Zirconia biological ceramic used for making hip joint and its preparation method

A technology of bioceramics and zirconia, applied in medical science, prosthesis, etc., can solve the problems of stainless steel fatigue, low strength, and poor plastic stability, and achieve high biocompatibility, good wear resistance, and high toughness.

Inactive Publication Date: 2015-08-12
SUZHOU VIVOTIDE BIOTECH
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Biological hard tissue substitute materials were first used body bones and animal bones, and later developed to use stainless steel and plastics. Due to the problems of dissolution, corrosion and fatigue of stainless steel, plastics have problems of poor stability and low strength.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A zirconia bioceramic for manufacturing hip joints, comprising the following components in parts by mass:

[0023] 85 parts of zirconia, 7 parts of nano-titanium oxide, 8 parts of nano-alumina, 3 parts of nano-zinc oxide, 5 parts of carbon fiber and 10 parts of calcium oxide.

[0024] According to the preparation method provided by the present invention, the zirconia bioceramic used to manufacture the hip joint is prepared, and the steps are as follows:

[0025] (1) Weighing: Accurately weigh each component;

[0026] (2) Ball milling: Mix the components together and put them into a ball mill for grinding and mixing;

[0027] (3) Cold press forming: the mixed powder is pressed with a 60T press;

[0028] (4) Put the formed powder into the mold and perform high-temperature calcination at a temperature of 1300°C and a pressure of 800MPa for 6 hours;

[0029] (5) After calcination, take it out after cooling, and then obtain a block-shaped zirconia bioceramic for manufactu...

Embodiment 2

[0032] A zirconia bioceramic for manufacturing hip joints, comprising the following components in parts by mass:

[0033] 65 parts of zirconia, 3 parts of nano-titanium oxide, 2 parts of nano-alumina, 1 part of nano-zinc oxide, 2 parts of carbon fiber and 5 parts of calcium oxide.

[0034] According to the preparation method provided by the present invention, the zirconia bioceramic used to manufacture the hip joint is prepared, and the steps are as follows:

[0035] (1) Weighing: Accurately weigh each component;

[0036] (2) Ball milling: Mix the components together and put them into a ball mill for grinding and mixing;

[0037] (3) Cold press forming: the mixed powder is pressed with a 60T press;

[0038] (4) Put the formed powder into the mold and perform high-temperature calcination at a temperature of 1300°C and a pressure of 700MPa for 5 hours;

[0039] (5) After calcination, take it out after cooling, and then obtain a block-shaped zirconia bioceramic for manufacturi...

Embodiment 3

[0042] A zirconia bioceramic for manufacturing hip joints, comprising the following components in parts by mass:

[0043] 80 parts of zirconia, 6 parts of nano-titanium oxide, 6 parts of nano-alumina, 3 parts of nano-zinc oxide, 4 parts of carbon fiber and 8 parts of calcium oxide.

[0044] According to the preparation method provided by the present invention, the zirconia bioceramic used to manufacture the hip joint is prepared, and the steps are as follows:

[0045] (1) Weighing: Accurately weigh each component;

[0046] (2) Ball milling: Mix the components together and put them into a ball mill for grinding and mixing;

[0047] (3) Cold press forming: the mixed powder is pressed with a 60T press;

[0048] (4) Put the formed powder into the mold and perform high-temperature calcination at a temperature of 1200°C and a pressure of 700MPa for 7 hours;

[0049] (5) After calcination, take it out after cooling, and then obtain a block-shaped zirconia bioceramic for manufactur...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Compressive strengthaaaaaaaaaa
Bending strengthaaaaaaaaaa
Toughnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a zirconia biological ceramic used for making hip joint and a preparation method thereof, and relates to the field of biological materials, the zirconia biological ceramic used for making the hip joint comprises the following components by mass: 65-85 parts of zirconia, 3-7 parts of nano titanium oxide, 2-8parts of nano aluminum, 1-3 parts of nano zinc oxide, 2-5 parts of carbon fiber and 5-10 parts of calcium oxide. The preparation steps of the preparation method of the zirconia biological ceramic used for making the hip joint are as follows: (1) weighing; (2) ball milling; (3) cold pressing molding; (4) high temperature calcination, and (5) cooling. The zirconia biological ceramic used for making the hip joint has high wear-resisting property and toughness, and good biological compatibility, and has good application prospect as a material for making the hip joint.

Description

technical field [0001] The invention belongs to the field of biomaterials, in particular to a zirconia bioceramic used for manufacturing hip joints and a preparation method of the bioceramic. Background technique [0002] With the development of material science and technology, biomaterials have become one of the important research directions in the field of biomedicine because of their special properties of repairing, replacing and regenerating body tissues. Biological hard tissue substitute materials were first used body bones and animal bones, and later developed to use stainless steel and plastics. Due to the problems of dissolution, corrosion and fatigue of stainless steel, plastics have problems of poor stability and low strength. Therefore, the bottleneck in the development of biomaterials is caused. The emergence of bioceramics has improved the shortage of existing alternative materials. Because of its many advantages, bioceramics has broad development prospects. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B35/49C04B35/80C04B35/645A61L27/10
Inventor 郭玉芹刘乐峰邱东成
Owner SUZHOU VIVOTIDE BIOTECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com