Preparation method of red ceramic glaze

A kind of ceramic glaze and glaze technology, applied in the field of ceramic manufacturing, can solve the problems of few red pigments, dark colors, high prices, etc.

Pending Publication Date: 2022-06-03
武汉甄美颜料有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although red glazes are widely loved by the masses, it is difficult to manufacture high-quality red glazes due to the small number of red pigments required for the manufacture of red glazes and poor high temperature stability.
Commonly used red pigments for glazes are only a few types such as Dahong, Yuanzihong and Iron Oxide Red. Among them, the red glaze produced by Dahong has the best quality, bright color and high glaze brightness, but the price is very expensive; The red glaze produced by Yuanzihong pigment is also of good quality and bright glaze, but its color is too purple, not the red favored by Chinese people, and the price is relatively expensive; although iron oxide red pigment is cheap, but because of its chemical Poor stability and easy to change color at high temperature. The existing technology uses iron red as the chromogenic agent to produce low-grade red glaze. Not only is the color dark, but the glaze has low brightness and poor thermal shock resistance, making it difficult to achieve high-quality red. Quality requirements for glazes

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Top Glaze Base Glaze Composition: Feldspar 47.3 Frit 21.3 Kaolin 7 Calcite 10 Quartz 15

[0032] Bottom glaze base glaze composition: feldspar 47.3 frit 35.5 glass fiber 15 kaolin 4.5 calcium carbonate 15 quartz 15

[0033] Surface layer glaze iron red dosage 25

[0034] Bottom Glaze Pigment 0

[0035] Firing temperature 1185 degrees

[0036] Product: Bright glaze, bright red color, good thermal stability

Embodiment 2

[0038] Top Glaze Base Glaze Composition: Feldspar 47.3 Frit 21.3 Kaolin 7 Calcite 10 Quartz 15

[0039] Bottom glaze base glaze composition: feldspar 47.3 frit 35.5 glass fiber 15 kaolin 4.5 calcium carbonate 15 quartz 15

[0040] Surface layer glaze iron red dosage 25

[0041] Bottom Glaze Pigment Iron Oxide Red 22

[0042] Firing temperature 1185 degrees

[0043] Product: Bright glaze, bright red color, good thermal stability

Embodiment 3

[0045] Top Glaze Base Glaze Composition: Feldspar 47.3 Frit 21.3 Kaolin 7 Calcite 10 Quartz 15

[0046] Bottom glaze base glaze composition: feldspar 47.3 frit 35.5 glass fiber 15 kaolin 4.5 calcium carbonate 15 quartz 15

[0047] Surface layer glaze iron red dosage 15

[0048] Bottom Glaze Pigment No

[0049] Firing temperature 1185 degrees

[0050] Product: Bright glaze, dark red color, good thermal stability.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of red ceramic glaze. The preparation of the high-grade red glaze is realized by increasing the use amount of the iron oxide red pigment and a double-layer glaze process. The red ceramic glaze prepared by the invention is bright in color, bright in glaze surface, high in thermal shock resistance and low in price. The usage amount of the iron oxide red is more than 12%, preferably 16-30%, preferably 20-25%, and especially more than 40%.

Description

1. Technical field [0001] The invention belongs to the field of ceramic manufacturing, and particularly relates to a preparation method of red ceramic glaze. 2. Background technology [0002] Ceramic glaze is one of the important components of ceramics, which plays an important role in strengthening, anti-corrosion, dustproof and beautifying utensils. According to different colors, ceramic glazes are divided into blue glazes, black glazes, yellow glazes, red glazes, gray glazes and brown glazes. Among them, red glazes are the most widely used ceramic glazes. Compared with other color glazes, red glaze has always been favored by the Chinese due to the influence of traditional aesthetic concepts, and it is one of the most widely used color glaze varieties. Although red glaze is widely loved by the masses, it is difficult to manufacture high-quality red glaze due to the small variety of red pigments required for the manufacture of red glaze and poor high temperature stability....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/14C04B41/86C04B41/89
CPCC03C8/14C04B41/86C04B41/89C04B41/5022C04B41/52C04B41/0072C04B41/504
Inventor 王国良盛秀娟
Owner 武汉甄美颜料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products