Rubber compound for outsoles of insulated industrial rubber boots and preparation method of rubber compound

A technology for industrial and mining rubber boots and rubber mixing, which is applied to shoe soles, applications, clothing, etc., can solve the problems of poor viscosity, large deformation of the film, and large punching shrinkage, etc., and achieve the effect of small deformation, small punching shrinkage, and good viscosity.

Active Publication Date: 2015-08-26
JIHUA 3539 SHOE MAKING
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the actual formula design, the rubber content of the outsole design of industrial and mining rubber boots is very high, usually no less than 50%, and in order to increase the wear resistance, the proportion of synthetic rubber is also high, which brings Some problems in molding and bonding, such as large die-cut shrinkage, large film deformation, poor viscosity, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0023] The invention also discloses an outsole compound rubber for insulating industrial and mining rubber boots and a preparation method thereof, comprising the following steps:

[0024] a. Glue breaking: Break the No. 2 standard rubber on the rubber breaking machine according to the set weight, put the butadiene rubber into the rubber after the standard rubber is softened and roll it, and mix it initially to make a film;

[0025] b. Mastication: Throw the produced film into an open mill with a roll distance of less than 0.5mm and a roll temperature of 40°C to 50°C by thin pass plastication method. The cooled rubber material is put into the open mill with a roller distance of 5mm-8mm, covered with rollers and plasticized, and C.S.R rubber is added in parts by weight, and processed to obtain a blended film, and then the blended film is put into the roller pitch Plasticize the thin pass again in the open mixer with a thickness of less than 0.5mm, and finally put the rubber comp...

Embodiment 1

[0032] In this example, the rubber compounding raw materials include the following components by weight: 65 parts of No. 2 standard rubber, 25 parts of butadiene rubber, 10 parts of C.S.R rubber, 5.2 parts of insoluble sulfur, 1.5 parts of stearic acid, and 2.3 parts of active zinc oxide. 2.8 parts, 2.8 parts of accelerator, 2.5 parts of anti-aging agent, 50 parts of white carbon black, 1.2 parts of silane coupling agent (Si69), 1.2 parts of silica dispersant, 5 parts of solid coumarone resin, 5 parts of high wear-resistant carbon black parts, 6 parts of pine tar, 15 parts of engine oil;

[0033] In this embodiment, the accelerator is a mixture of accelerator DM, accelerator M, and accelerator D, wherein the amount of accelerator DM is 1.5, the amount of accelerator M is 0.5, and the amount of accelerator D is 0.8;

[0034] In this embodiment, the anti-aging agent is a mixture of anti-aging agent 4010 and anti-aging agent D, the amount of anti-aging agent 4010 is 1 part, and t...

Embodiment 2

[0050] In this example, the rubber compounding raw materials include the following components by weight: 70 parts of No. 2 standard rubber, 20 parts of butadiene rubber, 10 parts of C.S.R rubber, 5.4 parts of insoluble sulfur, 1.5 parts of stearic acid, and 2.3 parts of active zinc oxide. Parts, 2.9 parts of accelerator, 2.5 parts of anti-aging agent, 50 parts of white carbon black, 1.2 parts of silane coupling agent (Si69), 1.2 parts of silica dispersant, 5 parts of solid coumarone resin, 5 parts of high wear-resistant carbon black parts, 6 parts of pine tar, 15 parts of engine oil;

[0051] In this embodiment, the accelerator is a mixture of accelerator DM, accelerator M, and accelerator D, wherein the amount of accelerator DM is 1.5, the amount of accelerator M is 0.6, and the amount of accelerator D is 0.8;

[0052] In this embodiment, the anti-aging agent is a mixture of anti-aging agent 4010 and anti-aging agent D, the amount of anti-aging agent 4010 is 1 part, and the a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a rubber compound for outsoles of insulated industrial rubber boots. The rubber compound comprises components in parts by weight as follows: NO.2 standard rubber, butadiene rubber, C.S.R rubber, insoluble sulfur, stearic acid, activated zinc oxide, an accelerant, an anti-ageing agent, white carbon black, a Si69 silane coupling agent, a white carbon black dispersing agent, solid coumarone resin, high-wearability carbon black, pine tar and engine oil. The rubber compound for the outsoles of the insulated industrial rubber boots has excellent insulating property, all that is needed is to shape an outsole rubber piece, an insulating layer is not required to be added, the process is simple, the number of workers required for each piece production line is reduced by more than six, and the rubber compound has the characteristics of small punching shrinkage, small deformation during storage of rubber pieces, good stickiness, light weight, good wear resistance and the like.

Description

technical field [0001] The invention relates to a rubber compound, in particular to a rubber compound for the outsole of insulating industrial and mining rubber boots and a preparation method thereof. Background technique [0002] In recent years, with the progress of society and the improvement of protection requirements for mine workers, the ordinary industrial and mining rubber boots worn by miners have been gradually reduced, and such as insulating rubber boots, anti-smashing rubber boots, anti-puncture rubber boots or composite rubber boots with the above functions It is gradually increasing, and the state has also issued relevant industry standards in order to enable mine workers to get better labor protection. Insulated industrial and mining rubber boots that are widely used at present, most of the manufacturers adopt the method of adding an insulating layer between the wear-resistant outsole (basically non-insulated rubber) and the sponge midsole, and there are very ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L7/00C08L9/00C08L11/00C08L45/02C08L91/00C08K13/06C08K9/06C08K3/36C08K3/04C08K3/06C08K5/09C08K3/22A43B13/04B29B7/52B29B7/72
CPCA43B13/04C08L7/00C08L2205/035C08L9/00C08L11/00C08L45/02C08L91/00C08K13/06C08K9/06C08K3/36C08K3/04C08K3/06C08K5/09C08K2003/2296
Inventor 徐兴华
Owner JIHUA 3539 SHOE MAKING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap