彩陶艺术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com