Preparation method of artificial rutile

A technology of artificial rutile and acid-soluble titanium slag, which is applied to the removal of solid waste, titanium oxide/hydroxide, titanium dioxide, etc., can solve the problems of high investment cost, low quality of titanium-rich materials, and increase the difficulty of technical operation. Improved purity, improved efficiency, and easy leaching effects

Active Publication Date: 2015-08-26
YUNNAN MINZU UNIV
View PDF2 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

CN 100455683C discloses a method for producing titanium-rich material from electric furnace titanium slag. The method uses titanium slag from a certain place in Yunnan as raw material, and proposes an acid-base combined leaching method to obtain TiO 2 >90% titanium-rich material, this process uses high-pressure equipment, the investment cost is high, and the difficulty of technical operation is also increased, and the quality of the titanium-rich material obtained is low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of artificial rutile
  • Preparation method of artificial rutile
  • Preparation method of artificial rutile

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0076] Embodiment 1: the preparation of artificial rutile

[0077] The implementation steps of this embodiment are as follows:

[0078] A. Modification treatment

[0079] The acid-soluble titanium slag obtained by Pangang Group Titanium Industry Co., Ltd. was analyzed by the method described in this specification, and its chemical composition is TiO by weight. 2 72.0%, SiO 2 9.5%, MgO 1.5% and CaO 0.5%; the particle size of the acid-soluble titanium slag is -100 mesh, which is 80% by weight.

[0080] According to the weight ratio of acid-soluble titanium slag and modifier is 5:1.4, described acid-soluble titanium slag and sodium carbonate modifier are mixed homogeneously, then in microwave box reactor (HM Type) in the microwave reactor sold under the conditions of microwave reactor frequency of 912MHz and temperature of 780°C for 2.4h, a modified acid-soluble titanium slag was obtained, which was detected by the method described in this specification. The chemical compos...

Embodiment 2

[0085] Embodiment 2: the preparation of artificial rutile

[0086] The implementation steps of this embodiment are as follows:

[0087] A. Modification treatment

[0088] The acid-soluble titanium slag obtained by Yunnan Xinli Nonferrous Metals Co., Ltd. was analyzed by the method described in this manual, and its chemical composition is TiO by weight 2 72.5%, SiO 2 9.2%, MgO 1.2% and CaO 0.5%; the particle size of the acid-soluble titanium slag is -100 mesh, which is 80 86 82 84 84 83% by weight.

[0089] According to the weight ratio of acid-soluble titanium slag and modifying agent is 5:1.6, described acid-soluble titanium slag and sodium hydroxide modifying agent are mixed uniformly, then by Kunming University of Science and Technology with trade name microwave box reactor ( In the microwave reactor sold by HM type), the frequency of the microwave reactor is 915MHz and the temperature is 800°C, and the modification treatment is carried out for 3.6h to obtain a modifie...

Embodiment 3

[0094] Embodiment 3: the preparation of artificial rutile

[0095] The implementation steps of this embodiment are as follows:

[0096] A. Modification treatment

[0097] The acid-soluble titanium slag obtained by Yunnan Copper Group Titanium Industry Co., Ltd. was analyzed by the method described in this specification, and its chemical composition is TiO by weight 2 72.8%, SiO 2 9.0%, MgO 0.9% and CaO 0.2%; the particle size of the acid-soluble titanium slag is -100 mesh, which is 82% by weight.

[0098] According to the weight ratio of acid-soluble titanium slag and modifier is 5:1.0, mix the acid-soluble titanium slag with sodium carbonate, sodium hydroxide, phosphorus pentoxide, sodium phosphate or ammonium dihydrogen phosphate modifier evenly , and then in a microwave reactor sold by Kunming University of Science and Technology under the condition of a frequency of 918MHz and a temperature of 750°C in a microwave reactor sold under the trade name Microwave Box Reacto...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Granularityaaaaaaaaaa
Granularityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of artificial rutile. The method comprises steps of acid-soluble titanium slag modification treatment, acid impurity removal, calcination and the like. The artificial rutile prepared with the method completely meets the requirement for production of titanium white with a chlorination process, and raw materials have high adaptability. A microwave heating manner is selected, the required equipment investment is 17% lower than that of the prior art, the energy consumption is reduced by 25%, the purity of the artificial rutile is higher than 91%, byproducts are fewer, environmental pollution is low, and requirement of energy saving, emission reduction and clean metallurgy are met.

Description

【Technical field】 [0001] The invention belongs to the technical field of preparation of inorganic crystals. More specifically, the present invention relates to a method for preparing artificial rutile. 【Background technique】 [0002] Acid-soluble titanium slag and metallic iron can be obtained by smelting ilmenite in an electric furnace. The smelting process is mainly to remove iron, but the ability to remove non-ferrous impurities is poor, so the product quality is greatly affected by the raw materials. At present, the main production method of titanium slag is mainly to use ilmenite as raw material, and adopt the method of electric furnace smelting to make acid-soluble high-titanium slag or process it into high-titanium slag and artificial rutile after enrichment treatment. [0003] Titanium-rich materials prepared by traditional electric furnace smelting ilmenite generally contain TiO 2 60%-75% by weight, and the content of calcium and magnesium can reach 4%-7%. The p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C01G23/047B09B3/00
CPCB09B3/00C01G23/047
Inventor 陈菓陈晋彭金辉张利波郭胜惠周俊文
Owner YUNNAN MINZU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com